Enamel Demineralization Adjacent to Orthodontic Brackets Bonded with ACTIVA BioACTIVE-RESTORATIVE

Experimental Dental Composites Containing a Novel Methacrylate-Functionalized Calcium Phosphate Component: Evaluation of Bioactivity and Physical Properties

The aim of this study was to synthesize and characterize a novel methacrylate-functionalized calcium phosphate (MCP) to be used as a bioactive compound for innovative dental composites. The characterization was accomplished by attenuated total reflectance Fourier-transform infrared spectroscopy (ATR-FTIR), scanning electron microscopy (SEM), and energy dispersive spectroscopy (EDS). The incorporation of MCP as a bioactive filler in esthetic dental composite formulations and the ability of MCP containing dental composites to promote the precipitation of hydroxyapatite (HAp) on the surfaces of those dental composites was explored. The translucency parameter, depth of cure, degree of conversion, ion release profile, and other physical properties of the composites were studied with respect to the amount of MCP added to the composites. Composite with 3 wt.% MCP showed the highest flexural strength and translucency compared to the control composite and composites with 6 wt.% and 20 wt.% MCP. The progress of the surface precipitation of hydroxyapatite on the MCP containing dental composites was studied by systematically increasing the MCP content in the composite and the time of specimen storage in Dulbecco's phosphate-buffered solution with calcium and magnesium. The results suggested that good bioactivity properties are exhibited by MCP containing composites. A direct correlation between the percentage of MCP in a composite formulation, the amount of time the specimen was stored in PBS, and the deposition of hydroxyapatite on the composite's surface was observed.

Biophysical and Fluoride Release Properties of a Resin Modified Glass Ionomer Cement Enriched with Bioactive Glasses

The aim of this study was to evaluate the bond strength, microleakage, cytotoxicity, cell migration and fluoride ion release over time from a resin-modified glass-ionomer cement (RMGIC) enriched with bioactive glasses (BAGs) and a nanohybrid restorative polymer resin agent used as adhesion material in the cemented brackets. One hundred and twenty bovine lower incisors were divided into three groups: (Transbond Plus Self Etching Primer (TSEP)/Transbond XT (TXT), TSEP/ACTIVA, orthophosphoric acid gel/ACTIVA) and brackets were bonded. A bond strength test and microleakage test were applied. A fluoride release test was applied after 60 days for the TXT and ACTIVA group. To evaluate cytotoxicity and cell migration, a cell viability and scratch migration assay were done for each group. p values < 0.05 were considered significant. Regarding bond strength and microleakage test, no significant differences were found between TSEP/TXT and TSEP/ACTIVA. At 6.4 pH, ACTIVA showed a higher degree of fluoride ion release, which increased with acid pH (3.5), with a maximum fluoride secretion at 30 days. MTT assay revealed that TXT reduces the viability of gingival cells with significant differences (p < 0.001) compared to the untreated cells (control group). ACTIVA provides optimal adhesive and microfiltration properties, releases substantial amounts of fluoride ions in both acid and neutral media, and its biocompatibility is greater than that of traditional composite resin adhesive systems.

In vitro wear of dual-cured bulkfill composites and flowable bulkfill composites

OBJECTIVES

The objective of this study is to test the wear of dual-cured bulkfill and flowable bulkfill composites.

MATERIALS AND METHODS

Six dual-cured bulkfill composites, Cention, Cention-Exp, Activa, Fill-up, Hyperfil Injectafill, and two flowable bulkfill composites Tetric Evoflow BulkFill and G-aenial Universal Flo were tested in this study (n = 8). Each composite was applied into an aluminum sample holder and cured with a Valo Grand (1230 mW/cm² ) or self-cured according to manufacturer's recommendations, and stored in water for 3 weeks. The samples were subjected to 120 000 load cycles of 49 N (CS-4) against spherical steatite antagonists and simultaneously subjected to 4440 thermocycles (5°C-55°C). At intervals between load cycles, polyvinyl siloxane impressions were taken and scanned with a True Definition Laser Scanner. The volumetric wear was calculated using image software (Geomagic). Microscopic images of selected wear facets and their corresponding worn antagonists were obtained using SEM. All data were analyzed using analysis of variance (ANOVA) and Tukey post hoc test for multiple comparison (α = .05; β = .2).

RESULTS

The load cycles volumetric wear-increase was linear. Two-way ANOVA showed significant main effects (material and light-cured) and significant interactions. Self-cured materials (mean = 0.38 mm³ ) showed more wear than light-cured materials (mean = 0.35mm³ ).

CONCLUSIONS

The bioactive materials except Activa light-cured showed significantly more wear than the flowable composites.

CLINICAL SIGNIFICANCE

This study demonstrated that most of the dual-cured composites, if light-cured, showed the same wear as the flowable composites used as control. Therefore, to obtain adequate wear resistance the dual-cured composites should be routinely light-cured.