Color changes in resin cement polymerized with different curing lights under indirect restorations

Changes in color and contrast ratio of resin composites after curing and storage in water

Purpose

To verify the color change and contrast ratio of resin composites after curing and after 30 days of storage in water.

Methods

Dentin A2 shades of different light-cured dental resin composites (Vittra APS, FGM, Brazil; Z350 XT, 3M ESPE, EUA; Tetric N-Ceram, Ivoclar Vivadent, Liechtenstein, and Charisma Diamond, Heraeus Kulzer, Germany) were tested. Ten rounded specimens (8 mm × 2 mm) were prepared for each material. Reflectance for all samples was obtained using a spectrophotometer (Minolta CM 3700d, Konica Minolta, Japan) before curing, immediately after curing, and after 30 days of storage in water. The color change (ΔE*lab) and contrast ratio (CR) data were analyzed using a one-way analysis of variance with Tukey's and paired t-tests (α = 1%).

Results

For all materials tested, significant color changes were noticeable after curing and after 30 days in water (p < 0.01). Significant changes in the CR values before curing, after curing, and 30 days of storage in water were observed in the resin composites investigated (p < 0.01) except for Z350 (p > 0.01).

Conclusion

The CR values and color changes after curing and 30 days of storage in water varied depending on the material tested. This study corroborates the clinical practice of curing a small amount of unpolymerized resin composite on the tooth surface to select the desired shade before undertaking esthetic restorative procedures.

Assessment of Heat Hazard during the Polymerization of Selected Light-Sensitive Dental Materials

Introduction. Polymerization of light-cured dental materials used for restoration of hard tooth tissue may lead to an increase in temperature that may have negative consequence for pulp vitality. Aim. The aim of this study was to determine maximum temperatures reached during the polymerization of selected dental materials, as well as the time that is needed for samples of sizes similar to those used in clinical practice to reach these temperatures. Materials and Methods. The study involved four composite restorative materials, one lining material and a dentine bonding agent. The polymerization was conducted with the use of a diode light-curing unit. The measurements of the external surface temperature of the samples were carried out using the Thermovision®550 thermal camera. Results. The examined materials significantly differed in terms of the maximum temperatures values they reached, as well as the time required for reaching the temperatures. A statistically significant positive correlation of the maximum temperature and the sample weight was observed. Conclusions. In clinical practice, it is crucial to bear in mind the risk of thermal damage involved in the application of light-cured materials. It can be reduced by using thin increments of composite materials.