Nano-hydroxyapatite could Compensate the Adverse Effect of soft carbonated Drinks on Enamel

Evaluation of shear bond strength and enamel remineralizing effect of experimental orthodontic composite containing nano-hydroxyapatite: An in vitro study

OBJECTIVE

The purpose of this study was to prepare an orthodontic composite containing hydroxyapatite nanoparticles to prevent demineralization and create a suitable environment for mineral deposition around orthodontic brackets, and to investigate the mechanical and remineralizing properties of the experimental adhesive composite.

METHODS

Experimental orthodontic composite were formulated using varying percentages of nano-hydroxyapatite particles. Assessments were based on four groups: a control group (3M™ Transbond™ XT) and experimental composites containing 2% (HA2), 5% (HA5) and 10% (HA10) hydroxyapatite. Vickers Microhardness test was performed to investigate the remineralizing effect in 3 stages: initial stage, after demineralization and after 4 weeks of exposure to artificial saliva. Scanning electron microscopy with energy dispersive X-ray spectroscopy analyser (SEM/EDAX) was used to evaluate hydroxyapatite precipitation and elemental composition of enamel surface. Shear Bond Strength tests were carried out using a universal testing machine and the debonding pattern was assessed using Adhesive Remnant Index (ARI).

RESULTS

All groups showed clinically acceptable SBS values. The highest SBS was achieved in the HA2 group, followed by Transbond™ XT, HA5 and HA10. There was no significant difference in the ARI scores. In terms of microhardness properties, HA5 and HA10 demonstrated a significant increase after 4 weeks. The results of SEM analysis showed the precipitation of hydroxyapatite crystals and EDAX analysis indicated the increase of calcium and phosphate ion peaks compared to the demineralized sample. The data were analysed using one-way ANOVA and Tukey's Post-hoc test.

CONCLUSIONS

Addition of hydroxyapatite nanoparticles to orthodontic composite can increase the mineral content and microhardness of the adjacent enamel. However, increasing the amount of nanoparticles reduces shear bond strength in a decreasing trend. The above-mentioned findings showed that incremental increase of nanoparticles of HA can be incorporated in composite to a certain extent and limitations are determined by mechanical properties (SBS) required for bracket bonding.

Biomimetic Effect of Nano-Hydroxyapatite in Demineralized Enamel before Orthodontic Bonding of Brackets and Attachments: Visual, Adhesion Strength, and Hardness in In Vitro Tests

Dietary habits with high consumption of acidic food can induce in orthodontic patients an increased risk of demineralization lesions around orthodontic brackets and bands. The purpose of the present laboratory study is to assess the in vitro visual efficacy of a biomimetic nano-hydroxyapatite remineralizing solution in a hypomineralized enamel surface and its effect on adhesion of fixed orthodontic appliances and on enamel microhardness. Intact teeth were demineralized, and subsequently the areas of demineralization were visually recorded using a 0-100 scale. Subsequently, a remineralizing solution (Biorepair® Repair Shock Treatment) was applied for ten minutes once a day/for one week per month for a total remineralizing treatment of 3 months. Visual effects were recorded. Moreover, bond strength was recorded and adhesive remnant index scores were measured for both orthodontic brackets and composite attachments both before demineralization and after demineralization and application of remineralizing solution. Also, Vickers microhardness was measured. All data were submitted to statistical analysis. The application of remineralizing solution induced a significant in vitro reduction of demineralized areas after the first week of application. No significant differences between untreated enamel surfaces and remineralized surfaces were detected after 2 months of remineralizing treatment. Bond strength values were significantly reduced for both brackets and attachments after remineralizing treatment. However, attachments showed higher adhesion values than brackets in both conditions tested. Remineralized enamel showed significantly higher microhardness values than demineralized enamel and lower values than intact enamel.

Effects of citric acid modified with fluoride, nano-hydroxyapatite and casein on eroded enamel

OBJECTIVES

The aim of this in vitro study was to evaluate the effects of citric acid containing fluoride, nano-hydroxyapatite, and casein on eroded enamel.

DESIGN

The crowns of 120 extracted bovine incisors were embedded in acrylic resin. An enamel window (2 × 3 mm) was created on the surface. Before in vitro pellicle formation samples were eroded in 1% citric acid (pH = 3.2) for 1 h at 36 °C and were randomly classified to eight groups (n = 15) as follows: Positive control: 1% citric acid, Negative control: Distilled water, F1: 0.047 mmol/L sodium fluoride, F2: 0.071 mmol/L sodium fluoride, NHA1: %0.05 Nano-Hydroxyapatite, NHA2: %0.1 Nano-Hydroxyapatite, C1: %0.02 Casein, C2: %0.2 Casein. Erosion cycling was performed three times daily for 3 days. In each cycle, the samples were immersed in 10 mL of control or modified solutions (10 min) and in 10 mL of artificial saliva (60 min). The surface roughness and enamel loss were analyzed by using profilometer, scanning electron microscopy (SEM) and atomic force microscopy techniques (AFM).

RESULTS

Among the groups, the positive control group was found to be having the highest erosive wear. Erosive wear in the F2, NHA2, C1, and C2 groups was not significantly different from the negative control group (p > 0.05). The C1 and C2 groups showed that erosion terminated and minimal tissue recovery occurred on the enamel surface.

CONCLUSION

Although all modifications reduced further demineralization, the citric acid modification with casein was found to be having a greater impact on dental erosion than the others.