The Effect of Chlorhexidine Mixed with Mineral Trioxide Aggregate on Bacterial Leakage of Apical Plug in Simulated Immature Teeth Using Human Fresh Saliva

Comparative evaluation of the antibacterial efficacy of two experimental calcium silicate-based intracanal medicaments: An in-vitro study

Introduction

Success of endodontic treatment relies on minimizing microbial load by chemo-mechanical preparation and intra-canal medication(ICM). Calcium hydroxide based ICMs have known disadvantages. Calcium silicate-based cements(CSC) exhibit antibacterial activity, thus promoting researchers to experiment with their formulations to use them as ICMs.

Aim

Evaluation and comparison of the antimicrobial efficacy of two experimental CSC (MTA & Biodentine + 2%chlorhexidine) and Bio-C Temp against E.faecalis.

Methods and Material

Test materials were divided into four groups namely Group1-Bio-C Temp, Group2-UltraCAL XS, Group3-Biodentine+2%CHX and Group4-MTA+2%CHX. Direct contact test was done by placing a standardized suspension of E.faecalis on test materials and bacterial growth was assessed spectrophotometrically using ELISA at one, three and seven days.

Statistical Analysis

Data was analysed using one-way ANOVA, Tukey's multiple post hoc test and paired-t test. Results: Intragroup comparison revealed decreased mean optical density(OD) in groups 1, 2, and 4; no significant difference in group 3. Intergroup comparison showed statistical differences in mean OD values between groups (3 and 4); groups (1 and 2) at days one(p-0.018) and three(p-0.035), but no difference individually. Group 4 showed the highest antimicrobial efficacy on day seven.

Conclusion

MTA+2%CHX & Biodentine+2%CHX showed better antimicrobial efficacy and hence could be used as potential ICMs.

Effect of Hyaluronic Acid in Modifying Tensile Strength of Nonabsorbable Suture Materials: An In Vitro Study

Background and Aims:

In periodontics and other surgical disciplines, sutures play a detrimental role in healing of wound. The use of chemical adjuncts to boost healing has been experimented in recent years. The aim of this study was to evaluate the role of hyaluronic acid rinse in influencing the tensile strengths of commonly used sutures.

Materials and Methods:

Two commonly used nonabsorbable suture materials, silk and polyamide, were used for this in vitro study. Tensile strengths of the suture materials were determined by pre- and post-immersion in hyaluronic acid (test) and chlorhexidine (control). A Tinius Olsen Universal Testing Machine was used to assess the tensile strength of the samples. The variables were assessed for normality using the Kolmogorov–Smirnov test. The Wilcoxon signed rank test and Mann–Whitney U test (for quantitative data within two groups) were used for quantitative data comparison of all the clinical indicators. The level of significance was set at P ≤ 0.05.

Results:

Polyamide showed better stability in terms of tensile strength when compared to silk. Hyaluronic acid as a chemical adjunct did not alter the tensile strengths of both suture materials pre- and post-immersion.

Conclusion:

This in vitro study has shown a promising property of hyaluronic acid with relation to stabilization of tensile strength of suture materials, which needs to be evaluated in clinical settings.

Calcium Silicate-Based Cements as Root Canal Medicament

Purpose

This study aims to retard the setting reaction of CSC by mixing it with 2% chlorhexidine gel (CHX) which will be used as an intracanal medicament, and to evaluate the removal of the experimental medicaments from the root canal.

Materials and Methods

White Portland cement, white ProRoot MTA and Biodentine were mixed with 2% CHX. The setting time, flowability and film thickness of the CSC/CHX mixture (experimental medicaments) were assessed and measured following the standards of ISO specification. Calcium ion release was measured using ICP-OES, while pH was tested using a pH meter. Moreover, twenty single-rooted teeth were filled with the experimental medicaments for seven days, then the medicaments were removed and the samples analyzed using SEM. Calcium hydroxide paste was used as a control.

Results

The setting time of the experimental medicaments was inhibited until 84 days. The calcium ion release of the experimental medicaments was significantly higher compared to the control over the period of 14 days (P<0.001). The mean pH value was above 11.45 for all tested materials over a period of 14 days, with no significant difference between them (P<0.05). There was no significant difference in film thickness of the experimental medicaments compared to the control (P> 0.05). However, the flowability of the experimental medicaments was significantly higher than the control (P<0.05). SEM showed no significant differences in the removal of the intracanal medicaments between all the tested groups.

Conclusion

The addition of 2% CHX to CSCs retarded or inhibited its setting reaction over a period of 84 days. The calcium ion release and flowability of these experimental medicaments was found to be better than calcium hydroxide. Removal of the intracanal medicaments from the root canal was successfully achieved in all groups. Therefore, these experimental medicaments have the potential to be used as an enhanced root canal medicament.