ENTANGLED NETWORK INFLUENCED BY CARBON BLACK IN SOLUTION SBR VULCANIZATES REVEALED BY THEORY AND EXPERIMENT

Influence of the Polarity of the Plasticizer on the Mechanical Stability of the Filler Network by Simultaneous Mechanical and Dielectric Analysis

Four styrene butadiene rubber (SBR) compounds were prepared to investigate the influence of the plasticizer polarity on the mechanical stability of the filler network using simultaneous mechanical and dielectric analysis. One compound was prepared without plasticizer and serves as a reference. The other three compounds were expanded with different plasticizers that have different polarities. Compared with an SBR sample without plasticizer, the conductivity of mechanically unloaded oil-extended SBR samples decreases by an order of magnitude. The polarity of the plasticizer shows hardly any influence because the plasticizers only affect the distribution of the filler clusters. Under static load, the dielectric properties seem to be oil-dependent. However, this behavior also results from the new distribution of the filler clusters caused by the mechanical damage and supported by the polarity grade of the plasticizer used. The Cole–Cole equation affirms these observations. The Cole–Cole relaxation time τ  and thus, the position of maximal dielectric loss increases as the polarity of the plasticizer used is also increased. This, in turn, decreases the broadness parameter α implying a broader response function.

EFFECT OF CELLULOSE FIBER SURFACE TREATMENT TO REPLACE CARBON BLACK IN NATURAL RUBBER HYBRID COMPOSITES

In recent years, cellulose fibers have attracted considerable attention as biofillers for natural rubber (NR) composites. However, neat cellulose cannot be used as a substitute for conventional fillers due to its poor compatibility with NR. Therefore, a new surface treatment via maleic anhydride grafted to polyisoprene (MAPI) in solution was developed to improve the filler–matrix interaction. Different contents of carbon black (CB) and cellulose fibers (before and after modification) were used as a hybrid filler system to investigate the possibility of CB substitution in NR composites. First, contact angle, Fourier transformed infrared spectrometry (FTIR), and scanning electron microscopy (SEM) techniques were used to confirm the successful cellulose surface treatment. Second, morphological analysis, Payne effect, and swelling behavior of the rubber compounds in toluene confirmed the effect of cellulose treatment on improving the interfacial filler–matrix adhesion. Finally, the results showed that the composite filled with 20 phr modified cellulose and 20 phr CB (50% replacement of CB) exhibited even better results than the composite filled with 40 phr of CB, since the tensile strength was only 7% lower, but the elongation at break, tensile modulus at 100%, and storage modulus at 25 °C were respectively 35%, 24%, and 22% higher.