Development of metal-resin composite restorative material. Part 4. Flexural strength and flexural modulus of metal-resin composite using Ag-In alloy particles as filler

Properties of model E-glass fiber composites with varying matrix monomer ratios

OBJECTIVE

To evaluate properties of fiber-reinforced-composites (FRC) containing Bis-EMA/UDMA monomers but identical dispersed phase (60% wt BaSi glass power +10% wt E-glass fibre).

METHODS

A control (Group A), monomer mixture comprising 60% Bis-GMA, 30% TEGDMA, and 10% PMMA (typical FRC monomers) was used. The following monomer mass fractions were mixed: 50% bis-GMA plus 50% of different ratios of Bis-EMA+UDMA to produce consistent formulations (Groups B-E) of workable viscosities was also studied. Flexural strength (FS), fracture toughness (KIC), water sorption (SP), solubility (SL) and hygroscopic expansion (HE) were measured. FS and KIC specimens were stored for 1, 7 d, and 30 d in water at 37 °C. SP/SL specimens were water-immersed for 168d, weighed at intervals, then dried for 84 d at 37 °C. To analyze differences in FS, and KIC, a two-way ANOVA and Tukey post-hoc tests (α = 0.05) were conducted. For SP/SL, and HE, one-way ANOVA with subsequent Tukey post-hoc tests (α = 0.05) were utilized.

RESULTS

FS and KIC for groups A, D, E decreased progressively after 1 d. Groups B and C (highest amounts of Bis-EMA) did not decrease significantly. The modified matrix composites performed significantly better than the control group for SP and HE. The control group outperformed the experimental composites only for SL with up to 250% higher SL for group E (6.9 μg/mm) but still below the maximum permissible threshold of 7.5 μg/mm.

SIGNIFICANCE

EXPERIMENTAL: composites with highest amounts of Bis-EMA showed improved hydrolytic stability and overall enhancement in several clinically-relevant properties. This makes them potential candidates for alternative matrices to a semi-interpenetrating network in fiber-reinforced composites.

Effect of Fibres on Physico-Mechanical Properties of Bulk-Fill Resin Composites

OBJECTIVE

To measure the flexural strength (FS) of bulk-fill resin composites and assess their long-term water absorption and solubility properties with and without the inclusion of short glass fibres.

METHODS

One resin composite, everX Flow with fibres, and four commercially available bulk-fill composites without fibres, namely, PALFIQUE, Activa, SDR Plus, and Filtek Bulk Fill One, were tested. Six specimens (2 × 2 × 25 mm) were fabricated for each material and stored in water for 1 day and 30 days to measure the flexural strength using a three-point bending test. To evaluate water absorption and solubility, circular disks measuring 15 × 2 mm (n = 5) were immersed in water for 60 days, and their weights were recorded periodically. After 60 days, the specimens were dried for an additional 21 days to determine solubility.

RESULTS

Flexural strength values ranged from 101.7 to 149.1 MPa. Significant distinctions were observed among the resin composites at the onset of the study (p < 0.05). The highest FS value was identified in everX Flow, while ACT exhibited the lowest (p < 0.05). However, the flexural strength values exhibited a significant decrease with increased storage time (p < 0.05), except for ACT, which demonstrated a noteworthy increase. Concerning water absorption and solubility, ACT displayed the highest absorption, while the range of solubility varied from -0.88 to 5.8 μg/mm3. ACT also had the highest solubility, whereas everX Flow exhibited negative solubility.

SIGNIFICANCE

The addition of short fibres, along with potential differences in matrix composition, enhanced the flexural strength of everX Flow. However, the substantial reduction in flexural strength observed in everX Flow and SDR following exposure to water corroborates the manufacturers' recommendation to apply a conventional resin composite cap on these materials.

Cytotoxicity of alloying elements and experimental titanium alloys by WST-1 and agar overlay tests

OBJECTIVE

This study was performed to evaluate the biocompatibility of nine types of pure metals using 36 experimental prosthetic titanium-based alloys containing 5, 10, 15, and 20wt% of each substituted metal.

METHODS

The cell viabilities for pure metals on Ti alloys that contain these elements were compared with that of commercially pure (CP) Ti using the WST-1 test and agar overlay test.

RESULTS

The ranking of pure metal cytotoxicity from most potent to least potent was: Co>Cu>In>Ag>Cr>Sn>Au>Pd>Pt>CP Ti. The cell viability ratios for pure Co, Cu, In, and Ag were 13.9±4.6%, 21.7±10.4%, 24.1±5.7%, and 24.8±6.0%, respectively, which were significantly lower than that for the control group (p<0.05). Pure Pd and Pt demonstrated good biocompatibility with cell viabilities of 93.8±9.6% and 97.2±7.1%, respectively. The Ti-5Pd alloy exhibited the highest cell viability (128.4±21.4%), which was greater than that of CP Ti. By alloying pure Co or Cu with Ti, the cell viabilities for the Ti-xCo and Ti-xCu alloys increased significantly up to 10wt% of the alloying element followed by a gradual decrease with a further increase in the concentration of the alloying element. Based on the agar overlay test, pure Ag, Co, Cr, Cu, and In were ranked as 'moderately cytotoxic', whereas all Ti alloys were ranked as 'noncytotoxic'.

SIGNIFICANCE

The cytotoxicity of pure Ag, Co, Cr, Cu, and In suggests a need for attention in alloy design. The cytotoxicity of alloying elements became more biocompatible when they were alloyed with titanium. However, the cytotoxicity of titanium alloys was observed when the concentration of the alloying element exceeded its respective allowable limit. The results obtained in this study can serve as a guide for the development of new Ti-based alloy systems.