Heat generated during dental treatments affecting intrapulpal temperature: a review

INTRODUCTION

Heat is generated and transferred to the dentine-pulp complex during various dental procedures, such as from friction during cavity preparations, exothermic reactions during the polymerisation of restorative materials and when polishing restorations. For in vitro studies, detrimental effects are possible when intra-pulpal temperature increases by more than 5.5°C (that is, the intra-pulpal temperature exceeds 42.4°C). This excessive heat transfer results in inflammation and necrosis of the pulp. Despite numerous studies stating the importance of heat transfer and control during dental procedures, there are limited studies that have quantified the significance. Past studies incorporated an experimental setup where a thermocouple is placed inside the pulp of an extracted human tooth and connected to an electronic digital thermometer.

METHODS

This review identified the opportunity for future research and develop both the understanding of various influencing factors on heat generation and the different sensor systems to measure the intrapulpal temperature.

CONCLUSION

Various steps of dental restorative procedures have the potential to generate considerable amounts of heat which can permanently damage the pulp, leading to pulp necrosis, discoloration of the tooth and eventually tooth loss. Thus, measures should be undertaken to limit pulp irritation and injury during procedures. This review highlighted the gap for future research and a need for an experimental setup which can simulate pulp blood flow, temperature, intraoral temperature and intraoral humidity to accurately simulate the intraoral conditions and record temperature changes during various dental procedures.

Cutting Efficiency of Welded Diamond and Vacuum Diffusion Technology Burs and Conventional Electroplated Burs on the Surface Changes of the Teeth - An In vitro Study

Context:

Welded diamond and vacuum diffusion technology (WDVDT) burs in comparison to electroplated burs claim to approach the solution of dental hard tissues by increased cutting efficiency, decreasing the overheating of oral tissues and thus reducing the microcracks on the prepared tooth surface.

Aims:

This study aimed to evaluate the cutting efficiency of two different rotary diamond burs used for tooth preparation with their repeated usage on the surface changes of the prepared tooth.

Settings and Design:

This in vitro comparative study evaluated the cutting efficiency and surface changes of the teeth prepared with conventional electroplated burs and WDVDT burs.

Subjects and Methods:

Thirty freshly extracted, healthy, noncarious human premolars were divided into Group A and Group B with 15 each, and were further subdivided into three subgroups depending on the different usage intervals as first, fifth, and tenth (A1–A3 and B1–B3). The surface of each prepared specimen was evaluated quantitatively using a surface profilometer, and qualitative analysis was done using a scanning electron microscope.

Statistical Analysis Used:

Two-way ANOVA and Turkey's multiple post hoc tests were used.

Results:

The mean surface roughness of Groups A1, A2, and A3 was 1.50 ± 0.40, 2.39 ± 0.39, and 2.65 ± 0.65 Ra, respectively. The mean surface roughness of Groups B1, B2, and B3 was 0.76 ± 0.23, 0.92 ± 0.10, and 1.24 ± 0.07 Ra, respectively. The mean surface roughness of the prepared tooth surface was significantly higher in Group A and its subgroups when compared to that of Group B and its subgroups.

Conclusions:

The study results showed that surface roughness was considerably lesser and also had less wear and increased cutting efficiency of tooth preparations using burs made with WDVDT compared to the preparations using conventional electroplated burs.

What is the changing frequency of diamond burs?

PURPOSE

The purpose of this study was to determine the changing frequency of a diamond bur after multiple usages on 3 different surfaces.

MATERIALS AND METHODS

Human premolar teeth (N = 26), disc shaped direct metal laser sintered CoCr (N = 3) and zirconia specimens (N = 3) were used in this study. Groups named basically as Group T for teeth, Group M for CoCr, and Group Z for zirconia. Round tapered black-band diamond bur was used. The specimens were randomly divided into three groups and placed with a special assembly onto the surveyor. 1, 5, and 10 preparation protocols were performed to the first, second, and third sub-groups, respectively. The subgroups were named according to preparation numbers (1, 5, 10). The mentioned bur of each group was then used at another horizontal preparation on a new tooth sample. The same procedure was used for CoCr and zirconia disc specimens. All of the bur surfaces were evaluated using roughness analysis. Then, horizontal tooth preparation surfaces were examined under both stereomicroscope and SEM. The depth maps of tooth surfaces were also obtained from digital stereomicroscopic images. The results were statistically analyzed using One-Way ANOVA, and the Tukey HSD post-hoc tests (α=.05).

RESULTS

All of the groups were significantly different from the control group (P<.001). There was no significant difference between groups Z5 and Z10 (P=.928). Significant differences were found among groups T5, M5, and Z5 (P<.001).

CONCLUSION

Diamond burs wear after multiple use and they should be changed after 5 teeth preparations at most. A diamond bur should not be used for teeth preparation after try-in procedures of metal or zirconia substructures.