Long-term fracture load of all-ceramic crowns: Effects of veneering ceramic thickness, application techniques, and cooling protocol

Effect of Finishing Protocols on the Surface Roughness and Fatigue Strength of a High-Translucent Zirconia

Purpose

In case of need for esthetical improvement of zirconia restorations, an individualization using extrinsic staining can be applied. This study aimed to evaluate the surface roughness and fatigue strength (survival) of high-translucency zirconia (3Y-TZP, YZ®HT, Vita Zanhfabrik) with extrinsic characterization and/or glaze.

Methods

Sixty (60) zirconia discs (12 × 1.2 mm) were obtained, sintered, and randomly distributed among three groups (n = 20) according to the surface finishing protocol: C (control), C + G (extrinsic characterization followed by a glaze layer), and G (glaze layer). The surface roughness (Ra) was analyzed with a contact profilometer. Subsequently, the specimens were subjected to a fatigue load profile starting at 120 N during 20,000 cycles at 4 Hz frequency, with a 5% increase at each step until failure. The failed specimens were evaluated under a stereomicroscope. Surface roughness analysis was evaluated by using one-way ANOVA and post hoc Tukey tests (95%); while fatigue survival probability was analyzed with Kaplan-Meier and Mantel-Cox (log- rank, 95%).

Results

One-way ANOVA revealed that surface roughness was affected by the finishing protocol, where C + G showed the highest mean value (0.46 ± 0.18 µm)A followed by G (0.30 ± 0.10 µm)B, and C (0.19 ± 0.02 µm)C. While for fatigue strength, the G protocol presented a higher mean value (243.00, and 222.36-263.63)A, followed by C + G (192.75 and 186.61-198.88)B and C (172.50 and 159.43-185.56)C.

Conclusion

Surface finishing protocols modify the surface roughness and fatigue strength of high-translucent zirconia. Regardless of the surface roughness, both glazing protocols improved the ceramic fatigue strength, favoring the restoration's long-term survival.

Effect of three different veneering techniques on the stress distribution and in vitro fatigue behavior of core-veneer all-ceramic fixed partial dentures

Background. The present study aimed to evaluate the influence of the veneering technique on the tensile stress distribution and survival of full-ceramic fixed dental prostheses (FDPs). Methods. A three-dimensional model of an FDP was modeled on a second premolar and a second molar with a pontic between them for finite element analysis (FEA). The groups were divided according to the veneering technique: conventional stratification, rapid layer, and CAD-on techniques. A mesh control test determined the number of elements and nodes. The materials' properties were attributed to each solid component with isotropic, homogeneous, and linear elastic behavior. For the in vitro fatigue test (n=30), the FDPs were cemented on dentin analog abutments and submitted to 2×10⁶ mechanical cycles (100 N at 3 Hz). Results. Maximum principal stress showed that the connector between the pontic and the second molar concentrated higher stresses, regardless of the techniques: Rapid layer (6 MPa) > CAD-on (5.5 MPa) > conventional stratification (4 MPa). The conventional stratification technique concentrated high stresses at the interface between the framework and veneering ceramic (2 MPa), followed by the rapid layer (1.8 MPa) and CAD-on (1.5 MPa) techniques. The crowns fabricated using the rapid layer and CAD-on techniques exhibited a 100% survival rate, while the conventional stratification group had 0% survival. Conclusion. Even with similar stress distribution between the veneering techniques, the conventional stratification technique was more prone to failure under fatigue due to higher defects incorporated than CAD-on and rapid layer techniques.

Comparison of Fracture Load of the Four Translucent Zirconia Crowns

Recently, translucent zirconia has become the most prevalent material used as a restorative material. This study aimed to compare the crown fracture load of the four most common different translucent zirconia brands available in the market at 1.5 mm thickness. Standardized tooth preparations for a full ceramic crown were designed digitally with software (AutoCAD) by placing a 1.0 mm chamfer margin and 1.5 mm occluso-cervical curvature for the crown sample manufacturing. Stylized crowns were chosen to control the thickness of the crown. The axial and occlusal thickness were standardized to 1.5 mm thickness except at the central pit, which was 1.3 mm thick. The STL file for the tooth dies was prepared using software (3Shape TRIOS^® Patient Monitoring, Copenhagen, Denmark). The tooth dies were printed with a resin material (NextDent Model 2.0, Vertex-Dental B.V., Soesterberg, The Netherlands) using a 3D printing software (3D Sprint^® Client Version 3.0.0.2494) from a 3D printer (NextDent™ 5100, Vertex-Dental B.V., Soesterberg, The Netherlands). The printing layer thickness was 50 µm. Then, a total of twenty-eight (N = 28) stylized crowns were milled out of AmannGirrbach (Amann Girrbach GmbH, Pforzheim, Germany) (n = 7), Cercon HT (Dentsply Sirona, Bensheim, Germany) (n = 7), Cercon XT (Dentsply Sirona, Bensheim, Germany) (n = 7), and Vita YZ XT (Zahnfabrik, Bäd Sackingen, Germany) (n = 7). Following sintering the crowns, sandblasting was performed and they were bonded to the tooth dies with the resin cement (RelyX U-200, 3M ESPE, Seefeld, Germany) and permitted to self-cure under finger pressure for 6 min. The crowns were loaded on the occlusal surface in a universal testing machine (MTS Centurion) with a stainless-steel ball indenter (7 mm radius) with a loading rate of 1 mm/min to contact the stylized crowns on each of the four cusps until failure. A rubber sheet (1.5 mm thickness) was positioned between the crown and indenter, which helped with the load distribution. Statistical analysis was done using SPSS version 20 (IBM Company, Chicago, USA). The fracture loads were analyzed using Dunnett’s T3 test, and the number of cracks was analyzed using the Mann–Whitney U test among the groups. The significant level was set at p value = 0.05. The mean fracture loads were 3086.54 ± 441.74 N, 4804.94 ± 70.12 N, 3317.76 ± 199.80 N, and 2921.87 ± 349.67 N for AmannGirrbac, Cercon HT, Cercon XT, and Vita YZ XT, respectively. The mean fracture loads for the surfaces with the greatest number of cracks (excluding the occlusal surfaces) were on the lingual surface for AmannGirrbach and Cercon HT, on the distal and mesial for Cercon XT, and on the buccal for Vita YZ XT. We found that the AmannGirrbach had the most overall cracks. Cercon XT had the greatest number of occlusal cracks and appeared to be the most shattered. Cercon HT had the least number of cracks. In conclusion, Cercon HT presented the best strength properties, the highest fracture load, and no visible cracks. AmannGirrbach presented the lowest strength properties.

Comparative Stress Evaluation between Bilayer, Monolithic and Cutback All-Ceramic Crown Designs: 3D Finite Element Study

Different all-ceramic crown designs are available to perform indirect restoration; however, the mechanical response of each model should still be elucidated. The study aims to evaluate the stress distribution in three different zirconia crown designs using finite element analysis. Different three-dimensional molar crowns were simulated: conventional bilayer zirconia covered with porcelain, a monolithic full-contour zirconia crown, and the cutback modified zirconia crown with porcelain veneered buccal face. The models were imported to the computer-aided engineering (CAE) software. Tetrahedral elements were used to form the mesh and the mechanical properties were assumed as isotropic, linear and homogeneous materials. The contacts were considered ideal. For the static structural mechanical analysis, 100 N occlusal load was applied and the bone tissue was fixed. Maximum principal stress showed that the stress pattern was different for the three crown designs, and the traditional bilayer model showed higher stress magnitude comparing to the other models. However, grayscale stress maps showed homogeneous stress distribution for all models. The all-ceramic crown designs affect the stress distribution, and the cutback porcelain-veneered zirconia crown can be a viable alternative to adequate function and esthetic when the monolithic zirconia crown cannot be indicated.