Resistance of bonded premolars to four artificial ageing models post enamel conditioning with a novel calcium-phosphate paste

Performance of novel enamel-conditioning calcium-phosphate pastes for orthodontic bonding: An in vitro study

Background

This study aimed to develop remineralizing calcium-phosphate (CaP) etchant pastes for enamel conditioning before bracket bonding and evaluate the bonding performance, failure pattern, and enamel surface integrity post bracket debonding in comparison with the conventional phosphoric acid (PA) etchant gel.

Material and Methods

Micro-sized monocalcium phosphate monohydrate and hydroxyapatite (micro- and nano-sized) powders were mixed with various phosphoric and nitric acid concentrations to develop eight acidic CaP pastes. Ninety extracted human premolars were randomly assigned into eight experimental and one control group (n=10). The developed pastes and control (commercial 37% PA-gel) were applied onto the enamel using the etch-and-rinse protocol before bonding metal brackets. Shear bond strength and adhesive remnant index (ARI) scores were evaluated after 24 hours water storage (24 h) and post 5000 thermocycling (TC). Field emission scanning electron microscopy (FE-SEM) was used to evaluate enamel damage after bracket debonding.

Results

The developed CaP pastes, excepting MNA1 and MPA1, resulted in significantly lower SBS values and ARI scores than 37% PA gel. Etching with 37% PA yielded roughened, cracked enamel surfaces with excessive retention of adhesive residue. In contrast, enamel treatment with the experimental pastes exhibited smooth, unblemished surfaces, with obvious CaP re-precipitation induced by mHPA2 and nHPA2 pastes and to a lesser extent by MPA2 paste.

Conclusions

Three newly developed CaP etchant pastes (MPA2, mHPA2, and nHPA2) can be promising alternative enamel conditioners that outperform conventional PA by generating adequate bracket bond strengths besides precipitating CaP crystals on the enamel. Moreover, these pastes maintained unblemished enamel surfaces with no or minimal adhesive residue after bracket removal. Key words:Enamel Conditioning, Calcium Phosphate, Bracket Bond Strength, Orthodontic Bonding, enamel damage.

Effect of Remineralizing Agents on Shear Bond Strength of Orthodontic Brackets-In Vitro Study

Orthodontic treatment can be effective only with the proper adhesion strength of the bonded elements on the teeth. The aim of the study was to analyze the influence of different remineralization products on the brackets (Evolve Low Profile Brackets 0.022 Roth prescription (DB Orthodontics Ltd., Silsden, England) shear bond strength (SBS)). In all, 40 teeth were investigated for this study; n = 30 demineralized (immersed in 0.1% citric acid for 30 min, twice a day, for 20 consecutive days) and n = 10 immersed only in artificial saliva. After the demineralization process, remineralization agents were applied to each group (n = 10): Group I: Elmex Sensitive professional^® toothpaste (CP, Gaba GmbH, Witten, Germany) and GC MI Paste Plus^® (GC, Leuven, Belgium), Group II: Elmex Sensitive professional^® toothpaste (CP, Gaba GmbH, Germany) and GC Tooth Mousse^® (Leuven, Belgium), Group III: Elmex Sensitive professional^® toothpaste (CP, Gaba GmbH, Germany). For the teeth in control group C, Elmex Sensitive professional^® toothpaste was used. SBS tests were performed by means of an advanced materials-testing machine that generated maximum load and tensile strength values. The data obtained underwent statistical analysis (ANOVA and Tuckey test) with a statistical threshold of p < 0.05. The SBS values were higher for group II (14.20 MPa) and I (10.36 MPa) and lower for group III (4.25 MPa) and C (4.11 MPa), with statistically significant differences between groups I and II when compared with groups III and C (p < 0.05). In conclusion, GC Tooth Mousse^® and MI-Paste Plus^® have no adverse effect on brackets SBS and are recommended to be used for enamel remineralization during orthodontic treatment.

Effects of an orthodontic primer containing amorphous fluorinated calcium phosphate nanoparticles on enamel white spot lesions

OBJECTIVES

The study investigated the effects of an orthodontic primer containing amorphous fluorinated calcium phosphate (AFCP) nanoparticles on enamel white spot lesions (WSLs).

MATERIALS AND METHODS

The AFCP nanoparticles were prepared and incorporated into Transbond XT Primer. Thirty-two human enamel slices were highly polished and randomly divided into four groups: no part covered (control), half covered with a primer containing 0 wt%, 25 wt%, and 35 wt% AFCP. Subsequently, samples were challenged by a modified pH-cycling and characterized by color measurement, micro-computed tomography, and scanning electron microscope (SEM). The bonding properties of the primers containing AFCP were assessed using shear bond strength test, and the mouse fibroblasts (L929) were employed to evaluate the cytotoxicity.

RESULTS

When the enamel was challenged by pH cycling, 25 wt% and 35 wt% AFCP groups exhibited less color change (ΔE) and less mineral loss than the control and 0 wt% AFCP groups. The SEM images showed that the original microstructural integrity and mineral deposition rate of the enamel surface were better in the 25 wt% and 35 wt% AFCP groups. In particular, the 35 wt% AFCP group exhibited the best performance after 3 weeks of pH cycling. The shear bond strength and cell viability revealed no significant difference among the tested groups (P > 0.05).

CONCLUSION

Using the primer containing 35 wt% AFCP might be a promising strategy for preventing the occurrence and development of WSLs during orthodontic treatment.

Bond Strength Survival of a Novel Calcium Phosphate-Enriched Orthodontic Self-Etching System after Various Ageing Protocols: An In Vitro Study

Objective

This study aimed to evaluate the orthodontic bond strength and enamel-preserving ability of a hydroxyapatite nanoparticles-containingself-etch system following exposure to various ageing methods.

Materials and Methods

Hydroxyapatite nanoparticles (nHAp) were incorporated into an orthodontic self-etch primer (SEP, Transbond™ plus) in three different concentrations (5%, 7%, and 9% wt) and tested versus the plain SEP (control) for shear bond strength (SBS), adhesive remnant index (ARI) scores, and enamel damage in range-finding experiments using premolar teeth. The best-performing formulation was further exposed to the following four artificial ageing methods: initial debonding, 24 h water storage, one-month water storage, and one-month acid challenge. A field-emission scanning electron microscope (FE-SEM) was used to examine the integrity of debonded enamel surfaces and calcium-phosphates (CaPs) reprecipitation.

Results

The best-performing formulation (7% nHAp-SEP) resulted in significantly lower SBS (p < 0.001) than the control SEP following the four artificial ageing methods. Nevertheless, it survived the ageing protocols and yielded clinically acceptable SBS with the advantages of leaving minimal adhesive residue, preserving enamel integrity and smoothness, and inducing CaP reprecipitation as confirmed by FE-SEM images.

Conclusions

A newly developed SEP produced adequate orthodontic bond strengths and left unblemished debonded enamel surfaces with minimal remnant adhesive and remineralisation potential, thereby suggesting simpler and safer bonding/debonding procedures.

A remineralizing orthodontic etchant that utilizes calcium phosphate ion clusters

This study aimed to investigate whether a phosphoric acid (H3PO4) solution containing calcium phosphate ion clusters (CPICs) could minimize enamel damage during long-term bracket bonding by dissolving the enamel surface and promoting enamel remineralization. The experimental design is as follows: first, three experimental etchants (H3PO4, CPICs-incorporated H3PO4 solution-I, and CPICs-incorporated H3PO4 solution-II) and two bonding resins (conventional orthodontic resin and self-adhesive orthodontic resin) were used in combination to create six groups, respectively. Each of these six groups was then divided into two sub-groups based on the presence or absence of thermocycling (TC). Twenty samples were assigned to each of the 12 groups (independent variables), and thus a total of 240 metal bracket-attached human premolars were used in this experiment. Bracket debonding was performed on each of 20 premolars in 12 groups, and shear bond strength (SBS) and adhesive remnant index (ARI) values were measured as dependent variables. Next, the three experimental etchants were applied (independent variables) to each of the three enamel samples, and the remineralization of the enamel surface was investigated as a dependent variable. The enamel surface was observed using electron scanning and atomic force microscopy. Furthermore, X-ray diffraction, energy dispersive spectroscopy (EDX) spectrum X-ray spectroscopy, and elemental mapping were performed, and the Knoop microhardness scale was measured. Therefore, the experiment was performed in two steps: SBS and ARI measurements for 12 groups, followed by observation of the enamel surface and microhardness measurements, according to the three types of etchants. As a result of the experiment, first, when the bracket was debonded, SBS did not decrease, and residual adhesive was hardly observed in the C2A group (before TC), C2A, and C1C groups (after TC) (p &lt; 0.001). Second, the experimental etchant containing CPICs achieved remineralization while demineralizing the enamel. This was verified through SEM/EDX, element mapping, XRD, and AFM. Also, the roughness and microhardness of the enamel surface were better in the remineralized surface by the experimental etchant containing CPICs (p &lt; 0.017). The CPICs-incorporated H3PO4 solution reduced ARI while maintaining SBS during bracket debonding, regardless of whether TC was performed or the type of resin. The etchant containing CPICs was also shown to remineralize the enamel and increase its microhardness.