Effect of brushing force on the abrasive dentin wear using slurries with different abrasivity values

OBJECTIVE

The aim of this study was to investigate the resulting abrasive dentin wear using abrasive slurries with different RDA values and applying increasing brushing forces.

METHODS

Forty-five bovine incisors were randomly allocated in three groups (A, B, C, n = 15). One hundred and eighty dentin samples were prepared from these incisors and allocated to twelve groups (A1-A4, B1-B4, C1-C4; n = 15). The groups were subjected to a brushing cycle (120 strokes/min, 25 min) as follows: groups A1 to A4 with an abrasive slurry (RDA = 71) applying increasing brushing forces (1, 2, 3 and 4 N). Groups B1 to B4 were brushed using an abrasive slurry (RDA = 85) and C1 to C4 (RDA = 133) applying the same above-mentioned brushing forces. Abrasive dentin wear was recorded using a stylus profilometer and compared amongst the groups using robust models. Pairwise comparisons in each model were tested and corrected after Tukey's method (α = 0.05).

RESULTS

Applying 1-N brushing force resulted in the same amount of abrasive dentin wear in all groups regardless of the abrasivity of the used slurry. Increasing the brushing force to 2 N resulted in statistically significantly higher abrasive wear in all groups. This increase in abrasive wear was much higher when the slurry with high abrasivity was used (RDA = 133) compared with the lower abrasive slurry (RDA = 71).

CONCLUSION

The abrasivity of the used slurry does not add to the resulting abrasive wear when the brushing force is kept at 1 N. It seems better to advise and help the patients (showing signs of non-carious cervical lesions) calibrating their brushing force to 1 N, than only to advise them to use toothpastes with lower abrasivities.

In vitro evaluation of fissure sealants' wear under erosive, abrasive and erosive/abrasive conditions

PURPOSE

To evaluate and compare the wear of selected resin-based fissure sealants with different compositions properties under erosive, abrasive, and erosive/abrasive conditions.

METHODS

Forty-five samples of the following resin-based fissure sealants were prepared: Fissurit (fluoride free), Fissurit F (with fluoride), Fissurit FX (55 wt.% filler content), Grandio Seal (70 wt.% nano-filler content) and bovine enamel. Fifteen samples from each material were randomly allocated into three groups according to the wear condition they would be subjected to as follows: erosive condition (citric acid, 1 min, pH 2.3), abrasive condition (120 brushing strokes at 2 N, toothpaste slurry RDA value = 69), and erosive/abrasive condition (combination of both). The wear challenges were repeated six times each day for 10 days. The material wear was measured using a stylus profilometer. Kruskal-Wallis and Conover's test was applied to compare the resulting material wear between the groups.

RESULTS

Under erosive conditions, Grandio Seal and Fissurit FX showed statistically significantly the least material wear. Under abrasive and erosive/abrasive conditions, Grandio Seal showed statistically significantly the least material wear. Fissurit F showed statistically significantly the highest material wear under abrasive and erosive/abrasive conditions, after dental enamel (p < 0.05).

CONCLUSION

Higher filler content in sealants leads to better wear resistance. Incorporating fluoride into sealants seems to reduce their wear resistance at similar filler contents.

Effect of toothbrush bristle stiffness and toothbrushing force on the abrasive dentine wear

Objective

To investigate the influence of toothbrush bristle stiffness and applied brushing force on the resulting abrasive dentine wear in vitro.

Methods

One hundred sixty bovine dentine samples were randomly allocated in eight groups (n = 20). Groups one to four were brushed with a soft‐bristle toothbrush with soft bristles applying 1, 2, 3 and 4 N brushing force, respectively. Groups five to eight were brushed with a medium‐bristle toothbrush applying the same aforementioned brushing forces (120 strokes/min, abrasive slurry (RDA = 121), 25 min). Profiles were recorded before and after the brushing sequence, and the median and interquartile range of abrasive dentine wear were calculated and compared using two‐way ANOVA and pairwise tests corrected after Tukey (α = 0.05).

Results

At 1, 2 and 3 N brushing force, the tested toothbrushes caused no significantly different abrasive dentine wear. At 4 N brushing force, the medium‐bristle toothbrush caused statistically significantly higher abrasive force than the soft‐bristle toothbrush. Using the medium‐bristle toothbrush, abrasive dentine wear statistically significantly increased with increasing brushing force from 1 to 3 N. However, increasing the brushing force to 4 N did not result in statistically significantly higher wear. Using the soft‐bristle toothbrush, abrasive dentine wear statistically significantly increased with increasing brushing force from 1 to 2 N. However, increasing the brushing force to 3 or 4 N did not result in statistically significantly higher wear.

Conclusion

The soft‐bristle toothbrush tends to cause less abrasive wear with increasing brushing force than the medium‐bristle toothbrush.

Effect of a sonic toothbrush on the abrasive dentine wear using toothpastes with different abrasivity values

Objective

This in vitro study aimed to investigate the effect of a sonic toothbrush on the resulting abrasive dentine wear using toothpastes with different abrasivities compared to the use of a manual toothbrush.

Methods

Ninety‐six bovine dentine samples were divided into six groups and subjected to a brushing sequence (sonic: 20 min, 0.9 N, 10 strokes/min; manual: 20 min, 1.6 N, 60 strokes/min) as follows: group 1: Elmex Sensitive Plus (RDA = 28) + manual toothbrush; group 2: Elmex Sensitive + sonic toothbrush; group 3: Elmex Kariesschutz (RDA = 65) + manual toothbrush; group 4: Elmex Kariesschutz +sonic toothbrush; group 5: Colgate Total Original (RDA = 121) + manual toothbrush; and group 6: Colgate Total Original +sonic toothbrush. The abrasive dentine wear was measured profilometrically.

Results

The median (IQR) abrasive dentine wear was as follows: Elmex Sensitive Plus (manual toothbrush: 2.7 µm (0.8), sonic toothbrush: 3.1 µm (1.9)); Elmex Kariesschutz (manual toothbrush: 4.9 µm (1.4), sonic toothbrush: 6.4 µm (2.1)); and Colgate Total Original (manual toothbrush: 5.2 µm (1.1), sonic toothbrush: 9.0 µm (3.1)). Differences in dentine wear between sonic and manual toothbrushes were statistically significant only in the groups brushed with Elmex Kariesschutz and Colgate Total Original (p ≤ 0.05).

Conclusion

Brushing with a sonic toothbrush could result in a higher abrasive dentine wear compared to manual toothbrush when combined with toothpastes with high abrasivity values.

Effect of dentin pretreatment on the resulting abrasive dentin wear

Background

This study aims to investigate the influence of different dentin pretreatment procedures on the resulting abrasive dentin wear.

Methods

Two groups (A, B) of 60 dentin samples each were prepared. Group A was brushed with an abrasive slurry (RDA = 85) and group B with a different abrasive slurry (RDA = 174). Four subgroups in each group (n = 15) were created (A1–A4) and (B1–B4). The subgroups were pretreated as follows: A1 + B1 with 1200-grit grinding paper, A2 + B2 with 1200- and 2000-grit papers, A3 + B3 with 1200-, 2000-, and 4000-grit papers, A4 + B4 with 1200-, 2000-, 4000-grit papers and with 1000 brushing strokes with a slurry of Elmex toothpaste. All samples were brushed for 25 min at 120 strokes/min. Abrasive dentin wear was measured for each sample profilometrically and the subgroups were compared with each other within the same group. Repeated measures one-way ANOVA was conducted to compare the subgroups and pairwise contrasts were estimated for multiple testing according to Tukey (α = 0.05).

Results

The resulting abrasive dentin wear in group A ranged between 15.3 ± 3.4 µm and 17.3 ± 5.5 µm and between 20.3 ± 6.8 µm and 22.5 ± 2.6 µm in group B. No statistically significant difference was noticed between any subgroups within the same group (p ˃ 0.05).

Conclusions

Different dentin pretreatment procedures do not affect the resulting abrasive dentin wear independent of the RDA value of the employed abrasive slurry.

Green Tea Extract Reduces the Erosive Dentine Wear Caused by Energy Drinks In Vitro

PURPOSE

To investigate the effect of energy drinks supplementation with green tea extract on the erosive dentine wear.

MATERIALS AND METHODS

Six groups of bovine dentine samples (n = 15) were subjected to four cycles erosive attacks (10 min, 25 °C) and remineralisation (artificial saliva, 60 min, 37°C) using the following formulas: tap water; green tea extract; Red Bull; Red Bull supplemented with green tea extract; Red Bull Light; Red Bull Light supplemented with green tea extract. The erosive dentine wear - ie, the irreversible dentine loss - was measured using a stylus profilometer (µm, accuracy = 40 nm).

RESULTS

Median and interquartile range (IQR) of erosive dentine wear for the tested energy drinks before and after the supplementation with green tea extract were calculated as follows: Red Bull (before: 3.3 µm (1.0)); after: 1.2 µm (0.6)); Red Bull Light (before: 3.3 µm (0.9)); after: 2.0 µm (0.4)). The difference between the groups before and after the supplementation was statistically significant (P ˂0.05). The erosive dentine wear for the tap water group was calculated at 0.4 µm (0.6) and for the green tea extract group at -1.0 µm (1.3).

CONCLUSIONS

Supplementation of energy drinks with green tea extract could reduce the erosive dentine wear caused by energy drink in vitro.

Prevention of Enamel Softening by Rinsing with a Calcium Solution before Dental Erosion

OBJECTIVES

This in situ study aimed to evaluate whether rinsing with a calcium-containing solution prior to an erosive attack reduces the softening of enamel.

MATERIALS AND METHODS

A total of 240 bovine enamel samples with determined baseline surface microhardness (KHN) were allocated to 5 runs in which each of the 12 volunteers performed the following experiment: 4 enamel samples were inserted in a custom-made intraoral appliance and carried in the mouth (upper jaw) for 30 min before each volunteer either rinsed his mouth for 60 s with a fluoride- and stannous ion-containing dental erosion protection mouth rinse as positive control (run 1), milk (run 2), a solution prepared from a 500-mg calcium effervescent tablet dissolved in 100 mL (run 3) or 200 mL (run 4) water, or did not perform any rinsing with a test solution before the erosive attack (run 5, negative control). To simulate the erosive attack, volunteers rinsed their mouth with a commercial soft drink (Sprite Zero) for 60 s and afterwards with water to stop the erosive process. Finally, surface microhardness was measured again and hardness loss (ΔKHN) calculated. A mixed effect model was fitted to the data set to investigate whether the different runs showed differences with respect to ΔKHN.

RESULTS

No significant difference in softening of enamel (mean of ΔKHN; lower confidence level/upper confidence level) was observed between the negative control run 5 (50.7; 60.8/40.6), run 2 (50.7; 60.8/40.6), run 3 (38.7; 48.8/28.6) and run 4 (40.7; 50.8/30.6) (p > 0.05, respectively). Enamel softening in the positive control run 1 (25.4; 35.6/15.3) was significantly lower compared to the softening in run 5 (p < 0.001). No significant difference was observed between run 1 and run 3 (p = 0.09).

CONCLUSION

Other than the fluoride- and stannous ion-containing dental erosion protection mouth rinse, none of the investigated calcium-containing solutions is able to significantly reduce erosion-induced softening of enamel.

Stability of two resin combinations used as sealants against toothbrush abrasion and acid challenge in vitro

OBJECTIVE

To test the stability of two conventional adhesives when combined with a low-viscosity caries infiltrant used for sealing sound enamel against toothbrush abrasion and acid challenge in vitro.

MATERIALS AND METHODS

Bovine enamel discs (Ø = 3 mm) randomly assigned to three groups (n = 10/group) were etched with 37% phosphoric acid for 30 s and treated with resins of different monomer contents forming three test groups: (1) Untreated specimens (Control); (2) Infiltrant (Icon, DMG) + conventional enamel bonding adhesive (Heliobond, Ivoclar Vivadent); and (3) Infiltrant + conventional orthodontic adhesive (Transbond XT Primer, 3M Unitek). All specimens were immersed in hydrochloric acid (pH 2.6) for up to 9 days, during which they were exposed to 1825 toothbrush-strokes per day. Calcium dissolution was assessed using Arsenazo III method at 24-h intervals. Data were analyzed by Kruskal-Wallis and Wilcoxon signed ranks tests.

RESULTS

Cumulative calcium dissolution for the untreated specimens (39.75 ± 7.32 μmol/ml) exceeded the sealed groups (Icon + Heliobond: 23.44 ± 7.03 μmol/ml; Icon + Transbond XT Primer: 22.17 ± 5.34 μmol/ml). Untreated specimens presented a relatively constant calcium dissolution rate throughout the experimental period, whereas the sealed groups presented a gradual increase indicating weakening of the seal by toothbrush abrasion. Both sealed groups presented significantly lower daily calcium dissolution at all time points compared to the control, except for Group 2 on the last measurement day.

CONCLUSIONS

Low-viscosity caries infiltrant application on sound enamel prior to conventional resin application provided a protective effect against enamel demineralization, but this effect was not stable when challenged mechanically by toothbrush abrasion.

Caries infiltrant combined with conventional adhesives for sealing sound enamel in vitro

OBJECTIVE

To test the null hypothesis that combining low-viscosity caries infiltrant with conventional adhesive resins would not improve sealing of sound enamel against demineralization in vitro.

MATERIALS AND METHODS

Bovine enamel discs (N = 60) with diameter of 3 mm were randomly assigned to six groups (n = 10). The discs were etched with 37% phosphoric acid for 30 seconds and treated with resins of different monomer content forming the following groups: (1) Icon (DMG), (2) Transbond XT Primer (3M ESPE), (3) Heliobond (Ivoclar Vivadent), (4) Icon + Transbond XT Primer, and (5) Icon + Heliobond. Untreated etched samples served as the negative control. Specimens were subjected to demineralization by immersion in hydrochloric acid (pH 2.6) for 80 hours. Calcium dissolution into the acid was assessed by colorimetric analysis using Arsenazo III method at 16-hour intervals. Groups presenting high protection against demineralization were subjected to further acidic challenge for 15 days with calcium measurements repeated at 24-hour intervals. Data were analyzed by Kruskal-Wallis test and Mann-Whitney U-test.

RESULTS

Untreated specimens showed the highest amount of demineralization. Icon and Transbond XT primer decreased the mineral loss significantly compared to the control. Heliobond performed significantly better than both Icon and Transbond XT primer. Combination of Icon both with Transbond XT primer or Heliobond served as the best protective measures and maintained the protective effect for the additional 15-day acidic challenge.

CONCLUSIONS

Within the limitations of this in vitro study, it could be concluded that the use of low-viscosity caries infiltrant prior to application of the tested conventional adhesives increases their protective effect against demineralization.

Marginal adaptation of ceramic and composite inlays in minimally invasive mod cavities

OBJECTIVES

This study aims to evaluate the effect of a minimally invasive mesial-occlusal-distal (mod) preparation on the marginal adaptation of ceramic and composite inlays with the aim of saving sound dental substance.

MATERIALS AND METHODS

Class II mod cavities were prepared in 50 extracted human molars and randomly allocated to five groups (n = 10). In all groups, the mesial-proximal box margins were located in the dentin, 1 mm below the cementoenamel junction (CEJ), while the distal box margins were 1 mm above the CEJ. In groups A and B, conventional standard preparations with a divergent angle of α = 6° were prepared. In groups C, D, and E, minimally invasive standard preparations with a convergent angle of α = 10° were prepared. In groups A and D, composite inlays and, in groups B and C, ceramic inlays were fabricated (chairside economical restoration of esthetic ceramics (CEREC)) and adhesively inserted. In group E, a direct composite filling using the incremental technique was placed. Replicas were taken before and after thermomechanical loading (1,200,000 cycles, 50/5 °C, max. load 49 N). Marginal integrity (tooth-luting composite, luting composite-inlay) was evaluated by scanning electron microscopy (× 200). The percentage of continuous margins in the different locations was compared between and within groups before and after cycling, using ANOVA and Scheffé post hoc test.

RESULTS

After the thermomechanical loading, no significant differences were observed between the different groups with respect to the interface of luting composite-inlay. At the interface of tooth-luting composite for preparations involving the dentin, groups A and B behaved significantly better compared to the control group E, which in turn were not different to groups C and D.

CONCLUSION

Composite and ceramic inlays inserted in minimally invasive prepared mod cavities result in margins not different from those of inlays placed in conventional mod preparations. Direct composite filling margins, however, were inferior to those attained by conventional indirect restorations.

CLINICAL RELEVANCE

Minimally invasive preparations for mod inlays with undercuts show marginal adaptation equal to that of conventional inlay preparation design.

Effect of a low-viscosity adhesive resin on the adhesion of metal brackets to enamel etched with hydrochloric or phosphoric acid combined with conventional adhesives

PURPOSE

This study investigated the effect of a low-viscosity adhesive resin (Icon) applied after either hydrochloric (HCl) or phosphoric acid (H3PO4) on the adhesion of metal brackets to enamel. Failure types were analyzed.

MATERIALS AND METHODS

The crowns of bovine incisors (N = 20) were sectioned mesio-distally and inciso-gingivally, then randomly assigned to 4 groups according to the following protocols to receive mandibular incisor brackets: 1) H3PO4 (37%)+TransbondXT (3M UNITEK); 2) H3PO4 (37%)+Icon+TransbondXT; 3) HCl (15%)+Icon (DMG)+TransbondXT 4) HCl (15%)+Icon+Heliobond (Ivoclar Vivadent)+TransbondXT. Specimens were stored in distilled water at 37°C for 24 h and thermocycled (5000x, 5°C to 55°C). The shear bond strength (SBS) test was performed using a universal testing machine (1 mm/min). Failure types were classified according to the Adhesive Remnant Index (ARI). Contact angles of adhesive resins were measured (n = 5 per adhesive) on ceramic surfaces.

RESULTS

No significant difference in SBS was observed, implying no difference between combinations of adhesive resins and etching agents (p = 0.712; ANOVA). The Weibull distribution presented significantly lower Weibull modulus (m) of group 3 (m = 2.97) compared to other groups (m = 5.2 to 6.6) (p < 0.05). The mean SBS results (MPa) in descending order were as follows: group 4 (46.7 ± 10.3) > group 1 (45.4 ± 7.9) > group 2 (44.2 ± 10.6) > group 3 (42.6 ± 15.5). While in groups 1, 3, and 4 exclusively an ARI score of 0 (no adhesive left on tooth) was observed, in group 2, only one specimen demonstrated score 1 (less than half of adhesive left on tooth). Contact angle measurements were as follows: Icon (25.86 ± 3.81 degrees), Heliobond (31.98 ± 3.17 degrees), TransbondXT (35 ± 2.21 degrees).

CONCLUSION

Icon can be safely used with the conventional adhesives tested on surfaces etched with either HCl or H3PO4.

Impact of laminar flow velocity of different acids on enamel calcium loss

OBJECTIVE

The aim of the study was to evaluate the impact of flow velocity under laminar flow conditions of different acidic solutions on enamel erosion.

MATERIAL AND METHODS

A total of 240 bovine enamel specimens were prepared and allocated to 30 groups (n = 8 each). Samples of 18 groups were superfused in a flow chamber system with laminar flow behavior using 1 ml of citric acid or hydrochloric acid (HCl) of pH 2.0, 2.6 or 3.0. Flow rates in the sample chamber were adjusted to 10, 60 or 100 μl/min. To simulate turbulent flow behavior, samples of six groups were immersed in 1 ml of the respective solution, which was vortexed (15 min, 600 rpm). For simulating non-agitated conditions, specimens of the remaining six groups were immersed in 1 ml of the respective solution without stirring. Calcium in the solutions, released from the enamel samples, was determined using Arsenazo III method.

RESULTS

For acidic solutions of pH 2.6 and 3.0, erosive potential of citric acid was equivalent to that of HCl at a flow of 100 μl/min. The same observation was made for the samples subjected to turbulent conditions at pH 3. At all other conditions, citric acid induced a significantly higher calcium loss than HCl.

CONCLUSION

It is concluded that under slow laminar flow conditions, flow rate variations lead to higher erosive impact of citric acid compared to hydrochloric acid at pH 2.0, but not at pH ≥ 2.6 and increasing laminar flow or turbulent conditions.

CLINICAL RELEVANCE

Erosive enamel dissolution under laminar flow conditions is a complex issue influenced by flow rate and acidic substrate.

Effect of sodium hypochlorite contamination on microhardness of dental core build-up materials

This study aimed to determine the influence of sodium hypochlorite (NaOCl) contamination on the microhardness of build-up composites. Fifty-two samples, from each of three build-up materials (LuxaCore Dual, MultiCore flow and Rebilda DC) were prepared. Half of the samples from each material were stored in physiologic saline (baseline control) while the other halves were stored in NaOCl. After 1 h, the samples were rinsed with tap water, cut axially and measured for Knoop hardness at different depth levels. The results were analysed by ANOVA and unpaired t-tests (p<0.05). Significant differences in microhardness were observed for LuxaCore Dual up to 0.2 mm, Rebilda DC up to 0.3 mm, and for MultiCore flow up to 0.4 mm under the surface level. Contact with sodium hypochlorite on build-up materials causes reduction of the microhardness. The softening is not only limited on the surface, but can also be found in deeper layers of build-up materials.