Stape THS, Viita-Aho T, Sezinando A, Wik P, Mutluay M, Tezvergil-Mutluay A. To etch or not to etch, Part I: On the fatigue strength and dentin bonding performance of universal adhesives. Dent Mater 2021; 37:949-960. [PMID: 33838928 DOI: 10.1016/j.dental.2021.02.016] [Citation(s) in RCA: 3] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [What about the content of this article? (0)] [Affiliation(s)] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/11/2020] [Revised: 02/05/2021] [Accepted: 02/24/2021] [Indexed: 11/24/2022]
Abstract
OBJECTIVE To characterize whether the bonding performance and fatigue strength of resin-dentin interfaces created by a universal adhesive would be affected by different H3PO4-application times to more accurately assess long-term durability. METHODS Mid-coronal flat dentin surfaces with standardized smear-layers were produced on sound third molars, etched with 32% H3PO4 for 0, 3 and 15 s, bonded with a mild universal adhesive (3M-ESPE) and restored with a nanofilled composite. Bonded specimens (0.9 × 0.9 mm) were stored in deionized water for 24 h and sectioned into beams for microtensile testing (n = 10). Resin-dentin beams were tested under tension until failure (0.5 mm/min) after 24 h or 6 month storage in artificial saliva at 37 ̊C. Bar-shaped resin-dentin beams (0.9 × 0.9 × 12 mm) were tested under 4-point-flexure initially at quasi-static loads (n = 22) and then under cyclic loads (n > 50). The stress-life fatigue behavior was evaluated using the twin-bonded interface approach by the staircase method at 4 Hz. Fractured interfaces and the tension side of unfractured beams were evaluated under SEM, along with the micro-morphology of the etched dentin surfaces and hybrid layers. Data were analyzed by ANOVA and Tukey test and Wilcoxon Rank Sum Test (α = 0.05). RESULTS Quasi-static loads were limited to discriminate the bonding performance of resin-dentin interfaces. Application modes significantly affected etching patterns, fatigue strength, endurance limits and hybrid layer morphology (p < 0.001). SIGNIFICANCE Reductions in fatigue strength of self-etched bonded interfaces raise concerns about the true ability of universal adhesives to properly bond to dentin.
Collapse
Affiliation(s)
- Thiago Henrique Scarabello Stape
- Department of Restorative Dentistry and Cariology, Adhesive Dentistry Research Group, Institute of Dentistry, University of Turku, Turku, Finland; Turku University Hospital, TYKS, University of Turku, Turku, Finland.
| | - Tapio Viita-Aho
- Department of Restorative Dentistry and Cariology, Adhesive Dentistry Research Group, Institute of Dentistry, University of Turku, Turku, Finland; Turku University Hospital, TYKS, University of Turku, Turku, Finland.
| | - Ana Sezinando
- Department of Restorative Dentistry and Cariology, Adhesive Dentistry Research Group, Institute of Dentistry, University of Turku, Turku, Finland.
| | - Patrik Wik
- Department of Restorative Dentistry and Cariology, Adhesive Dentistry Research Group, Institute of Dentistry, University of Turku, Turku, Finland; Turku University Hospital, TYKS, University of Turku, Turku, Finland.
| | - Murat Mutluay
- Department of Restorative Dentistry and Cariology, Adhesive Dentistry Research Group, Institute of Dentistry, University of Turku, Turku, Finland; Turku University Hospital, TYKS, University of Turku, Turku, Finland; Department of Prosthetic Dentistry, Institute of Dentistry, University of Eastern Finland, Kuopio, Finland.
| | - Arzu Tezvergil-Mutluay
- Department of Restorative Dentistry and Cariology, Adhesive Dentistry Research Group, Institute of Dentistry, University of Turku, Turku, Finland; Turku University Hospital, TYKS, University of Turku, Turku, Finland.
| |
Collapse
|