Makkeyah F, Elsahn NA, Bakr MM, Al Ankily M. Effect of Acidic Media on Surface Topography and Color Stability of Two Different Glass Ceramics. Eur J Dent 2024. [PMID: 38776980 DOI: 10.1055/s-0044-1786842] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 05/25/2024] Open
Abstract
OBJECTIVE The aim of this study was to determine the effect of two acidic beverages (orange juice and H3PO4-containing fizzy drink) on the surface topography and color stability of two commonly used computer-aided design/computer-aided manufacturing (CAD/CAM) ceramic materials. MATERIALS AND METHODS Sixty samples of two CAD/CAM ceramic materials, lithium disilicate (IPS e-max CAD) and zirconia reinforced lithium silicate (Vita Suprinity), were prepared according to the manufacturer's instructions. The samples were immersed in one of three media (artificial saliva, orange juice and H3PO4-containing fizzy drink) and then stored in an incubator at 37 °C for 24 hours). Before and after immersion in different media, the surface roughness (Ra) of the samples was assessed using profilometer (JITAI8101 Surface Roughness Tester-Beijing Jitai Tech Detection Device Co. Ltd, China) and the color parameters were measured using VITA Easyshade Advance 4.01 (VITA shade, VITA made, VITA). Surface topography was observed using scanning electron microscope (SEM) and surface mineral content was compared before and after immersion. Paired sample t-test was used to determine the change in Ra before and after immersion. Two-way analysis of variance was used to determine the effect of different CAD/CAM materials and immersion media on the mean ∆Ra and mean ∆E of the studied groups. Tukey's honest significant difference posthoc test was used for multiple comparisons at a level of significance (α = 0.05). RESULTS A significant increase in Ra and a decrease in the color stability of the two investigated ceramic materials were detected after immersion in the acidic media than in artificial saliva. SEM and energy-dispersive X-ray results revealed the dissolution of the glassy matrix and the exposure of silicate crystals. CONCLUSION The surface topography and color stability of glass ceramics are affected by the pH of different acidic media.
Collapse
Affiliation(s)
- Fatma Makkeyah
- Fixed Prosthodontics Department, Faculty of Dentistry, The British University in Egypt, Cairo, Egypt
| | - Nesrine A Elsahn
- Department of Clinical Sciences, College of Dentistry, Ajman University, Ajman, United Arab Emirates
- Center of Medical and Bio-allied Health Sciences Research, Ajman University, Ajman, United Arab Emirates
- Department of Operative Dentistry, Faculty of Dentistry, Cairo University, Cairo, Egypt
| | - Mahmoud M Bakr
- General Dental Practice, School of Medicine and Dentistry, Griffith University, Gold Coast, Queensland, Australia
| | - Mahmoud Al Ankily
- Oral Biology Department, Faculty of Dentistry, The British University in Egypt, Cairo, Egypt
| |
Collapse
|
2
|
Elraggal A, Abdelraheem IM, Watts DC, Roy S, Dommeti VK, Alshabib A, Althaqafi KA, Afifi RR. Biomechanical reinforcement by CAD-CAM materials affects stress distributions of posterior composite bridges: 3D finite element analysis. Dent Mater 2024; 40:869-877. [PMID: 38609774 DOI: 10.1016/j.dental.2024.04.001] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/17/2024] [Revised: 03/28/2024] [Accepted: 04/02/2024] [Indexed: 04/14/2024]
Abstract
OBJECTIVES This 3D finite element analysis study aimed to investigate the effect of reinforcing CAD-CAM bars on stress distribution in various components of a posterior composite bridge. METHODS A virtual model mimicking the absence of an upper second premolar was created, featuring class II cavity preparations on the proximal surfaces of the adjacent abutment teeth surrounding the edentulous space. Five distinct finite element analysis (FEA) models were generated, each representing a CAD-CAM reinforcing bar material: 3-YTZP (IPS. emax ZirCAD MO; Zr), lithium disilicate (IPS e.max CAD; EX), nano-hybrid resin composite (Grandio Blocs; GB), Fibre-reinforced composite (Trilor; Tri), and polyetheretherketone (PEEK). A veneering resin composite was employed to simulate the replacement of the missing premolar (pontic). In the FEA, an axial force of 600 N and a transverse load of 20 N were applied at the center of the pontic. Subsequently, maximum von Mises (mvM) and maximum principal stresses (σmax) were computed across various components of the generated models. Additionally, shear stresses at the interface between the CAD-CAM bars and the veneering resin composite were determined. RESULTS CAD-CAM materials with high modulus of elasticity, such as Zr and EX, exhibited the highest mvM stresses and shear stresses while transferring the lowest stress to the veneering resin composite in comparison to other materials. Conversely, PEEK demonstrated the lowest mvM stresses but produced the highest stresses within the veneering resin composite. There was a uniform distribution of mvM stresses in the remaining tooth structure among all groups, except for a noticeable elevation in the molar region of Zr and EX groups. SIGNIFICANCE Reinforcing CAD-CAM bar materials with a high modulus of elasticity, such as Zr and EX, may result in debonding failures at the connector sites of posterior composite bridges. Conversely, GB, PEEK, and Tri have the potential to cause fracture failures at the connectors rather than debonding.
Collapse
Affiliation(s)
- Alaaeldin Elraggal
- Division of Dentistry, School of Medical Sciences, Faculty of Biology, Medicine and Health, The University of Manchester, Manchester, UK; Conservative Dentistry Department, Faculty of Dentistry, Alexandria University, Alexandria, Egypt.
| | - Islam M Abdelraheem
- Conservative Dentistry Department, Faculty of Dentistry, Alexandria University, Alexandria, Egypt
| | - David C Watts
- Division of Dentistry, School of Medical Sciences, Faculty of Biology, Medicine and Health, The University of Manchester, Manchester, UK
| | - Sandipan Roy
- Department of Mechanical Engineering, SRM Institute of Science and Technology, Kattankulathur 603203, Tamil Nadu, India
| | - Vamsi Krishna Dommeti
- Department of Mechanical Engineering, SRM Institute of Science and Technology, Kattankulathur 603203, Tamil Nadu, India
| | - Abdulrahman Alshabib
- Restorative Dentistry Department, Faculty of Dentistry, King Saud University, Riyadh, Saudi Arabia
| | - Khaled Abid Althaqafi
- Restorative Dentistry Department, Faculty of Dentistry, College of Dental Medicine, University of Umm Al Qura, Makkah, Saudi Arabia
| | - Rania R Afifi
- Conservative Dentistry Department, Faculty of Dentistry, Alexandria University, Alexandria, Egypt
| |
Collapse
|
3
|
Elsahn NA, El-Damanhoury HM, Shirazi Z, Saleh ARM. Surface Properties and Wear Resistance of Injectable and Computer-Aided Design/Computer Aided Manufacturing-Milled Resin Composite Thin Occlusal Veneers. Eur J Dent 2023; 17:663-672. [PMID: 36220115 PMCID: PMC10569885 DOI: 10.1055/s-0042-1750769] [Citation(s) in RCA: 3] [Impact Index Per Article: 3.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 10/17/2022] Open
Abstract
OBJECTIVES This study was conducted to investigate the microhardness, surface roughness (Ra), and wear behavior of thin occlusal veneers (TOV) fabricated from different injectable composite materials and compare them to a Computer-Aided Design (CAD)/Computer-Aided Manufacturing (CAM) resin-based material. MATERIALS AND METHODS A 1-mm occusal veneer preparation was done in a mandibular right second molar typodont tooth. The prepared model was duplicated to fabricate 32 replicas and divided into four groups (n = 8). Standard TOV were fabricated either indirectly from Cerasmart blocks, Cerasmart, GC (CS), or directly from Beautifil Injectable X, Shofu (BF), G-ænial Universal injectable, GC (GU), or SonicFill 2, Kerr (SF) using the injection molding technique. All the specimens were subjected to both thermomechanical cyclic loading (TMC) in a chewing simulator. Wear measurement was conducted by three-dimensional (3D) scanning of the veneered models before and after TMC, and the difference in the volume of the sample was recorded as the volumetric material loss due to wear. Ra before and after TMC and Vickers microhardness (VHN) of the tested materials were measured using standardized samples (n = 8). Representative samples from each group were investigated under a stereomicroscope and a scanning electron microscope. STATISTICAL ANALYSIS One-way analysis of variance (ANOVA) was applied to detect the effect of material on VHN and wear. Two-way ANOVA was utilized to examine the impact of material and TMC on Ra. Multiple comparisons between the groups were conducted using Tukey's post hoc test (α = 0.05). The Pearson's correlation coefficient was used to determine the relationship between hardness and wear and between roughness and wear (α = 0.05). RESULTS CS exhibited the highest mean VHN (p ≤ 0.001), followed by GU and SF which were statistically similar (p = 0.883) but significantly higher than BF (p < 0.001). After TMC, GU revealed the lowest Ra and volumetric wear (VW), followed by CS, BF, and SF (p < 0.5). A highly significant correlation existed between Ra and VW (p = 0.001, R 2 = 0.9803). CONCLUSION The effect of TMC on the surface properties and wear resistance of the investigated TOV is material-dependent. GU injectable TOV are less influenced by TMC than CS milled TOV. In contrast, BF and SF demonstrated significant VW and Ra which might limit their clinical use as TOV.
Collapse
Affiliation(s)
- Nesrine A. Elsahn
- Department of Clinical Sciences, College of Dentistry, Ajman University, Ajman, United Arab Emirates
- Center of Medical and Bio-allied Health Sciences Research, Ajman University, Ajman, United Arab Emirates
- Department of Operative Dentistry, Faculty of Dentistry, Cairo University, Cairo, Egypt
| | - Hatem M. El-Damanhoury
- Department of Preventive and Restorative Dentistry, College of Dental Medicine, University of Sharjah, Sharjah, United Arab Emirates
| | - Zainab Shirazi
- Center of Medical and Bio-allied Health Sciences Research, Ajman University, Ajman, United Arab Emirates
| | - Abdul Rahman M. Saleh
- Department of Clinical Sciences, College of Dentistry, Ajman University, Ajman, United Arab Emirates
- Center of Medical and Bio-allied Health Sciences Research, Ajman University, Ajman, United Arab Emirates
| |
Collapse
|
4
|
Elraggal A, R Afifi R, Alamoush RA, Raheem IA, Watts DC. Effect of acidic media on flexural strength and fatigue of CAD-CAM dental materials. Dent Mater 2023; 39:57-69. [PMID: 36496258 DOI: 10.1016/j.dental.2022.11.019] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 08/08/2022] [Revised: 11/13/2022] [Accepted: 11/25/2022] [Indexed: 12/12/2022]
Abstract
OBJECTIVE To investigate the effect of acidic media, including beverages and gastric fluids on flexural strength and fatigue of CAD-CAM materials. METHODS Four CAD-CAM materials (high-translucency zirconia (Ceramill Zolid HT+), lithium disilicate (IPS e-max CAD), hybrid ceramic (Vita Enamic), and nanohybrid resin composite (Grandio Blocs) were prepared and immersed in one of five media (gastric HCl, white wine, Coca-Cola, orange juice, and artificial saliva) in an incubator (37 ℃, 24 h). Surface topography and roughness were obtained using a scanning electron microscope (SEM) and a stylus contact profilometer, respectively. Initial 3-point flexural strength was measured for half of the bars (n = 20/gp) using a universal testing machine (0.5 mm/min). The other bars underwent 106 cyclic fatigue loadings before measurement of residual 3-point flexural strength. Data were statistically analyzed (two-way and three-way ANOVA, Tukey's post-hoc, p < 0.05). Weibull distributions were plotted for reliability analysis. RESULTS Zirconia bars has the highest initial flexural strengths followed by lithium disilicate, while resin composite and hybrid ceramic groups had the lowest strength regardless of the erosive medium. Cyclic fatigue significantly reduced initial flexural strengths for all materials except for hybrid ceramic and resin composite. Weibull moduli were the highest for zirconia, lithium disilicate and resin composite and lowest for hybrid ceramic. SIGNIFICANCE Erosive media significantly changed surface roughness of CAD-CAM materials except for zirconia and resin composite without jeopardizing the flexural strength of the CAD-CAM materials. Despite the higher flexural strengths for zirconia and lithium disilicate, resin composite and hybrid ceramic were more resistant to cyclic fatigue.
Collapse
Affiliation(s)
- Alaaeldin Elraggal
- Conservative Dentistry Department, Faculty of Dentistry, Alexandria University, Alexandria, Egypt.
| | - Rania R Afifi
- Conservative Dentistry Department, Faculty of Dentistry, Alexandria University, Alexandria, Egypt
| | - Rasha A Alamoush
- Department of Prosthodontics, School of Dentistry, The University of Jordan, Amman, Jordan
| | - Islam Abdel Raheem
- Conservative Dentistry Department, Faculty of Dentistry, Alexandria University, Alexandria, Egypt
| | - David C Watts
- School of Medical Sciences, University of Manchester, Manchester, UK
| |
Collapse
|
5
|
Ramos RQ, Coelho NF, Lopes GC. Three-year Follow-up of Conservative Direct Composite Veneers on Eroded Teeth. Oper Dent 2022; 47:131-137. [PMID: 35290465 DOI: 10.2341/20-308-s] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Accepted: 03/20/2021] [Indexed: 11/23/2022]
Abstract
This clinical case describes an esthetic rehabilitation of a young patient presenting with erosive tooth wear. The etiological factors for the erosion in this clinical case was excessive carbonated beverages and lemon water intake. The patient's main complaint was the yellowish aspect of her smile. The treatment procedure selected was direct resin composite veneers in the six maxillary anterior teeth. A three-year follow-up of the case is presented. The three-year follow-up showed a successful clinical performance of the treatment procedure after a finishing/polishing protocol.
Collapse
Affiliation(s)
- R Q Ramos
- *Renato Quirino Ramos, DDS, MSD, Department of Dentistry, Federal University of Santa Catarina (UFSC), Campus Trindade, Florianópolis, Santa Catarina, Brazil
| | - N F Coelho
- Natalia Fiuza Coelho, DDS, MSD, Department of Dentistry, Federal University of Santa Catarina (UFSC), Florianópolis, Santa Catarina, Brazil
| | - G C Lopes
- Guilherme Carpena Lopes, DDS, MSD, PhD, Department of Dentistry, Federal University of Santa Catarina (UFSC), Florianópolis, SC, Brazil
| |
Collapse
|
6
|
Alencar MF, Pereira MT, De-Moraes MDR, Santiago SL, Passos VF. The effects of intrinsic and extrinsic acids on nanofilled and bulk fill resin composites: Roughness, surface hardness, and scanning electron microscopy analysis. Microsc Res Tech 2019; 83:202-207. [PMID: 31729109 DOI: 10.1002/jemt.23403] [Citation(s) in RCA: 6] [Impact Index Per Article: 1.2] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 10/26/2018] [Revised: 09/25/2019] [Accepted: 10/22/2019] [Indexed: 11/08/2022]
Abstract
The objective of this study was to examine the effects of extrinsic or intrinsic acids on nanofilled and bulk fill resin materials in vitro. A total of 90 disks were prepared using dental restorative material (Filtek Z350XT, GrandioSO, Filtek Bulk Fill, X-tra fil). Thirty disks of each material were sub-divided into three groups (n = 10) that were immersed for 7 days in deionized water (DW), 5% citric acid (CA-pH 2.1), or 0.1% hydrochloric acid (HCl-pH = 1.2). Surface hardness and roughness (stylus profilometer by Ra parameter) analysis were performed before and after immersion. Morphological changes were evaluated by scanning electron microscopy. The data were analyzed by two-way ANOVA and Tukey's test (α = 0.05). All tested materials did not show significant differences in the effects of the DW, CA, or HCl solutions on surface roughness (p = .368). Likewise, the hardness loss was not affected by the solutions tested (p = .646), but there was a difference in the resin type (p = .002). Filtek Bulk Fill resin hardness was less affected, while Filtek Z350XT and GrandioSO presented the most hardness loss after 7 days of solution immersion. In terms of this experimental study, the results demonstrate the effectiveness of the mechanical properties (roughness and hardness surface) of nanofilled and bulk fill resin materials to resist erosion from extrinsic and intrinsic acids, therefore being potential candidates for dental applications.
Collapse
Affiliation(s)
- Milena F Alencar
- Doctor of Dental Surgery, School of Dentistry, University of Fortaleza, Fortaleza, Brazil
| | - Mirella T Pereira
- Doctor of Dental Surgery, School of Dentistry, University of Fortaleza, Fortaleza, Brazil
| | | | - Sérgio L Santiago
- Department of Restorative Dentistry, Federal University of Ceara, Faculty of Pharmacy, Dentistry and Nursing, Fortaleza, Brazil
| | - Vanara F Passos
- Department of Restorative Dentistry, Federal University of Ceara, Faculty of Pharmacy, Dentistry and Nursing, Fortaleza, Brazil
| |
Collapse
|