Ultrasonic measurement of dentin remineralization effects of dentifrices and silver diamine fluoride

OBJECTIVE

This study investigated the dentin remineralization effect of the application of a functionalized tri-calcium phosphate (fTCP) dentifrice and a silver diamine fluoride (SDF) solution.

MATERIAL AND METHODS

The materials used were: a fluoride-containing dentifrice with fTCP (fTCP＋), a fluoride-containing dentifrice without fTCP (fTCP-) and a 38% SDF solution. Following treatment, the dentin slabs were immersed in a 0.1-M lactic acid buffer solution and then placed in artificial saliva. This procedure was repeated three times daily for 28 days. The propagation time of longitudinal ultrasonic velocities (UV) and the Knoop hardness (KH) of the samples were measured. The samples were also observed using scanning electron microscopy.

RESULTS

The SDF and fTCP＋ groups showed higher UV than the fTCP - group regardless of the application method. The F-SDF group at 28 days showed significantly higher UV (4121 ± 102 m/s) than the F-fTCP + group (3731 ± 65 m/s) (p < .05). The F-SDF group at 28 days showed significantly higher KH (47.4 ± 2.2) than the F-fTCP＋ group (43.3 ± 1.0) and the F-fTCP - group (42.9 ± 2.1) (p < .05). Closure of the dentinal tubules and crystal precipitation was detected on the surface of the fTCP＋ group to a greater extent than the fTCP - group.

CONCLUSIONS

The fTCP-containing dentifrice and SDF solution effectively enhanced bovine dentin remineralization.

Evaluation of Color-matching Ability of a Structural Colored Resin Composite

PURPOSE

The present study evaluated the color-matching ability of a structural colored resin composite to compare it with resin composites employing pigments.

METHODS AND MATERIALS

A structural colored resin composite (Omnichroma [OMC]), a supranano-filled resin composite (Estelite ∑ Quick [ELQ]), and a nano-filled resin composite (Filtek Supreme Ultra [FSU]) were used. Each resin composite was packed into a Teflon mold and pressed down with a clear strip under a glass slide. The specimens were light irradiated through the slide with a light-emitting diode curing unit. The thickness of the specimens (n=6) was measured with a digital caliper before being transferred to distilled water and stored at 37°C for 24 hours. The measurements of the optical characteristics of the specimens on a black-and-white background were performed using a spectrophotometer. D65 (CIE D65) was used as a light source for the spectrophotometer. Measurements were repeated three times for each specimen under each color-measurement condition, and average values for three same-shade specimens were calculated. One-way analysis of variance and Tukey post hoc tests were used (α=0.05). To determine its ability to match the color of artificial teeth, each shade of resin composite was placed in a cavity before performing color measurements. Using a spectrophotometer (CMS-35F S/C) with a flexible sensor, L*, a*, and b* values were obtained.

RESULTS

The spectral reflectance curve of OMC showed that it reflected light wavelengths from 430-700 nm regardless of the background color and thickness of the specimens. The percentage of reflectance of ELQ decreased near wavelengths of 550-580 nm. Regarding the influence of background color on CIE L*, a*, b* values, the L* level showed significantly higher values for all tested materials with white backgrounds, and OMC was most affected by the difference in background color. However, a* values of ELQ and FSU were significantly higher with a black background than with a white background, and OMC showed a significantly higher value with a white background than with a black background. The b* values were higher with a white background than with a black background and were significantly higher for all three products, and these tendencies were much greater for ELQ and FSU.

CONCLUSIONS

The ability of OMC to match the color of artificial teeth showed acceptable color compatibility, regardless of the shade of the artificial teeth and the depth of the cavity. However, ELQ and FSU showed reduced color compatibility, especially for a cavity depth of 3.0 mm. Excellent color matching ability was confirmed for the structural colored resin composite OMC, resulting in reduced color differences and therefore improving the esthetic appearance of the restoration, simplifying shade matching, and compensating for any color mismatch.

Reconsideration of Enamel Etching Protocols for Universal Adhesives: Effect of Etching Method and Etching Time

PURPOSE

To evaluate whether different etching methods with reduced etching times would improve the enamel bonding efficacy of universal adhesives.

MATERIALS AND METHODS

Three enamel etching methods were evaluated - 1. phosphoric acid ester monomer etching (PPM); 2. phosphoric acid etching (PPA); and 3. polyalkenoic acid etching (PLA) - as were three universal adhesives: 1. BeautiBond Universal (BU); 2. Prime&Bond elect (PE); and 3. Scotchbond Universal Adhesive (SU). The shear bond strengths of the universal adhesives to ground enamel and ground enamel etched for 1, 5, 10, and 15 s with different etching methods were determined after 24 h and 10,000 thermal cycles. Surface roughness average (Ra) and surface area ratio (surface area:planar area) were measured using a confocal laser scanning microscope. Field-emission scanning electron microscope (FE-SEM) observations of enamel with different etching protocols were also conducted.

RESULTS

The bond strengths of universal adhesives to enamel subjected to PPA etching with maximum times of 1-15 s and PLA etching for 15 s were significantly higher than those to ground enamel. The bond strength to enamel subjected to PPM etching did not increase and was similar to that for ground enamel. PPA and PLA etching were effective at increasing the Ra and surface area ratio of enamel. Although both values were significantly higher than those of ground enamel, those subjected to PPA etching were significantly higher than those which underwent PLA etching. In addition, the Ra and surface area of enamel subjected to PPM etching were similar to those of ground enamel, regardless of the etching time.

CONCLUSIONS

Phosphoric acid etching for <1-15 s and polyalkenoic-acid etching for 15 s both improve the bonding of universal adhesives, the Ra, and the surface area ratio of enamel. However, phosphoric acid ester monomer etching was not effective, regardless of the etching time.

Influence of warm air-drying on enamel bond strength and surface free-energy of self-etch adhesives

We examined the effect of warm air-drying on the enamel bond strengths and the surface free-energy of three single-step self-etch adhesives. Bovine mandibular incisors were mounted in self-curing resin and then wet ground with #600 silicon carbide (SiC) paper. The adhesives were applied according to the instructions of the respective manufacturers and then dried in a stream of normal (23°C) or warm (37°C) air for 5, 10, and 20 s. After visible-light irradiation of the adhesives, resin composites were condensed into a mold and polymerized. Ten samples per test group were stored in distilled water at 37°C for 24 h and then the bond strengths were measured. The surface free-energies were determined by measuring the contact angles of three test liquids placed on the cured adhesives. The enamel bond strengths varied according to the air-drying time and ranged from 15.8 to 19.1 MPa. The trends for the bond strengths were different among the materials. The value of the γS⁺ component increased slightly when drying was performed with a stream of warm air, whereas that of the γS⁻ component decreased significantly. These data suggest that warm air-drying is essential to obtain adequate enamel bond strengths, although increasing the drying time did not significantly influence the bond strength.

Comparison of the wear and flexural characteristics of flowable resin composites for posterior lesions

OBJECTIVES

To determine the localized wear and flexural properties of flowable resin composites for posterior lesions compared with universal resin composites produced by the same manufacturers.

METHODS

Ten specimens of each of three flowable resins, G-ænial Universal Flo, G-ænial Flo and Clearfil Majesty Flow, and the corresponding resin composite materials, Kalore and Clearfil Majesty Esthetics, were prepared in custom fixtures and subjected to 400,000 wear machine cycles to simulate localized wear. The total maximum depth and volume loss of the wear facets was calculated for each specimen using a profilometer. A three-point bending test was performed to determine the flexural strength, modulus of elasticity and resilience. Values were statistically compared using one-way analysis of variance (ANOVA) followed by Tukey's Honestly Significant Difference (HSD) test.

RESULTS

The wear depth ranged from 58.3-126.9 m and the volumetric loss ranged from 0.019-0.049 mm(3), with significant differences observed between restorative materials. The wear depth of G-ænial Universal Flo was significantly smaller than those of the other resin composites tested. The flexural strengths and elastic modulus ranged from 90.5-135.1 MPa and from 4.7-7.6 GPa, respectively. A significantly greater flexural strength and higher elastic modulus was found for G-ænial Universal Flo than the other composites.

CONCLUSIONS

The wear and mechanical properties of the flowable resin composites tested suggested improved performance compared with universal resin composites.

Effect of warm air-drying on dentin bond strength of single-step self-etch adhesives

The effect of warm air-drying on the dentin bond strengths of the single-step self-etch adhesives was determined. The adhesives were applied to bovine dentin followed by drying in a stream of warm air for 5, 10, and 15 s at 37°C. Resin composites were condensed into a mold and polymerized. Specimens were stored in distilled water at 37°C for 24 h, then shear tested. The surface free-energies were determined by measuring the contact angles of three test liquids placed on the cured adhesives. The dentin bond strengths varied according to the air-drying time. The value of the acid component increased slightly when drying was performed with a stream of warm air, whereas that of the base component decreased significantly. These data suggested that warm air-drying was essential to obtain adequate bond strengths, although increasing the drying time did not significantly influence the bond strength.

Ultrasonic measurement of the effects of adhesive application and power density on the polymerization behavior of core build-up resins

OBJECTIVE

To use ultrasonic measurements to monitor the effects of adhesive application and power density on the polymerization behavior of dual-cured core build-up resins.

METHODS

Ultrasonic measurements were carried out using a pulser-receiver, transducers and an oscilloscope. The core build-up resins were mixed, inserted into a transparent mold and then placed onto a sample stage with or without self-etch adhesive. Power densities of 0 (no light irradiation), 200 and 600 mW/cm(2) were used for curing. The transit time through the core build-up resin disk was divided by the specimen thickness to obtain the longitudinal sound velocity (V).

RESULTS

Light irradiation of the core build-up resins at a power density of 600 mW/cm(2) caused V values to rise to an initial plateau of 1550-1650 m/s, then to rise rapidly to a second plateau of 2800-3200 m/s. The rate of V increase was slower when the resin cements were light-irradiated and became faster when irradiated at a higher power density. There were no significant differences between the groups with or without adhesive.

CONCLUSIONS

The polymerization behavior of the core build-up resins was affected by the power density of the curing unit. The influence of adhesive application differed among the core build-up resins tested.

Influence of oxygen inhibition on the surface free energy and enamel bond strength of self-etch adhesives

We compared the surface free energies and enamel bond strengths of single-step self-etch adhesives with and without an oxygen-inhibited layer. The adhesives were applied to the enamel surfaces of bovine incisors, light irradiated, and the oxygen-inhibited layer was either retained or removed with ethanol. The surface free energies and their components (γ(S)(LW), γ(S)(+), and γ(S)(-)) were determined by measuring the contact angles of three test liquids placed on the cured adhesives. The enamel bond strengths of specimens with and without the oxygen-inhibited layer were measured. For all surfaces, the value of the estimated surface tension component γ(S)(LW) was relatively constant. The value of the γ(S)(+) component increased slightly when the oxygen-inhibited layer was removed, whereas that of the γ(S)(-) component decreased significantly. The enamel bond strengths of the self-etch adhesives were significantly lower in the specimens without an oxygen-inhibited layer. The oxygen-inhibited layer therefore appeared to promote higher enamel bond strength.

Development of Production Robot System that can Assemble Products with Cable and Connector

To realize automatic robot-based electrical and electronic product assembly, we developed the handling of cables with connectors - flexible goods which are an obstacle to automation. The element technologies we developed include 3D vision sensing for cable extraction, force control for connector insertion, error recovery for improving system stability, and task-level programming for quick system start-up. We assembled FA control equipment to verify the feasibility of our developments.

Acetyl-CoA carboxylase from Escherichia coli: gene organization and nucleotide sequence of the biotin carboxylase subunit

Biotin carboxylase [biotin-carboxyl-carrier-protein:carbon-dioxide ligase (ADP-forming), EC 6.3.4.14] is the enzyme mediating the first step of the acetyl-CoA carboxylase [acetyl-CoA:carbon-dioxide ligase (ADP-forming), EC 6.4.1.2] reaction. We screened an Escherichia coli DNA library and a DNA fragment carrying the biotin carboxylase gene fabG, and its flanking regions were cloned. The gene for biotin carboxyl carrier protein was found 13 base pairs upstream of the fabG gene. Nucleotide sequencing of the recombinant plasmids revealed that the fabG codes for a 449-amino acid residue protein with a calculated molecular weight of 49,320, a value in good agreement with that of 51,000 determined by SDS/polyacrylamide gel electrophoresis of the purified enzyme. The deduced amino acid sequence of biotin carboxylase is also consistent with the partial amino acid sequence determined by Edman degradation. The primary structure of this enzyme exhibits a high homology with those of other biotin-dependent enzymes and carbamoyl-phosphate synthetase [carbon-dioxide:L-glutamine amino-ligase (ADP-forming, carbamate-phosphorylating), EC 6.3.5.5]; therefore, all these enzymes probably function through the same mechanism of reaction.

Cytoprotective action of roxatidine acetate HCl

The cytoprotective action of roxatidine acetate HCl (roxatidine) was investigated. We also studied the involvement of endogenous prostaglandins (PGs) in the cytoprotective action of roxatidine and the effect of roxatidine on SRS content in pleurisy induced by A23187. Simultaneously, these effects of roxatidine were compared with those of other histamine H2-receptor antagonists at the same anti-secretory activity level. Roxatidine prevented formation of the gastric mucosal lesions induced by abs. ethanol, 0.6 N HCl and 0.2 N NaOH, but it failed to prevent 30% NaCl-induced gastric mucosal lesions. Cimetidine, ranitidine and famotidine failed to prevent formation of the gastric mucosal lesions induced by necrotizing agents. The cytoprotective action of roxatidine was not abolished by pretreatment with indomethacin. Roxatidine did not greatly influence SRS production. Consequently, it appears that roxatidine has a cytoprotective action and that this action is not associated with endogenous PGs and SRS.

Role of beta 2-adrenoceptor blockade and circulating adrenaline level for the pressor responses to beta-adrenoceptor blocking drugs in rats

The present experiments were designed to elucidate what mechanism(s) would be responsible for beta-adrenoceptor blocking drugs (beta-blockers)-induced pressor responses in rats. In urethane-anaesthetized rats, 6 beta-blockers at i.v. doses ranging from 0.3 to 300 micrograms/kg evoked the pressor response in a dose-dependent manner. The relative potency in causing the pressor action was correlated not to their beta 1-blocking activities (r = 0.374, P greater than 0.05) but to their beta 2-blocking ones (r = 0.856, P less than 0.05). In pithed or adrenalectomized rats with low levels of plasma catecholamines, however, propranolol failed to exert its sustained pressor action. Propranolol (300 micrograms/kg i.v.) distinctly potentiated the pressor responses not to noradrenaline but to adrenaline and to electrical stimulation of the sympathetic outflow (E.S.) in pithed rats. On the contrary, there was not any potentiation of pressor response to E.S. in pithed, adrenalectomized rats treated with propranolol (300 micrograms/kg i.v.). In rats treated with phenoxybenzamine (5 mg/kg i.v.), adrenaline was shown to have much more potent vasodilating action resulting from beta 2-stimulation than noradrenaline, the dose difference for causing the diastolic blood pressure decrease by a 25 mm Hg being almost 80 times. In pithed rats, infusion of adrenaline at the rate of 0.02 micrograms/min caused a significant increase in plasma adrenaline level from 0.02 +/- 0.01 to 0.45 +/- 0.048 ng/ml, being close to basal level obtained in urethane-anaesthetized rats. Under this situation, propranolol (1-100 micrograms/kg i.v.) showed a distinct pressor response in a dose-dependent fashion as observed in adrenal intact rats anaesthetized with urethane.(ABSTRACT TRUNCATED AT 250 WORDS)

[Antihypertensive action of adrenergic beta-receptor blockers and its effect on the entire sympathetic outflow in spontaneously hypertensive rats]

Three kinds of beta-adrenoceptor blocking agents were orally administered to spontaneously hypertensive rats (SH rats) from 5 to 13 weeks of age, and their effects on the development of hypertension and on peripheral sympathetic nervous system were investigated. In SH rats treated with the vehicle (2% Tween 80) for 8 weeks, systolic blood pressure increased from 132 +/- 1.3 to 179 +/- 2.7 mmHg (n = 10). Treatment with propranolol (2 X 50 mg/kg/day p.o., n = 8), pindolol (2 X 15 mg/kg/day p.o., n = 8) and D-32 (2 X 15 or 2 X 50 mg/kg/day p.o., n = 9) for 8 weeks slightly but definitely depressed the aforesaid development of hypertension, and their average reduction in systolic blood pressure was approximately 15 mmHg. In the pressor response to electrical stimulation of pre-ganglionic sympathetic nerves, there was not any difference between SH rats treated with vehicle and beta-adrenoceptor blocking agents (propranolol and D-32). P.o. administration of guanethidine or phentolamine, however, caused a slight hypotension and produced a significant reduction in the pressor response to electrical stimulation. SH rats treated with propranolol showed a leftward shift of the pressor response curve not to norepinephrine but to angiotensin II as compared with that obtained from vehicle treated SH rats. This phenomenon is probably due to the decreased renin release by the prolonged-treatment with drug. On the basis of these results, we could not obtain any clear evidence that the antihypertensive action exerted by beta-adrenoceptor blocking agents resulted from some interference with the function of the peripheral sympathetic nervous system.