Dentin Cross-linking Effect of Carbodiimide After 5 Years

Carbodiimide (EDC)-based dentin primers preserve hybrid layer (HL) integrity. However, aging >1 y has not been investigated. The present study examined whether the cross-linking effect of EDC was reflected in dentin bond strength, endogenous enzymatic activity, and the chemical profile of the HL after 5-y aging in artificial saliva. Noncarious human third molars (N = 42) were cut to expose middle/deep coronal dentin and treated as follows: group 1, dentin etched with 35% H₃PO₄, pretreated with a 0.3M aqueous EDC primer for 1 min and restored with XP Bond (Dentsply Sirona); group 2, as in group 1 but without EDC pretreatment; group 3, Clearfil SE Bond (Kuraray-Noritake) primer applied to dentin surface, followed by EDC pretreatment as in group 1 and application of bond; group 4, as in group 3 without EDC pretreatment. After composite buildup, the specimens were cut into sticks or slabs, depending on the experiment. All tests were performed at baseline (T0) and after 5 y of aging (T5) in artificial saliva at 37 °C. Microtensile bond strength (µTBS) was tested at a crosshead speed of 1 mm/min until failure. Endogenous enzymatic activity was investigated with in situ zymography. The chemical profile of HL was determined via Raman spectroscopy. Three-way analysis of variance and post hoc Tukey test were used to analyze µTBS and in situ zymography data (α = 0.05). EDC pretreatment and aging significantly influenced µTBS and in situ zymography results (P < 0.05). Higher bond strength and lower gelatinolytic activity were identified in the EDC-treated groups at T5 (P < 0.05), especially in the etch-and-rinse groups. Raman spectra revealed less defined amide III peaks in control specimens at T5. The EDC cross-linking effect persisted in the HL for 5 y in terms of bond strength, collagen structure preservation, and dentinal enzyme silencing.

Substantivity of Carbodiimide Inhibition on Dentinal Enzyme Activity over Time

The use of 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide HCl (EDC) has recently been investigated for its effectiveness in the prevention of collagen degradation over time and the improvement of resin-dentin bond durability. The objective of the present study was to evaluate the effects of a 0.3 M EDC-containing conditioner on endogenous enzymatic activities within the hybrid layer (HL) created by a self-etch or an etch-and-rinse adhesive after 1 y. The activity within the HL was examined using in situ zymography and confocal laser scanning microscopy after 24 h or 1-y storage in artificial saliva. Dentin specimens were bonded with Clearfil SE Bond (CSE) or XP Bond (XPB). For CSE, the self-etching primer was applied and treated with 0.3 M EDC for 1 min, and then the bonding agent was applied. For XPB, dentin was etched and treated with 0.3 M EDC for 1 min and then bonded with the primer-bonding agent. Control specimens were prepared without EDC treatment. Slices containing the adhesive-dentin interface were covered with fluorescein-conjugated gelatin and observed with a multiphoton confocal microscope. Fluorescence intensity emitted by hydrolyzed fluorescein-conjugated gelatin was quantified, and the amount of gelatinolytic activity was represented by the percentage of green fluorescence emitted within the HL. After 24 h of storage, enzymatic activity was detected by in situ zymography within the HLs of both tested adhesives, with XPB higher than CSE ( P < 0.05). Almost no fluorescence signal was detected when specimens were pretreated with EDC compared to controls ( P < 0.05). After 1 y of storage, enzymatic activities significantly increased for all groups (excluding XPB control) compared to 24-h storage ( P < 0.05), with EDC pretreated specimens exhibiting significantly lower activity than controls ( P < 0.05). The present study showed, for the first time, that the use of EDC for both the self-etch and the etch-and-rinse approaches results in the reduction but not complete inhibition of matrix-bound collagenolytic enzyme activities over time in the HL.