A Comparitive Evaluation of the Effect of Sports and Fruit Drinks on the Surface Roughness of Nanofilled Composite and Light Cure GIC–An In Vitro Study

The Effect of Usage of Antiasthmatic Inhalers on Color Stability and Surface Roughness of Dental Restorative Materials: An In Vitro Study

OBJECTIVES

 Increased demand for esthetics by parents and children has resulted in the use of tooth-colored restorative materials. Children with chronic respiratory conditions like asthma use inhalers which have shown to affect the surface of restorative materials. Hence, the aim of the present study was to evaluate the effect of antiasthmatic inhalers on color stability and surface roughness of three restorative materials.

MATERIALS AND METHODS

 Forty samples each of three dental restorative materials: group A: glass ionomer cement (GIC), group B: alkasite restorative material, and group C: composite resins were prepared. Each group was further divided into two subgroups of 20 samples each according to the inhaler used. All the specimens were polished using polishing discs and stored in artificial saliva in order to simulate the oral environment. The baseline color value and surface roughness of all the samples were measured using a spectrophotometer and a profilometer, respectively. Group 1 and group 2 were exposed to 0.31 mg of salbutamol sulfate and 20 mg formoterol fumarate in combination with budesonide, respectively, for every 12 hours, for a period of 15 days following which the samples were evaluated for color changes and surface roughness.

STATISTICAL ANALYSIS

 The data obtained was subjected to statistical analysis and level of significance was set at p < 0.05.

RESULTS

 Exposure to both the inhalers caused a change in color and surface roughness in all three restorative materials. There was a significant change in the color of GIC and composite resin (ΔE > 3.3), following exposure to both the inhalers (p < 0.05). The change in color of alkasite restorative material was not significant. A significant increase in the surface roughness of composite resin from 0.56 ± 0.14 to 0.67 ± 0.19 was seen following 15 days' exposure to formoterol in combination with budesonide inhaler (p < 0.05).

CONCLUSION

 Following exposure, both the inhalers had an equal effect on color and surface roughness of all three restorative materials. Alkasite restorative material showed greater resistance to change in color and surface roughness when exposed to antiasthmatic inhalers, compared to GIC and composite resin. Thus, children who use inhalers and nebulizers should be advised to implement more precautionary oral hygiene measures and periodic dental visits.

In vitro surface and color changes of tooth-colored restorative materials after sport and energy drink cyclic immersions

BACKGROUND

There has not been any research conducted on surface properties and color changes from sport and energy drinks on bulk-fill resin composite, nanohybrid resin composite and glass ionomer restorative material. The aim of this in vitro study was to investigate the effect of sport and energy drinks on surface hardness, roughness and color changes of bulk-fill resin composite, nanohybrid resin composite and glass ionomer restorative material, and to also evaluate the acidity and titratable acidity of the drinks.

METHODS

One hundred and forty-seven specimens of each tooth-colored restorative material were prepared in a polytetrafluoroethylene mold (10 mm. in diameter and 2 mm. in thickness). Before immersion, baseline data of hardness, roughness, and color value were recorded. Each material was divided into 3 groups for sport drink, energy drink, and deionized water (serving as a control). The specimens were immersed in a storage agent for 5 s, then in artificial saliva for 5 s alternately for 24 cycles, and then stored in artificial saliva for 24 h. The immersion cycle was repeated for 14 days and hardness, roughness and color values were measured at 7 and 14 days.

RESULTS

After immersion, the glass ionomer restorative material had statistically less hardness, more roughness and more color changes than the others (P < 0.05). Energy drink groups statistically caused more surface and color changes than sport drink groups (P < 0.05).

CONCLUSION

Sport and energy drinks affected hardness, roughness, and color changes in all the tooth-colored restorative materials evaluated.

Conventional and Resin-Modified Glass Ionomer Cement Surface Characteristics after Acidic Challenges

The aim of the present study was to assess by atomic force microscopy (AFM) the surface roughness of a traditional glass ionomer cement- GIC (Fuji IX GP, GC Corporation, Tokyo, Japan) and a resin modified glass ionomer cement- RMGIC (Vitremer, 3M ESPE, St. Paul, MN, USA) after different immersion regimes on some acidic drinks. Sixteen cylindrical samples having the height of 5 mm and the thickness of 2 mm were obtained from each material and they were divided into two groups: Group I (Fuji IX samples) and Group II (Vitremer samples). Specimens of each group were then randomly divided into 4 subgroups: subgroup A (control)—15 samples were kept in artificial saliva and in the other three subgroups, each having 15 samples the samples were immersed in Coca-Cola (subgroup B), Cappy lemonade and mint (subgroup C) and Fuzetea (subgroup D) for 7 days (subgroups A1–D1), 14 days (subgroups A2–D2), and 21 days (subgroups A3–D3). AFM qualitative and quantitative surface evaluation (mean value of surface roughness parameter, Sa) of each sample was performed. The highest surface roughness was determined when both materials were submerged 14 days in acidic drinks. Traditional GIC was more affected by acidic environment when comparing to RMGIC.