Effect of dentin dehydration and composite resin polymerization mode on bond strength of two self-etch adhesives

Assessment of Bonding Effectiveness of Adhesive Materials to Tooth Structure using Bond Strength Test Methods: A Review of Literature

Background

The rapid developments in the field of adhesive dental materials have led to improvements in many aspects of clinical dentistry. Adhesive bond strength plays an important role in determining the clinical performance and longevity of dental restorations. Nevertheless, bond strength tests have never been well-standardized, although a number of important recommendations have been made.

Objective

The aim of this paper is to critically review the validity of different bond strength testing methods for assessment of bonding effectiveness of adhesive materials to tooth structure and discuss factors that may affect bond strength measurement.

Data Collection

Relevant literature published between 1983 and 2018 was collected and reviewed from the PubMed database and Google scholar resources.

Review Results

Results of the current bond testing methods should be used to compare materials tested under the same laboratory settings, but they shouldn't be used to make direct inferences on their clinical behaviour. Shear and micro-shear tests, result in non-uniform stress distribution, stress concentration at the substrate area, and predominantly tensile stresses rather than shear stresses. Micro-tensile bond tests provide many advantages over the shear tests, although these methods are technique sensitive and labour intensive.

Conclusion

Bond strength testing methods should be well-standardized, but there are many factors that cannot be fully controlled which leads to variation and misinterpretation of the data about the bonding abilities of adhesives.

Clinical Significance

New adhesive materials should be subjected to a combination of testing protocols to properly assess their bonding effectiveness.

Comparison of the Dentin Bond Strength of Two Self-Etch Adhesives After Prolonged Air-Drying and Additional Light-Curing

OBJECTIVES

It has been reported that the water, solvents, or the primer incorporated into adhesive resins decrease the polymerization, compromise the mechanical properties, reduce the bond strength, and lead to a poor bonding performance of self-etch adhesives. This article evaluated the effect of air-drying and light-curing duration of self-etch adhesives on the micro-shear bond strength between composite resin and dentin.

MATERIALS AND METHODS

A total of 120 extracted sound human third molars were randomly divided into twelve groups (n=10). The occlusal dentin in each tooth was exposed. Clearfil SE Bond (CSEB) and Clearfil S3 Bond (CS3B) were used according to the manufacturer's instructions, followed by air-drying for 3 and 10 seconds in different groups. The adhesives were light-cured for 10, 20 and 40 seconds in different subgroups. Next, the composite resin (Clearfil AP-X) was placed on the dentin surface and was polymerized for 40 seconds. The micro-shear bond strength values were determined using a universal testing machine, and the results were statistically analyzed by three-way ANOVA and Tukey's post-hoc test (α=0.05).

RESULTS

CSEB exhibited a significantly higher dentin bond strength than CS3B. Increasing the curing time of CSEB resulted in an increase in the bond strength, whereas an increase in the air-drying time did not affect the bond strength of the two adhesives.

CONCLUSIONS

Within the limitations of this study, an increase in the curing time improved the bond strength of CSEB, whereas the air-drying time did not affect the bond strength of the evaluated adhesives.