Silver vanadate nanomaterial incorporated into heat-cured resin and coating in printed resin - Antimicrobial activity in two multi-species biofilms and wettability

OBJECTIVES

To incorporate the nanostructured silver vanadate decorated with silver nanoparticles (AgVO3) into denture base materials: heat-cured (HC) and 3D printed (3DP) resins, at concentrations of 2.5 %, 5 %, and 10 %; and to evaluate the antimicrobial activity in two multi-species biofilm: (1) Candida albicans, Candida glabrata, and Streptococcus mutans, (2) Candida albicans, Pseudomonas aeruginosa, and Staphylococcus aureus, and the wettability.

METHODS

The AgVO3 was added to the HC powder, and printed samples were coated with 3DP with AgVO3 incorporated. After biofilm formation, the antimicrobial activity was evaluated by colony forming units per milliliter (CFU/mL), metabolic activity, and epifluorescence microscopy. Wettability was assessed by the contact angles with water and artificial saliva.

RESULTS

In biofilm (1), HC-5 % and HC-10 % showed activity against S. mutans, HC-10 % against C. glabrata, and HC-10 % and 3DP-10 % had higher CFU/mL of C. albicans. 3DP-5 % had lower metabolic activity than the 3DP control. In biofilm (2), HC-10 % reduced S. aureus and P. aeruginosa, and HC-5 %, 3DP-2.5 %, and 3DP-5 % reduced S. aureus. 3DP incorporated with AgVO3, HC-5 %, and HC-10 % reduced biofilm (2) metabolic activity. 3DP-5 % and 3DP-10 % increased wettability with water and saliva.

CONCLUSION

HC-10 % was effective against C. glabrata, S. mutans, P. aeruginosa, and S. aureus, and HC-5 % reduced S. mutans and S. aureus. For 3DP, 2.5 % and 5 % reduced S. aureus. The incorporation of AgVO3 into both resins reduced the metabolic activity of biofilms but had no effect on C. albicans. The wettability of the 3DP with water and saliva increased with the addition of AgVO3.

CLINICAL SIGNIFICANCE

The incorporation of silver vanadate into the denture base materials provides antimicrobial efficacy and can prevent the aggravation of oral and systemic diseases. The incorporation of nanomaterials into printed resins is challenging and the coating is an alternative to obtain the inner denture base with antimicrobial effect.

3D printed denture base material: The effect of incorporating TiO2 nanoparticles and artificial ageing on the physical and mechanical properties

OBJECTIVES

To evaluate the physical and mechanical properties of three-dimensional (3D) printed denture base resin incorporating TiO2 nanoparticles (NPs), subjected to a physical ageing process.

METHODS

Acrylic denture base samples were prepared by a Stereolithography (SLA) 3D printing technique reinforced with different concentrations (0.10, 0.25, 0.50, and 0.75) of silanated TiO2 NPs. The resulting nanocomposite materials were characterized in terms of degree of conversion (DC), and sorption/solubility flexural strength, impact strength, Vickers hardness and Martens hardness and compared with unmodified resin and conventional heat-cured (HC) material. The nanocomposites were reassessed after subjecting them to ageing in artificial saliva. A fractured surface was studied under a scanning electron microscope (SEM).

RESULTS

The addition of TiO2 NPs into 3D-printed resin significantly improved flexural strength/modulus, impact strength, Vickers hardness, and DC, while also slightly enhancing Martens hardness compared to the unmodified resin. Sorption values did not show any improvements, while solubility was reduced significantly. The addition of 0.10 wt% NPs provided the highest performance amongst the other concentrations, and 0.75 wt% NPs showed the lowest. Although ageing degraded the materials' performance to a certain extent, the trends remained the same. SEM images showed a homogenous distribution of the NPs at lower concentrations (0.10 and 0.25 wt%) but revealed agglomeration of the NPs with the higher concentrations (0.50 and 0.75 wt%).

SIGNIFICANCE

The outcomes of this study suggested that the incorporation of TiO2 NPs (0.10 wt%) into 3D-printed denture base material showed superior performance compared to the unmodified 3D-printed resin even after ageing in artificial saliva. The nanocomposite has the potential to extend service life of denture bases in future clinical use.

A Comparison of the Surface and Mechanical Properties of 3D Printable Denture-Base Resin Material and Conventional Polymethylmethacrylate (PMMA)

PURPOSE

To study the surface and mechanical properties of 3D printed denture-base resin materials and compare them with conventional heat-cured polymethylmethacrylate (PMMA).

MATERIALS AND METHODS

Three brands of 3D printed denture-base resin materials and one conventional heat-cured PMMA were tested in this study: NextDent 3D printed resin, Dentona 3D printed resin, ASIGA 3D printed resin, and Meliodent conventional PMMA. Sixty specimens (25 × 25 × 3 mm) were fabricated (n=15 per group) to perform the following tests: wettability, surface roughness, and microhardness. One hundred twenty specimens (65 × 10 × 3 mm) were fabricated (n=30 per group) and stored in distilled water at (37 ±1°C) for 7 days. Specimens (N = 15) in each group were subjected to the three-point bending test and impact strength test, employing the Charpy configuration on un-notched specimens. The morphology of the fractured specimens was studied under scanning electron microscope (SEM). Statistical analysis was performed using one-way ANOVA and Tukey-pairwise multiple comparisons with 95% confidence interval. P-values of ≤0.05 were considered significant.

RESULTS

The conventional heat-cured specimens demonstrated the highest means of surface roughness (0.23 ± 0.07 μm), Vickers hardness number (18.11 ±0.65) and flexural strength (92.44 ±7.91 MPa), and the lowest mean of contact angle (66.71° ±3.38°). ASIGA group showed the highest mean of contact angle (73.44° ±2.74°) and the lowest mean of surface roughness (0.19 ±0.03 μm). The highest mean of impact strength was recorded in the Dentona group (17.98 ±1.76 kg/m² ). NextDent specimens showed the lowest means of Vickers hardness number (16.20 ±0.93), flexural strength (74.89 ±8.44 MPa), impact strength (15.20 ±0.69 kg/m² ), and recorded the highest mean of bending modulus (2,115.80 ±178.95 MPa).

CONCLUSIONS

3D printed resin exhibited noticeable differences in surface and mechanical properties between different brands and with conventional heat-polymerized PMMA.

3D-Printed Nanocomposite Denture-Base Resins: Effect of ZrO2 Nanoparticles on the Mechanical and Surface Properties In Vitro

Due to the low mechanical performances of 3D-printed denture base resins, ZrO2 nanoparticles (ZrO2NPs) were incorporated into different 3D-printed resins and their effects on the flexure strength, elastic modulus, impact strength, hardness, and surface roughness were evaluated. A total of 286 specimens were fabricated in dimensions per respective test and divided according to materials into three groups: heat-polymerized as a control group and two 3D-printed resins (NextDent and ASIGA) which were modified with 0.5 wt.%, 1 wt.%, 3 wt.%, and 5 wt.% ZrO2NPs. The flexure strength and elastic modulus, impact strength, hardness, and surface roughness (µm) were measured using the three-point bending test, Charpy’s impact test, Vickers hardness test, and a profilometer, respectively. The data were analyzed by ANOVA and Tukey’s post hoc test (α = 0.05). The results showed that, in comparison to heat-polymerized resin, the unmodified 3D-printed resins showed a significant decrease in all tested properties (p < 0.001) except surface roughness (p = 0.11). In between 3D-printed resins, the addition of ZrO2NPs to 3D-printed resins showed a significant increase in flexure strength, impact strength, and hardness (p < 0.05) while showing no significant differences in surface roughness and elastic modulus (p > 0.05). Our study demonstrated that the unmodified 3D-printed resins showed inferior mechanical behavior when compared with heat-polymerized acrylic resin while the addition of ZrO2NPs improved the properties of 3D-printed resins. Therefore, the introduced 3D-printable nanocomposite denture-base resins are suitable for clinical use.

Influence of different postcuring parameters on mechanical properties and biocompatibility of 3D printed crown and bridge resin for temporary restorations

This study analyzed the flexural properties, Vickers hardness, degree of conversion (DC), and cell viability of 3D printed crown and bridge resin postcured using various types of postcuring equipment (PCE). 3D printed specimens were postcured for various times using different types of 3D printing PCE [for 5, 15, and 30 min using LC 3D Print Box (LC), Form Cure (FC), Cure M (CM), and Veltz 3D (VE) devices] and the VALO handheld light-curing (VA) device for 20, 40, and 60 s. Neither the flexural strength (132.27-145.79 MPa) nor the flexural modulus (1.52-1.83 GPa) differed significantly when postcuring for 30 min using the LC, FC, CM, or VE device, or for 20, 40, or 60 s of postcuring using the VA device (p > 0.05). The Vickers hardness was highest after 30 min of postcuring for all groups, and varied significantly with the postcuring time in the LC (p < 0.001) and CM (p < 0.001) groups. DC was significantly higher for the 5-min CM group (84.97 ± 4.02%) than for the GS, 30-min FC, 5-min VE, and 20-s VA groups. Cell viability of the postcured resin specimens was 56.46-92.29%, and varied significantly in the CM and VE groups according to the postcuring time (p < 0.05). Confocal laser scanning microscopy observations showed well-developed cell morphology and numerous cell-cell contacts in all groups except the GS group. This study found that the use of different types of PCE did not significantly affect the flexural properties of 3D printed crown and bridge resin, whereas there were significant variations in DC, Vickers hardness, and cell viability.