Influence of demographic, surgical and implant variables on wear rate and osteolysis in ABG I hip arthroplasty

Particle disease: biologic mechanisms of periprosthetic osteolysis in total hip arthroplasty

Numerous studies provide detailed insight into the triggering and amplification mechanisms of the inflammatory response associated with prosthetic wear particles, promoting final dominance of bone resorption over bone formation in multiple bone multicellular units around an implant. In fact, inflammation is a highly regulated process tightly linked to simultaneous stimulation of tissue protective and regenerative mechanisms in order to prevent collateral damage of periprosthetic tissues. A variety of cytokines, chemokines, hormones and specific cell populations, including macrophages, dendritic and stem cells, attempt to balance tissue architecture and minimize inflammation. Based on this fact, we postulate that the local tissue homeostatic mechanisms more effectively regulate the pro-inflammatory/pro-osteolytic cells/pathways in patients with none/mild periprosthetic osteolysis (PPOL) than in patients with severe PPOL. In this line of thinking, 'particle disease theory' can be understood, at least partially, in terms of the failure of local tissue homeostatic mechanisms. As a result, we envision focusing current research on homeostatic mechanisms in addition to traditional efforts to elucidate details of pro-inflammatory/pro-osteolytic pathways. We believe this approach could open new avenues for research and potential therapeutic strategies.

Risk factors for accelerated polyethylene wear and osteolysis in ABG I total hip arthroplasty

We analysed data from 155 revisions of identical cementless hip prostheses to determine the influence of patient-, implant- and surgery-related factors on the polyethylene wear rate and size of periprosthetic osteolysis (OL). This was calculated by logistic regression analysis. Factors associated with an increased/decreased wear rate included position of the cup relative to Kohler's line, increase in abduction angle of the cup, traumatic and inflammatory arthritis as a primary diagnosis, and patient height. Severe acetabular bone defects were predicted by an increased wear rate (odds ratio, OR = 5.782 for wear rate above 200 mm(3)/y), and increased height of the patient (OR = 0.905 per each centimetre). Predictors of severe bone defects in the femur were the increased wear rate (OR = 3.479 for wear rate above 200 mm(3)/y) and placement of the cup outside of the true acetabulum (OR = 3.292). Variables related to surgical technique were the most predictive of polyethylene wear rate.

Poor survival of ABG I hip prosthesis in younger patients

BACKGROUND

Hydroxyapatite coated (HAC) hip implants have been used in clinical practice for more than two decades. However, the majority of studies have reported only intermediate term outcomes that are not reliable for predicting long-term behavior in all implants. The aim of this study was to determine the performance of HAC total hip arthroplasty in younger patients over a 10-year follow-up period.

METHODS AND RESULTS

This was an observational retrospective study of a 137 consecutive hips with the ABG I prosthesis. Of these, 128 were available for the last investigation. Median duration of follow-up was 10.9 years. The mean age at time of index surgery was 46+/-6.7 years. Probability of implant survival was estimated using the Kaplan-Meier method. The overall 12-year cumulative survival was 0.55 (95% CI, 0.443-0.659). Periprosthetic osteolysis (57 %) was the most frequent reason for failure followed by aseptic loosening (28 %). When only aseptic loosening was included in the analysis, the same figures for cup and stem were 0.873 (95% CI, 0.808-0.938) and 0.992 (95% CI, 0.976- 1.0), respectively. Patients with a smaller cup size were those at high risk for revision due to wear-related complications (odds ratio, OR=4.3; 95% CI, 1.734-10.555).

CONCLUSION

This study reports one of the poorest 12-year survivorship data for cementless acetabular component in the literature. The main reason for premature failure was osteolysis, strongly related to high wear rate of polyethylene.