Evaluation of the effect of natural versus synthetic matrix metalloproteinase silencers in preservation of dentin collagen and long-term bond strength of total etch adhesive

Influence of Phosphoric, Glycolic, and Ferulic Acids on Dentin Enzymatic Degradation, Ultimate Tensile Strength, and Permeability

This study evaluated dentin enzymatic degradation based on the total matrix metalloproteinase (MMP) activity of demineralized dentin matrices before and after exposure to phosphoric acid (PA), glycolic acid (GA), and ferulic acid (FA). The release of hydroxyproline (HP), ultimate tensile strength (UTS), and dentin permeability (DP) were also evaluated. Dentin collagen matrices were assessed according to total MMP activity before and after treatment with the tested acids (n=10) for 15 seconds and compared with the control (GM6001 inhibitor). Dentin beams were analyzed for HP release and UTS after the treatments. Dentin discs were tested for DP at a pressure of 5 psi before and after treatment with the acids (n=10). The FA group had a lower percentage of enzymatic inhibition than the PA and GA groups (p<0.0001). No significant difference in UTS was found among the acids (p=0.6824), but HP release was significantly higher in the FA group than in the PA and GA groups (p<0.0001). No significant difference in DP was found for the acids (p=0.0535). GA led to less activation of MMPs and less release of HP, whereas the UTS and DP for GA were like those found for PA. In contrast, FA promoted greater enzymatic activity and greater release of HP, while having similar results to GA and PA regarding mechanical properties.

Hesperidin reduces dentin wear after erosion and erosion/abrasion cycling in vitro

OBJECTIVE

To evaluate the action of hesperidin (HPN) at different concentrations to prevent dentin erosive wear, associated or not to abrasion.

METHODS

A study with 6 experimental groups (n = 10) for erosion (experiment 1) and another 6 for erosion + abrasion (experiment 2). The treatments were: distilled water (DW), DW with collagenase (DW + Col), 0.46% epigallocatechin-3-gallate (EGCG) and 0.1%, 0.5% or 1% HPN. The specimens were submitted to a cycle (3x/day) for 5 days that consisted of immersion on 1% citric acid (5 min), artificial saliva (60 min), treatment (5 min), brushing (150 movements only in experiment 2), and artificial saliva (60 min / overnight). Collagenase was added in artificial saliva for all groups except DW-group. Dentin changes were assessed with optical profilometry and scanning electron microscopy. Data were submitted to one-way analysis of variance and Tukey tests (α = 0.05).

RESULTS

For experiment 1, DW showed the lowest wear and did not significantly differ from EGCG. DW + Col showed the highest wear, being significantly different from HPN at 1%. In experiment 2, DW showed the lowest wear and DW + Col the highest. EGCG showed less wear than the three groups treated with HPN. In addition, for both cycling models, there were no significant differences among the three concentrations of HPN analyzed. In micrographs of HPN-treated groups, it could be observed the formation of a barrier on the dentin that promoted the obliteration of the tubules.

CONCLUSIONS

HPN was able to preserve the demineralized organic matrix layer but did not overcome the effect of EGCG.