Effects of light curing modes and resin composites on temperature rise under human dentin: an in vitro study

How does indirect air-cooling influence pulp chamber temperature in different volume teeth and absence/presence of resin-based composite during light curing?

Background

Light-curing of materials during restorative dental procedures poses a risk for pulp tissue overheating. Therefore, the aim of this study was to investigate the effect of indirect air-cooling on pulp chamber temperatures during light-curing of varying volume teeth and absence/presence of resin-based composite (RBC) at different exposure time.

Methods

The volume of 11 human teeth was measured by micro computed tomograph. An experimental rig controlled the thermal environment of the teeth and a thermocouple inserted retrograde into the root canal measured temperature changes. Pulp chamber temperature was measured with and without air-cooling on teeth without and with RBC at 15 s, 30 s and 60 s intervals. Generalized estimating equations were used for statistical analysis.

Results

The temperature increase with air-cooling (versus no air-cooling) was lower in teeth despite absence/presence of RBC (β = − 4.26, 95%CI − 5.33 and β = − 4.47, 95%CI − 5.60, respectively). With air-cooling, the temperature increase in teeth with RBC was lower compared to teeth without RBC (β = − 0.42, 95%CI -0.79; − 0.05). Higher teeth volume resulted in lower temperature increase with air-cooling than without air-cooling (β = − 0.04, 95%CI -0.07; − 0.01 and β = − 0.17, 95%CI -0.30; − 0.05, respectively).

Conclusions

Air-cooling resulted in lower pulp chamber temperature increase. Using air-cooling, the temperature increase was lower in teeth with RBC compared to teeth without RBC. Lower volume teeth resulted in higher temperature increase, thus they seemed to benefit more from air-cooling compared to higher volume teeth. Air-cooling could be an effective tool in controlling pulp temperature increase during light-curing, especially when the tooth volume is small.

Light-curing units used in dentistry: Effect of their characteristics on temperature development in teeth

This study aimed to investigate pulp chamber and surface temperature development using different LED light curing units (LCUs). Eight brands of LED-LCUs were tested in a laboratory bench model. The pulp chamber and surface temperature were recorded with a type T thermocouple and infrared cameras, respectively. The highest pulp chamber and surface temperature increase was 6.1±0.3°C and 20.1±1.7°C, respectively. Wide-spectrum LED-LCUs produced higher pulp chamber temperature increase at 0 mm and 2 mm but lower at 4 mm. Narrow-spectrum LED-LCUs produced higher surface temperature increase. LED-LCU featuring modulated output mode resulted in lower increase in pulp chamber temperature but higher on surface temperature. LED-LCU with light guide tip delivering an inhomogeneous beam caused higher increase in temperature on the surface and in the pulp chamber. LED-LCUs with different spectral emission, output mode and light guide tip design contributed to different temperature development in the pulp chamber and at the surface of teeth.

Temperature Changes in Composite Materials during Photopolymerization

During polymerization, composite materials cause a temperature rise which may lead to irreversible changes in the dental pulp. The mechanical properties of composite materials depend on a number of factors, such as the composition of the material, the type of polymerization unit, the polymerization mode, and the duration of polymerization. The objective of this study was to assess the temperature rise values and flexural strength of composite materials, as obtained using different modes and times of polymerization. A total of six composite materials were used in the study. Samples of each of the materials were cured using seven polymerization protocols. A CMP-401 digital meter (Sonel, Świdnica, Poland), complete with a type K thermocouple (NiCr-Ni), was used to record the temperature increases during the light curing of the resin composites. Temperature rises were recorded beneath the composite disc in an acrylic matrix. The specimens were tested for flexural strength using a Cometech QC-508M2 testing machine. The lowest results for the increased mean temperature were obtained for Fast-Cure 3 s (39.0 °C), while the highest results were obtained for Fast-Cure 20 s (45.8 °C). The highest average temperature values for all tested protocols were recorded for the Z550 Filtek material. Mean flexural strengths as measured in each test group were higher than the minimum value for composite materials as per the ISO:4049 standard. In the case of deep caries with a thin layer of dentin separating the filling from pulp, a base layer or a short polymerization duration mode is recommended to protect pulp from thermal injury.

Assessment of Heat Hazard during the Polymerization of Selected Light-Sensitive Dental Materials

Introduction. Polymerization of light-cured dental materials used for restoration of hard tooth tissue may lead to an increase in temperature that may have negative consequence for pulp vitality. Aim. The aim of this study was to determine maximum temperatures reached during the polymerization of selected dental materials, as well as the time that is needed for samples of sizes similar to those used in clinical practice to reach these temperatures. Materials and Methods. The study involved four composite restorative materials, one lining material and a dentine bonding agent. The polymerization was conducted with the use of a diode light-curing unit. The measurements of the external surface temperature of the samples were carried out using the Thermovision®550 thermal camera. Results. The examined materials significantly differed in terms of the maximum temperatures values they reached, as well as the time required for reaching the temperatures. A statistically significant positive correlation of the maximum temperature and the sample weight was observed. Conclusions. In clinical practice, it is crucial to bear in mind the risk of thermal damage involved in the application of light-cured materials. It can be reduced by using thin increments of composite materials.

Thermal analysis of bulk filled composite resin polymerization using various light curing modes according to the curing depth and approximation to the cavity wall

OBJECTIVE

The purpose of this study was to investigate the polymerization temperature of a bulk filled composite resin light-activated with various light curing modes using infrared thermography according to the curing depth and approximation to the cavity wall.

MATERIAL AND METHODS

Composite resin (AeliteFlo, Bisco, Schaumburg, IL, USA) was inserted into a Class II cavity prepared in the Teflon blocks and was cured with a LED light curing unit (Dr's Light, GoodDoctors Co., Seoul, Korea) using various light curing modes for 20 s. Polymerization temperature was measured with an infrared thermographic camera (Thermovision 900 SW/TE, Agema Infra-red Systems AB, Danderyd, Sweden) for 40 s at measurement spots adjacent to the cavity wall and in the middle of the cavity from the surface to a 4 mm depth. Data were analyzed according to the light curing modes with one-way ANOVA, and according to curing depth and approximation to the cavity wall with two-way ANOVA.

RESULTS

The peak polymerization temperature of the composite resin was not affected by the light curing modes. According to the curing depth, the peak polymerization temperature at the depth of 1 mm to 3 mm was significantly higher than that at the depth of 4 mm, and on the surface. The peak polymerization temperature of the spots in the middle of the cavity was higher than that measured in spots adjacent to the cavity wall.

CONCLUSION

In the photopolymerization of the composite resin, the temperature was higher in the middle of the cavity compared to the outer surface or at the internal walls of the prepared cavity.

Physical properties of self-, dual-, and light-cured direct core materials

The objective of this study is to evaluate flexural strength, flexural modulus, compressive strength, curing temperature, curing depth, volumetric shrinkage, water sorption, and hygroscopic expansion of two self-, three dual-, and three light-curing resin-based core materials. Flexural strength and water sorption were measured according to ISO 4049, flexural modulus, compressive strength, curing temperature, and curing depth according to well-proven, literature-known methods, and the volumetric behavior was determined by the Archimedes' principle. ANOVA was calculated to find differences between the materials' properties, and correlation of water sorption and hygroscopic expansion was analysed according to Pearson (p < 0.05). Clearfil Photo Core demonstrated the highest flexural strength (125 ± 12 MPa) and curing depth (15.2 ± 0.1 mm) and had the highest flexural modulus (≈12.6 ± 1.2 GPa) concertedly with Multicore HB. The best compressive strength was measured for Voco Rebilda SC and Clearfil DC Core Auto (≈260 ± 10 MPa). Encore SuperCure Contrast had the lowest water sorption (11.8 ± 3.3 µg mm(-3)) and hygroscopic expansion (0.0 ± 0.2 vol.%). Clearfil Photo Core and Encore SuperCure Contrast demonstrated the lowest shrinkage (≈2.1 ± 0.1 vol.%). Water sorption and hygroscopic expansion had a very strong positive correlation. The investigated core materials significantly differed in the tested properties. The performance of the materials depended on their formulation, as well as on the respective curing process.