Bond Strength to Microtraction and Nanofiltration Using Ethanol Wet Bonding Technique in Fresh Extracted Teeth: An Ex Vivo Study

A polyhexamethylene biguanide-assembly assisted strategy of dentin bonding greatly promotes bonding effects and caries treatment

Structural degeneration of a hybrid layer composed of a demineralized dentin matrix (DDM) and adhesive causes unsatisfactory functional outcomes in terms of bonding repair and caries treatment and is accompanied by high prevalence of secondary caries. Clinically, defects in the hybrid layer from insufficient adhesive infiltration, bacterial load from retained infected-dentin, and bacterial attack from the oral cavity are the main threats to degeneration. Currently, there is no strategy to simultaneously address adhesive penetration and bacterial infection. Herein, based on the core role of the strongly-polar hydrated DDM interface in dentin bonding, an interface-reconstructed bonding strategy assisted by electrostatic assembly of broad-spectrum germicidal polyhexamethylene biguanide (PHMB) is proposed that kills two birds with one stone. PHMB is absorbed onto the anionic 3D DDM forming a PHMB/DDM complex. The surface potential of the DDM increases by about 100 mV, the anion content decreases by 20%, and the interface water content decreases by nearly 40%. All of these changes contribute to the penetration of the adhesive, thereby improving the bonding strength and durability. After thermal cycling aging, the bonding strength of the PHMB group was 1.45-1.65 times that of the control group. In terms of antibacterial properties, PHMB treatment not only has a bacterial-killing ability due to the already formed biofilm but also significantly reduces the adhesion of bacteria, thereby delaying the occurrence of secondary caries. In summary, PHMB treatment reconstructed the DDM interface, resulting in a defect-low and inherent antibacterial hybrid layer that improves the bonding effect, treatment of caries and even prevention of secondary caries.

Reconstruction of a Demineralized Dentin Matrix via Rapid Deposition of CaF2 Nanoparticles In Situ Promotes Dentin Bonding

Dentin bonding based on a wet-bonding technique is the fundamental technique used daily in clinics for tooth-restoration fixation and clinical treatment of tooth-related diseases. Limited bonding durability led by insufficient adhesive infiltration in the demineralized dentin (DD) matrix is the biggest concern in contemporary adhesive dentistry. This study proposes that the highly hydrated noncollagenous protein (NCP)-formed interfacial microenvironment of the DD matrix is the root cause of this problem. Meanwhile, the endogenous phosphate groups of the NCPs are used as pseudonuclei to rapidly induce the formation of amorphous CaF₂ nanoparticles in situ in the interfacial microenvironment. The DD matrix is thus reconstructed into a novel porous structure. It markedly facilitates the infiltration of dentin adhesives in the DD matrix and also endows the DD matrix with anticollapsing capability when water evaporates. Whether using a wet-bonding or air-drying mode, the bonding effectiveness is greatly promoted, with the 12 month bonding strength being about twice that of the corresponding control groups. This suggests that the nanoreinforced DD matrix eliminates the dependence of bonding effectiveness on the moisture status of the DD surface controlled only by experiences of dentists. Consequently, this bonding strategy not only greatly improves bonding durability but also overcomes the technical sensitivity of bonding operations of the total-etched bonding pattern. This exhibits the potential to promote dentin bonding and is of great significance to dentistry.

Effects of Different Light-curing Modes on the Compressive Strengths of Nanohybrid Resin-based Composites: A Comparative In Vitro Study

Objective

To evaluate the effects of polymerization conducted by using LED lamps of different wavelengths (polywave and monowave) on the compressive strengths of nanohybrid composite resins Filtek™ Bulk Fill - 3M and 3M™ Filtek™ Z350 XT.

Materials and Methods

The study was prospective, experimental in vitro, and comparative. The sample consisted of nanohybrid composite resins. The sample size (n) was 100 specimens, divided into 10 groups. CRIS (Checklist for Reporting In-vitro Studies) Guidelines were used for writing this article.

Results

There were statistically significant differences between all groups with P < 0.001. Group 2 (nanohybrid composite resin blocks 3M™ Filtek™ Z350 XT with Monowave LED lamps) showed the highest compressive strength of 238.36±34.69N; CI (213.55-263.18) N. This was followed by Group 4 (nanohybrid composite resin blocks 3M™ Filtek™ Z350 XT with Poliwave LED lamps, High Power) and Group 6 (nanohybrid composite resin blocks 3M™ Filtek™ Z350 XT with Poliwave LED lamps, Soft Star), with compressive strengths of 222.33 ± 53.09N, and 209.21 ± 22.52N, respectively.

Conclusions

Significant differences were found between the compressive strengths of 3M™ Filtek™ Z350 XT and Filtek™ Bulk Fill - 3M resins, and that of resins photopolymerized with monowave and polywave LED lamps and halogen light. Thus, the types of light and lamp directly influence the compressive strengths of the composite resins.