Comparison of the Effect of Dentin Bonding, Dentin Sealing Agents on the Microleakage of Provisional Crowns Fabricated with Direct and Indirect Technique-An Invitro Study

In vitro fatigue and fracture testing of temporary materials from different manufacturing processes in implant-supported anterior crowns

OBJECTIVES

The aim of this study was to investigate the in vitro fatigue and fracture force of temporary implant-supported anterior crowns made of different materials with different abutment total occlusal convergence (TOC), with/without a screw channel, and with different types of fabrication.

MATERIALS AND METHODS

One hundred ninety-two implant-supported crowns were manufactured (4° or 8° TOC; with/without screw channel) form 6 materials (n = 8; 2 × additive, 3 × subtractive, 1 × automix; reference). Crowns were temporarily cemented, screw channels were closed (polytetrafluoroethylene, resin composite), and crowns were stored in water (37 °C; 10 days) before thermal cycling and mechanical loading (TCML). Fracture force was determined.

STATISTICS

Kolmogorov-Smirnov, ANOVA; Bonferroni; Kaplan-Meier; log-rank; α = 0.05.

RESULTS

Failure during TCML varied between 0 failures and total failure. Mean survival was between 1.8 × 105 and 4.8 × 105 cycles. The highest impact on survival presented the material (η2 = 0.072, p < .001). Fracture forces varied between 265.7 and 628.6 N. The highest impact on force was found for the material (η2 = 0.084, p < .001).

CONCLUSION

Additively and subtractively manufactured crowns provided similar or higher survival rates and fracture forces compared to automix crowns. The choice of material is decisive for the survival and fracture force. The fabrication is not crucial. A smaller TOC led to higher fracture force. Manually inserted screw channels had negative effects on fatigue testing.

CLINICAL RELEVANCE

The highest stability has been shown for crowns with a low TOC, which are manufactured additively and subtractively. In automix-fabricated crowns, manually inserted screw channels have negative effects.

Influence of Polymeric Restorative Materials on the Stress Distribution in Posterior Fixed Partial Dentures: 3D Finite Element Analysis

Background: This study evaluated the effect of interim restorative materials (acrylic resin (AR), resin composite (RC) or polyetheretherketone (PEEK) for dental computer-aided design/computer-aided manufacturing (CAD/CAM)) on the stress distribution of a posterior three-unit fixed partial denture. Methods: The abutment teeth (first molar and first premolar) were modeled using the BioCAD protocol containing 1.5 mm of axial reduction and converging axial walls. A static structural analysis was performed in the computer-aided engineering software, and the Maximum Principal Stress criterion was used to analyze the prosthesis and the cement layers of both abutment teeth. The materials were considered isotropic, linearly elastic, homogeneous and with bonded contacts. An axial load (600 N) was applied to the occlusal surface of the second premolar. Results: Regardless of the restorative material, the region of the prosthetic connectors showed the highest tensile stress magnitude. The highest stress peak was observed with the use of RC (129 MPa) compared to PEEK and AR. For the cement layers, RC showed the lowest values in the occlusal region (7 MPa) and the highest values for the cervical margin (14 MPa) compared to PEEK (21 and 12 MPa) and AR (21 and 13 MPa). Conclusions: Different interim restorative materials for posterior fixed partial dentures present different biomechanical behavior. The use of resin composite can attenuate the stress magnitude on the cement layer, and the use of acrylic resin can attenuate the stress magnitude on the connector region.