Influence of Adding Nanoparticles of Silver Vanadate on Antibacterial Effect and Physicochemical Properties of Endodontic Sealers

Introduction

The aim of this study was adding the nanostructured silver vanadate decorated with silver nanoparticles (AgVO₃) (0, 2.5, 5, and 10%) to the endodontic sealers AH-Plus, Sealer 26 and Endomethasone N, and evaluate the antimicrobial activity, solubility and pH.

Methods and Materials

The antimicrobial activity of freshly mixed sealers (n=10) and set sealers (n=9) against Enterococcus faecalis (E. faecalis) was evaluated by colony forming units per milliliter and epifluorescence microscopy. Solubility (n=9) and pH (n=10), 6 and 24 h and 7, 14, and 30 days were also evaluated. The Kruskal-Wallis and Dunn's post-test were applied for the antimicrobial activity of fresh sealers. ANOVA and Tukey's post-test was used for set sealers and solubility, and Friedman's two-way analysis of variance for pH (α=0.05).

Results

The fresh sealers inhibited E. faecalis. Set Sealer 26 (5 and 10% AgVO₃) and Endomethasone N (2.5, 5, and 10% AgVO₃) presented higher activity then the corresponding controls. Modification with AgVO₃ did not influence the solubility of AH Plus and Sealer 26, but Endomethasone N (5%) presented reduced solubility. The AH-Plus groups showed acidic pH, and Sealer 26, basic pH after 30 days. Endomethasone N (5 and 10% AgVO₃) presented statistical difference compared to 0% (P<0.05).

Conclusion

In this in vitro study all fresh sealers and set Sealer 26 (5 and 10%) and Endomethasone N (2.5, 5, and 10%) presented higher antimicrobial activity than controls. The modification with 5% and 10% AgVO₃ decreased solubility and pH of Endomethasone N, but did not affect the other groups.

Effect of Nd:YAG and Diode Lasers on Apical Seal of Root Canals Filled with AH Plus and Mineral Trioxide Aggregate-Based Sealers

OBJECTIVES

Laser irradiation, as an adjunct to root canal preparation, may increase the success rate of endodontic treatments. This study aimed to assess the effect of neodymium-doped yttrium aluminum garnet (Nd:YAG) and diode lasers on the apical seal of the root canals filled with AH Plus® and mineral trioxide aggregate (MTA)-based sealers.

MATERIALS AND METHODS

This in-vitro experimental study was conducted on 96 single-rooted, single-canal extracted human teeth with closed apices. The root canals were prepared by using ProTaper® rotary instruments and were randomly divided into six groups (n=16): 940-nm diode laser and AH Plus® sealer (group 1), Nd:YAG laser and AH Plus® sealer (group 2), AH Plus® sealer (group 3), 940-nm diode laser and MTA-based sealer (group 4), Nd:YAG laser and MTA-based sealer (group 5), MTA-based sealer (group 6), as well as positive and negative control groups. A bacterial leakage model was used for microleakage assessment. Qualitative assessment was done by using a scanning electron microscope (SEM). Data were analyzed by two-way analysis of variance (ANOVA) at the significance level of 0.05.

RESULTS

There were statistically significant differences between the experimental and control groups (P=0.002). The laser-treated groups showed a lower apical microleakage compared to the non-laser-treated groups, although the difference was not statistically significant (P>0.05). No significant differences were noted between the two lasers in terms of the apical microleakage, irrespective of the type of sealer (P>0.05).

CONCLUSIONS

Laser irradiation, as an adjunct to root canal preparation, has no significant effect on the level of apical microleakage.

The Effect of BC Sealer, AH-Plus and Dorifill on Push-out Bond Strength of Fiber Post

Introduction:

Dentinal canal walls are in direct contact with endodontic sealers prior to post space preparation and luting cements after post space preparation. This direct contact may affect the bond strength of intraradicular posts to root dentin. This study aimed to assess the effect of three different sealers on the bond strength of fiber posts to root dentin.

Methods and Materials:

The canals of 56 extracted single-rooted human premolars after selection and decoronation were prepared. For obturation of the canals, specimens were randomly divided into four groups (n=14) according to the type of sealer used in conjunction with gutta-percha: group 1 (control) without any sealer; group 2 with AH-Plus sealer (resin based); group 3 with Dorifill sealer (ZOE-based); and group 4 with BC Sealer (calcium silicate-based). Nine mm-deep post space was prepared in the canal of each specimen. Intraradicular fiber posts were cemented using dual-cure resin cement (Panavia F2.0). Sections of 1 mm thickness were made at the coronal, middle and apical thirds of the post space of each specimen. The push-out bond strength of post to root dentin was measured in a universal testing machine. The data were analyzed using one-way ANOVA and post-hoc Tukey’s test.

Results:

The mean push-out bond strength in the coronal third was significantly lower in Dorifill group compared to AH-Plus (P=0.004). This value was significantly lower in BC Sealer group than AH-Plus (P=0.000) and control group (P=0.03). In middle and apical thirds, the mean push-out bond strength was not significantly different among the four groups (P=0.407, P=0.065, respectively). The mean push-out bond strength was significantly lower in apical than coronal third in AH-Plus group (P=0.001).

Conclusion:

Application of BC Sealer and Dorifill decreased the mean push-out bond strength of intracanal post to root dentin in the coronal third in comparison to AH-Plus.