Accuracy, adaptation and margin quality of monolithic zirconia crowns fabricated by 3D printing versus subtractive manufacturing technique: A systematic review and meta-analysis of in vitro studies

OBJECTIVE

The purpose of this systematic review and meta-analysis was to evaluate the accuracy (trueness and precision), marginal and internal adaptation, and margin quality of zirconia crowns made by additive manufacturing compared to subtractive manufacturing technology.

METHODS

The investigation adhered to the PRISMA-ScR guidelines for systematic reviews and was registered at the Prospero database (n°CRD42023452927). Four electronic databases, including PubMed, Scopus, Embase, and Web of Science and manual search was conducted to find relevant studies published until September 2023. In vitro studies that assessed the trueness and precision, marginal and internal adaptation, and margin quality of printed crowns compared to milled ones were included. Studies on crowns over implants, pontics, temporary restorations, laminates, or exclusively experimental materials were excluded.

RESULTS

A total of 9 studies were included in the descriptive reporting and 7 for meta-analysis. The global meta-analysis of the trueness (P<0.74,I2=90%) and the margin quality (P<0.61,I2=0%) indicated no significant difference between the root mean square of printed and milled zirconia crowns. The subgroup analysis for the printing system showed a significant effect (P<0.01). The meta-analysis of the crown areas indicated no significant difference in most of the areas, except for the marginal (favoring milled crowns) and axial (favoring printed crowns) areas. For precision and adaptation, both methods showed a clinically acceptable level.

CONCLUSIONS

Additive manufacturing technology produces crowns with trueness and margin quality comparable to subtractive manufacturing. Both techniques have demonstrated the ability to produce crowns with precision levels, internal discrepancy, and marginal fit within clinically acceptable limits.

CLINICAL SIGNIFICANCE

s3D printing emerges as a promising and potentially applicable alternative method for manufacturing zirconia crowns, as it shows trueness and margin quality comparable to restorations produced by the subtractive method.

Biaxial flexure strength and physicochemical characterization of a CAD/CAM lithium disilicate ceramic: effect of etching time, silane, and adhesive applications

OBJECTIVE

To evaluate the effect of different acid etching time and bonding agent (silane and/or adhesive system) on biaxial flexural strength and physico-chemical properties of a lithium disilicate ceramic.

MATERIAL AND METHODS

One hundred twenty ceramic discs were made and divided into 8 groups (n = 15) according to factors "etching time" (20 and 120 s) with hydrofluoric acid (HF) and "bonding agent" (C, no bonding agent; S, silane, A, adhesive; and SA, silane + adhesive). After surface treatment, a resin cement layer was applied to the surface and all specimens were subjected to biaxial flexural strength (BFS) test with treated surfaces loaded in tension (1 mm/min). The Weibull analyses and complementary analyses were also performed. Statistical analysis was done with 2-way ANOVA and the Tukey test (α = 0.05).

RESULTS

ANOVA revealed that the factors "etching time" (p = 0.0003) and "bonding agent" (p = 0.007) were statistically significant. In the overall analysis, the HF120S group (272.02 ± 35.30A MPa) presented significantly higher BFS than that of HF120C (218.45 ± 17.15CD MPa) and HF20S (228.40 ± 37.83BCDMPa). On the other hand, the HF20A group (208.92 ± 31.16D MPa) had significantly lower BFS than HF120S (272.02 ± 35.30A), HF120A (254.42 ± 26.87ABC) and HF120SA (259.30 ± 36.55AB) groups (Tukey). The Weibull modulus (m) of all groups was significantly different from each other (p = 0.000).

CONCLUSIONS

Regardless of etching time, the application of silane alone is sufficient to increase the flexural strength of glass ceramic, eliminating the need for the application of adhesive systems. Moreover, if only silane or adhesive is applied, 120-s HF application should increase the flexural resistance of the lithium disilicate ceramic.

CLINICAL SIGNIFICANCE

Applications of adhesive systems after silanization can be suppressed from the surface treatment protocol of glass ceramics, since it does not improve their mechanical strength.

Effect of different surface treatments and multimode adhesive application on the Weibull characteristics, wettability, surface topography and adhesion to CAD/CAM lithium disilicate ceramic

This paper aims to evaluate the effect of different surface treatments on surface topography, wettability, and shear bond strength of resin cement to glass ceramic.