Shear bond strength of zirconia to resin: The effects of specimen preparation and loading procedure

Shear bond strength of different luting agents to polyether ether ketone

Background

Polyether ether ketone (PEEK) was recently introduced to dentistry. However, difficulty in provision of a strong durable bond is its main drawback. Thus, precise surface treatment and use of a suitable luting agent are imperative for bonding of PEEK restorations. This study aimed to assess the effect of type of luting agent on shear bond strength (SBS) of PEEK.

Materials and Methods

In this in vitro study, 60 square-shaped PEEK samples were fabricated and sandblasted with 110 μm Al₂O₃ particles. The samples were then divided into four groups based on the type of cement used (n = 15): zinc phosphate cement, Panavia F2, Panavia V5, and resin-modified glass-ionomer (RMGI) cement. After bonding, the samples were thermocycled for 5000 cycles. The SBS was measured by a universal testing machine. The surface of samples was inspected under a video measuring machine to determine the mode of failure. Data were analyzed using the Kruskal-Wallis test via SPSS version 24 (α = 0.05).

and Methods

In this in vitro study, 60 square-shaped PEEK samples were fabricated and sandblasted with 110 μm Al₂O₃ particles. The samples were then divided into four groups based on the type of cement used (n = 15): zinc phosphate cement, Panavia F2, Panavia V5, and resin-modified glass-ionomer (RMGI) cement. After bonding, the samples were thermocycled for 5000 cycles. The SBS was measured by a universal testing machine. The surface of samples was inspected under a video measuring machine to determine the mode of failure. Data were analyzed using the Kruskal-Wallis test via SPSS version 24 (α = 0.05).

Results

RMGI did not bond to PEEK. The SBS values were 4.02 ± 2.87 megapascals (MPa) for Panavia V5, 10.84 ± 6.05 MPa for Panavia F2, and 10.50 ± 2.88 MPa for zinc phosphate. The SBS in the Panavia V5 group was significantly lower than that in the Panavia F2 (P = 0.001) and zinc phosphate (P < 0.001) groups. No significant difference existed between the Panavia F2 and zinc phosphate groups in this respect (P > 0.05).

Conclusion

Panavia F2 resin cement and zinc phosphate conventional cement provided the highest bond strength to PEEK, while RMGI did not bond to PEEK.

Bonding ability of resin cements to different types of CAD/CAM composite blocks

This study investigated the bonding performance of two different types of resin cements to computer-aided design/computer-aided manufacturing (CAD/CAM) composite blocks based on the shear bond strength (SBS) test. A silane-containing self-adhesive resin cement (Panavia SA Cement Universal) and resin luting cement (Block HC Cem) with a primer, were used. Specimens were fabricated from three different types of CAD/CAM composite blocks, and their surfaces were blasted with alumina. Resin cements were bonded to the specimens, and their SBSs were measured after 15 min, 24 h, and after being subjected to thermal cycling for 10,000 and 30,000 cycles. Three-way ANOVA for bond strength revealed that CAD/CAM composite block, resin cement and storage time significantly influenced the SBS values, and the three-way interactions between the evaluated factors, and all the interactions were significant. It was concluded that the bonding performance of resin cements to CAD/CAM composite blocks were material and storage period dependent.