Despite enjoying high favourable outcome rates, root canal treatment is not always successful. Root canal retreatment is a widely practised option for managing a non-healing root treated tooth. A basic distinction between retreatment and initial treatment is the requirement to remove the existing root filling material occupying the root canal space. Only then, can the technical deficiencies and possible causes of failure be addressed. Hence, the successful removal of the root filling material is critical to achieving the objectives of retreatment. Many different materials and techniques have been used for root canal filling, which have been documented in a plethora of studies; these are mainly laboratory studies investigating the removal of root filling materials. To help guide future research, which may then better inform clinical practice in relation to retreatment procedures, the focus of this narrative review is on the research methods and experimental models employed to study the removal of root filling materials. The current available literature demonstrates great variation in the research methodologies used to study the removal of root filling material, including direct visualization by splitting tooth samples or clearing, three-dimensional radiographic imaging including using microcomputed tomography or cone-beam computed tomography, and a combination of these techniques. Depending on the research method employed, variation also exists in quantification of root filling material removal; these include measurements of surface area, volume or weight, and criteria-based (semi-quantitative) assessment. Experimental models, using human teeth or resin models, differ with respect to standardization techniques and replication of the clinical scenario including initial sample preparation, canal filling, allocation and technical aspects of retreatment procedures. Future models should replicate, as closely as possible, the clinical scenario. Currently, microcomputed tomography provides a highly detailed, non-invasive and non-destructive method of objectively assessing and quantifying root filling removal.

Incidence of apical crack formation and propagation during removal of root canal filling materials with different engine driven nickel-titanium instruments

Objectives

To determine the incidence of crack formation and propagation in apical root dentin after retreatment procedures performed using ProTaper Universal Retreatment (PTR), Mtwo-R, ProTaper Next (PTN), and Twisted File Adaptive (TFA) systems.

Materials and Methods

The study consisted of 120 extracted mandibular premolars. One millimeter from the apex of each tooth was ground perpendicular to the long axis of the tooth, and the apical surface was polished. Twenty teeth served as the negative control group. One hundred teeth were prepared, obturated, and then divided into 5 retreatment groups. The retreatment procedures were performed using the following files: PTR, Mtwo-R, PTN, TFA, and hand files. After filling material removal, apical enlargement was done using apical size 0.50 mm ProTaper Universal (PTU), Mtwo, PTN, TFA, and hand files. Digital images of the apical root surfaces were recorded before preparation, after preparation, after obturation, after filling removal, and after apical enlargement using a stereomicroscope. The images were then inspected for the presence of new apical cracks and crack propagation. Data were analyzed with χ² tests using SPSS 21.0 software.

Results

New cracks and crack propagation occurred in all the experimental groups during the retreatment process. Nickel-titanium rotary file systems caused significantly more apical crack formation and propagation than the hand files. The PTU system caused significantly more apical cracks than the other groups after the apical enlargement stage.

Conclusions

This study showed that retreatment procedures and apical enlargement after the use of retreatment files can cause crack formation and propagation in apical dentin.