Remineralization Potential of Sports Drink Containing Nano-Sized Hydroxyapatite

Effects of citric acid modified with fluoride, nano-hydroxyapatite and casein on eroded enamel

OBJECTIVES

The aim of this in vitro study was to evaluate the effects of citric acid containing fluoride, nano-hydroxyapatite, and casein on eroded enamel.

DESIGN

The crowns of 120 extracted bovine incisors were embedded in acrylic resin. An enamel window (2 × 3 mm) was created on the surface. Before in vitro pellicle formation samples were eroded in 1% citric acid (pH = 3.2) for 1 h at 36 °C and were randomly classified to eight groups (n = 15) as follows: Positive control: 1% citric acid, Negative control: Distilled water, F1: 0.047 mmol/L sodium fluoride, F2: 0.071 mmol/L sodium fluoride, NHA1: %0.05 Nano-Hydroxyapatite, NHA2: %0.1 Nano-Hydroxyapatite, C1: %0.02 Casein, C2: %0.2 Casein. Erosion cycling was performed three times daily for 3 days. In each cycle, the samples were immersed in 10 mL of control or modified solutions (10 min) and in 10 mL of artificial saliva (60 min). The surface roughness and enamel loss were analyzed by using profilometer, scanning electron microscopy (SEM) and atomic force microscopy techniques (AFM).

RESULTS

Among the groups, the positive control group was found to be having the highest erosive wear. Erosive wear in the F2, NHA2, C1, and C2 groups was not significantly different from the negative control group (p > 0.05). The C1 and C2 groups showed that erosion terminated and minimal tissue recovery occurred on the enamel surface.

CONCLUSION

Although all modifications reduced further demineralization, the citric acid modification with casein was found to be having a greater impact on dental erosion than the others.

Nano-hydroxyapatite could Compensate the Adverse Effect of soft carbonated Drinks on Enamel

INTRODUCTION

Since one of the most important disadvantages of soft drinks includes their adverse effect on mineral content of enamel because of their low pH, this study examined the microhardness of enamel before and after exposure to a soft drink containing different concentrations of nano-hydroxyapatite (nano-HA) as an additive.

MATERIALS AND METHODS

Sixty caries free human premolars were mounted in epoxy resin. After polishing, the baseline micro-hardness was recorded three times for each specimen using a Vickers indenter at 50 gm load. Subsequently, the samples were divided into six groups, which were treated for 5 minutes at 9°C by a cola-based drink contacting 0, 0.5, 1, 5, and 10 wt.% of nano-HA while the control group was immersed in artificial saliva. Ultimately, the final microhardness was assessed three times again for each specimen.

RESULTS

Paired t-test showed that in groups containing 0 and 0.5 wt.% of nano-HA, the microhardness was significantly reduced after treatment protocol (p = 0.00 and 0.01 respectively). Whereas in the other groups the microhardness was not significantly changed after treatment (p > 0.05).

CONCLUSION

Pure cola-based drink has a pronounced adverse effect on enamel microhardness, while admixing it with nano-HA could act as a protective factor.

CLINICAL SIGNIFICANCE

Although soft beverages are hazardous to tooth structure, some additives could compensate their adverse effect.

Nanodimensional and Nanocrystalline Apatites and Other Calcium Orthophosphates in Biomedical Engineering, Biology and Medicine

Recent developments in biomineralization have already demonstrated that nanosized particles play an important role in the formation of hard tissues of animals. Namely, the basic inorganic building blocks of bones and teeth of mammals are nanodimensional and nanocrystalline calcium orthophosphates (in the form of apatites) of a biological origin. In mammals, tens to hundreds nanocrystals of a biological apatite were found to be combined into self-assembled structures under the control of various bioorganic matrixes. In addition, the structures of both dental enamel and bones could be mimicked by an oriented aggregation of nanosized calcium orthophosphates, determined by the biomolecules. The application and prospective use of nanodimensional and nanocrystalline calcium orthophosphates for a clinical repair of damaged bones and teeth are also known. For example, a greater viability and a better proliferation of various types of cells were detected on smaller crystals of calcium orthophosphates. Thus, the nanodimensional and nanocrystalline forms of calcium orthophosphates have a great potential to revolutionize the field of hard tissue engineering starting from bone repair and augmentation to the controlled drug delivery devices. This paper reviews current state of knowledge and recent developments of this subject starting from the synthesis and characterization to biomedical and clinical applications. More to the point, this review provides possible directions of future research and development.