Effect of ultrasonic agitation on push-out bond strength and adaptation of root-end filling materials

Impact of different disinfection protocols on the bond strength of NeoMTA 2 bioceramic sealer used as a root canal apical plug (in vitro study)

INTRODUCTION

Treatment of an immature permanent tooth required a special disinfection protocol due to the presence of thin radicular walls, which are prone to fracture. Mineral Trioxide Aggregate (MTA) has been proposed as a root repair material for root canal treatment. The aim of this in vitro study was to compare the push-out bond strength of conventional White MTA cements and second generation NeoMTA 2 in imitated immature roots treated with different disinfection protocols, which are 5.25% sodium hypochlorite (NaOCl), followed by 17% ethylenediaminetetraacetic acid (EDTA), and NaOCl, followed by 20% etidronic acid (HEBP).

METHODS

The root canals of freshly extracted single-root teeth were manually prepared until 90 K-file to imitate immature roots. Roots were randomly divided into four groups (G) according to the disinfection protocol (n = 15 per group). where G1 (NaOCl + EDTA + White MTA) and G2 (NaOCl + EDTA + NeoMTA 2) While G3 (NaOCl + HEBP + White MTA) and G4 (NaOCl + HEBP + NeoMTA 2) All groups were activated with manual agitation. All specimens were incubated for 48 h. The apical third of each root was perpendicularly sectioned to attain a slice of 3 mm thickness. Push-out bond strength values were assessed using a two-way ANOVA and a Student's t test.

RESULTS

G3 and G4 that were treated with HEPB showed higher significant push-out bond strength mean values than G1 and G2 treated with an EDTA chelating agent. Irrespective of the chelating agent used, it was found that both NeoMTA 2 and White MTA had no significant influence on push-out bond strength mean values (p ≤ 0.05).

CONCLUSION

The combined use of 5.25% NaOCl and 20% HEBP increased the push-out strength values of both NeoMTA 2 and White MTA, rendering them suitable to be used as an alternative chelating agent to EDTA.

Effect of ultrasonic activation on setting time, pH and calcium ion release, solubility, and chemical structure of calcium silicate sealers

This study evaluated the setting time, pH, calcium ion release, solubility, and chemical structure of four calcium silicate sealers after ultrasonic activation (UA). Five sealers were evaluated: Sealer Plus (SP - control); Sealer Plus BC (SPBC), Bio C Sealers (BCS), Endosequence BC Sealer (EBC), and BioRoot RCS (BR). Ten groups were created based on the use or not of ultrasonic activation: SP; SP/UA; SPBC; SPBC/UA; BCS; BCS/UA; EBC; EBC/UA; BR; and BR/UA. Setting time was performed based on ISO 6876:2012 and ASTM C266-07 specifications. Solubility at 24hs, based on ISO 6876:2012. pH and calcium release were evaluated at 1, 24, 72, and 168hs. Raman spectroscopy was used to evaluate structural changes. Quantitative data were analyzed using One-Way ANOVA and Tukey post-hoc test (α=5%). Raman spectroscopy results were qualitatively analyzed. Setting times and solubility of all sealers were not affected by UA (p>0.05). The highest solubility was found for BCS, BCS/UA; and BR, BR/UA (p<0.05). After 24hs, calcium silicate sealers had higher pH than SP and SP/UA (p<0.05). BR and BR/UA had the highest pH at all time points. SP and SP/UA had stable pH at all time points. SP and SP/UA had the lowest calcium release values at all time points (p<0.05). EBC and EBC/UA calcium release significantly differ at 24,72 and 168hs (p<0.05). No chemical changes were observed during Raman spectroscopy. In conclusion, ultrasonic activation affected calcium ion release only for EndoSequence BC Sealer. Ultrasonic activation did not influence the initial and final setting time, solubility, pH, and chemical structure of any investigated sealers.

Effect of Endo-Z bur or Bladesonic ultrasonic tip on the adaptation of filling material. A micro-CT study

This study aimed to evaluate the effect of apicoectomy performed with a bur or an ultrasonic tip on the adaptation of the filling material to root canal dentin. Twenty human mandibular incisors were selected and prepared with a ProDesign Logic system up to diameter 40/.05. The root canals were filled with Bio-C Sealer (Angelus, PR, Brazil) using the single cone technique and were stored at 37ºC and 95% relative humidity for 7 days. After this period, the apicoectomy of the 3 millimeters of the root apex was performed using Endo-Z bur (Dentsply Sirona) or Bladesonic ultrasonic tip (Helse Ultrasonic, Santa Rosa de Viterbo, Brazil) (n=10). The specimens were scanned by micro-computed tomography (micro-CT; SkyScan 1176) with a voxel size of 8.74 µm after obturation and after apicoectomy. The percentage of voids at the interface between the filling material and the root canal wall was evaluated in the apical 4 mm of the root after apicoectomy, besides the time cutting to both devices. The data obtained were submitted to paired and unpaired t-tests (α = 0.05). Endo-Z and Bladesonic increased the percentage of voids between the filling material and the dentin after apicectomy (p<0.05), and they were similar (p>0.05). Endo-Z has a shorter time to perform apicoectomy compared to Bladesonic (p<0.05). Apicectomies with Endo-Z or Bladesonic could harm the material/dentin interface, while the Endo-Z bur was faster than the Bladesonic ultrasonic tip.

Effect of Different Mixing Methods on Physicochemical Properties of Mineral Trioxide Aggregate: A Systematic Review

Background

Mineral trioxide aggregate (MTA) is a commonly used endodontic biomaterial. The physicochemical properties of MTA have a crucial role in designating clinical outcome, and different factors can affect these properties. Various methods have been used for mixing MTA, including manual, mechanical, and ultrasonic. The aim of this systematic review was to evaluate the effect of different mixing methods on the physicochemical properties of MTA.

Materials and Methods

Electronic databases including PubMed, Embase, Web of Science, and Scopus were searched up to May 2022. In order to cover gray literature, the ProQuest and Google Scholar databases were also searched to detect theses and conference proceedings. For quality assessment of the included studies, we used a modified version of the Cochrane risk of bias tool for randomized controlled trials (RCTs). Experimental studies which had assessed at least one property of MTA and compared at least two different mixing methods of MTA were included in this study. All animal studies, reviews, case reports, and case series were excluded.

Results

Fourteen studies were included. The results showed that the ultrasonic mixing method significantly improved some MTA characteristics, including microhardness, flowability, solubility, setting time, and porosity. However, the mechanical mixing method improved other properties including flowability, solubility, push-out bond strength, and hydration. The manual mixing method showed inferior results compared to other mixing methods in terms of microhardness, flowability, solubility, setting time, push-out bond strength, porosity, and hydration. Different mixing methods had a similar effect on compressive strength, sealing ability, pH and calcium ion release, volume change, film thickness, and flexural strength of MTA.

Conclusion

Mechanical and ultrasonic mixing methods are superior to the manual mixing method in terms of improving physicochemical properties of MTA. No report of selection bias and varieties in methodologies were limitations of evidence.

Micro-CT comparative evaluation of porosity and dentin adaptation of root end filling materials applied with incremental, bulk, and ultrasonic activation techniques

The purpose of this study is to investigate the effect of different application methods on the adaptation to dentin and porosity properties of calcium silicate based materials. This study included 72 maxillary canine teeth that had been extracted for various reasons. Following the root canal treatment, root, end resections were performed on the specimens. After the apicectomy, 3 mm deep cavities were created. All materials were mixed according to the manufacturer's instructions. Retrograde cavities were filled with RetroMTA [Group 1a-1c], Biodentine [Group 2a-2c] and BioAggregate [Group 3a-3c]. Placement techniques were applied for each material by using incremental, bulk technique and ultrasonic activation, respectively. The samples were scanned with the SkyScan 1272 μCT system. Porosity values were higher in bulk fill and incremental placement techniques than ultrasonic technique when using MTA and BioAggregate (p < 0.05), but Biodentine showed no statistically significant difference (p > 0.05) on using different placement techniques. The ultrasonic activation technique is beneficial to improve the condensation quality of MTA and BioAggregate. Biodentine showed better results regardless of different application techniques.

Influence of Ultrasonic Activation on the Physicochemical Properties of Calcium Silicate-Based Cements

Purpose

To evaluate the influence of ultrasonic activation on the physicochemical properties of setting time (ST), flow (FL), dimensional change (DC), and solubility (SL) of the cements: MTA, MTA Repair HP, and Biodentine®.

Materials and Methods

Two experimental groups were formed according to the cement activation protocol: without ultrasonic activation and with ultrasonic activation. Cements were manipulated according to the manufacturers' instructions. Ultrasonic activation group was performed with an E1 insert at power 3 (24–32 kHz) for 30 s directly in the center of the cement mass. The molds for analysis of the physicochemical properties were filled out and evaluated according to specification No. 57 from ANSI/ADA. The results were analyzed using the ANOVA test (two-way), complemented by Tukey's test (α = 0.05). The distilled water used during the solubility test was submitted to spectrometry to verify the release of calcium ions. The morphologies of the external surface and the cross-section of the samples were analyzed by means of a scanning electron microscope (SEM).

Results

For the ST, ultrasonic activation reduced the values of MTA, MTA Repair HP, and Biodentine (P < 0.05). For the FL, ultrasonic activation did not alter the flow of MTA (P > 0.05); however, it increased the flow MTA Repair HP and Biodentine (P < 0.05). For the DC, the percentage values of dimensional change were higher when there was ultrasonic activation in all repair cements (P < 0.05). For SL, there was a reduction in the percentage of the values in MTA and MTA Repair HP (P < 0.05); however, there was no change in the values of Biodentine (P > 0.05). Ultrasonic activation favored the release of calcium ions from all cements. The SEM analysis showed, in general, that the ultrasonic activation reduced and altered the particle shape of the cement.

Conclusions

The ultrasonic activation interfered in the ST, DC, FL, ultrastructural morphology, and calcium release of the repair cements. However, it did not affect the solubility of Biodentine®.

Effect of ultrasonic activation of the adhesive system on dentin tubule penetration and the pushout bond strength of fiber posts

STATEMENT OF PROBLEM

Whether ultrasonic activation of the adhesive system improves dentin tubule penetration and the bond strength of fiber posts to root dentin is unclear.

PURPOSE

The purpose of this in vitro study was to evaluate the effect of ultrasonic activation of 2 adhesive systems (etch-and-rinse and self-etch) and 1 glass ionomer cement on the dentin tubule penetration and pushout bond strength of fiber posts to root dentin.

MATERIAL AND METHODS

Sixty maxillary central incisors were endodontically treated and divided into 6 groups (n=10) as per the post cementation strategy: etch-and-rinse, etch-and-rinse and ultrasonic, self-etch, self-etch and ultrasonic, glass ionomer cement, and glass ionomer cement and ultrasonic. The primers, the adhesives, and the glass ionomer cement were activated for 20 seconds each, and the fiber posts were cemented with a resin cement. Dentin tubule penetration was evaluated by confocal laser scanning microscopy and the pushout bond strength measured at 3 post locations: cervical, middle, and apical. The failure patterns were also described after pushout testing.

RESULTS

Self-etch and ultrasonic showed higher dentin tubule penetration than the other cementation strategies (P<.05) and improved the bond strength values (P<.05), which were higher than etch-and-rinse and ultrasonic and glass ionomer cement and ultrasonic (P<.05). Adhesive failures at the cement and dentin interface were predominant in the etch-and-rinse, self-etch, and self-etch and ultrasonic groups.

CONCLUSIONS

Ultrasonic activation improved the dentin tubule penetration of a self-etch adhesive system. The bond strength of fiber posts cemented with a self-etch adhesive system and a resin cement was improved after ultrasonic activation.

Dental discoloration caused by Grey-MTAFlow cement: analysis of its physicochemical, biological and antimicrobial properties

Tricalcium silicate-based cement are materials used in reparative and regenerative procedures in endodontics. A recently proposed formulation aimed to enhance handling during clinical use with a versatile material applicable by syringe. Although, the use of bismuth oxide as radiopacifier and grey raw powder are drawbacks considering aesthetics.

Effect of Ultrasonic Activation of Endodontic Sealers on Intratubular Penetration and Bond Strength to Root Dentin

INTRODUCTION

This study aimed to evaluate the effect of ultrasonic activation (UA) of endodontic sealers on dentin tubule penetration and the bond strength to root dentin.

METHOD

One hundred single-rooted teeth were prepared with 40.06 nickel-titanium instruments and divided into 2 groups: with or without UA. Three resin-based sealers (MTA Fillapex [Angelus Dental Solutions, Londrina, PR, Brazil], Sealer Plus [MK Life Medical and Dental Products, Porto Alegre, RS, Brazil], and AH Plus [Dentsply, DeTrey GmbH, Konstanz, Germany]; n = 20) and 2 calcium silicate-based sealers (Sealer Plus BC [MK Life Medical and Dental Products] and EndoSequence BC [Brasseler, Savannah, GA], n = 20) were used and subdivided (n = 10) according to the protocols. Fluo-3 (Thermo Fisher Scientific, Waltham, MA) and rhodamine B dyes were added to the calcium silicate- and resin-based sealers, respectively. In the UA groups, the activation was performed for 40 seconds followed by lateral compaction. Samples were transversely sectioned to evaluate the dentin tubule penetration and the bond strength to root dentin. The penetration data were analyzed with the Student t test, 1-factor analysis of variance, and Bonferroni tests. Bond strength was evaluated using the Student t test, Kruskal-Wallis, and Dunn post hoc test.

RESULTS

Resin-based sealers showed the highest tubule penetration without UA (P < .05). UA significantly enhanced MTA Fillapex and Endosequence BC dentin tubule penetration (P < .05). AH Plus and Sealer Plus BC improved their bond strength to root dentin after UA (P < .05). AH Plus/UA, Sealer Plus/UA, and Sealer Plus BC/UA presented the highest bond strength values (P < .05). Adhesive failures were predominant in all groups regardless of the use of ultrasound.

CONCLUSIONS

UA interferes with tubule penetration and the bond strength to root dentin of resin- and calcium silicate-based sealers.

Micro-computed tomographic evaluation of the flow and filling ability of endodontic materials using different test models

Objectives

This study compared the flow and filling of several retrograde filling materials using new different test models.

Materials and Methods

Glass plates were manufactured with a central cavity and 4 grooves in the horizontal and vertical directions. Grooves with the dimensions used in the previous study (1 × 1 × 2 mm; length, width, and height respectively) were compared with grooves measuring 1 × 1 × 1 and 1 × 2 × 1 mm. Biodentine, intermediate restorative material (IRM), and mineral trioxide aggregate (MTA) were evaluated. Each material was placed in the central cavity, and then another glass plate and a metal weight were placed over the cement. The glass plate/material set was scanned using micro-computed tomography. Flow was calculated by linear measurements in the grooves. Central filling was calculated in the central cavity (mm³) and lateral filling was measured up to 2 mm from the central cavity.

Results

Biodentine presented the least flow and better filling than IRM when evaluated in the 1 × 1 × 2 model. In a comparison of the test models, MTA had the most flow in the 1 × 1 × 2 model. All materials had lower lateral filling when the 1 × 1 × 2 model was used.

Conclusions

Flow and filling were affected by the size of the test models. Higher grooves and materials with greater flow resulted in lower filling capacity. The test model measuring 1 × 1 × 2 mm showed a better ability to differentiate among the materials.