Intraoral wear of PICN CAD-CAM composite restorations used in severe tooth wear treatment: 5-year results of a prospective clinical study using 3D profilometry

OBJECTIVES

To evaluate, in a prospective clinical study over 5 years with ex vivo 3D profilometry analyses, the intraoral wear of Polymer-Infiltrated Ceramic Network (PICN) CAD-CAM composite restorations used in severe tooth wear treatment with the One-Step No-Prep technique.

METHODS

192 PICN (Vita Enamic) restorations on molars and premolars were included in a prospective clinical study involving patients treated according to the One-step No-prep protocol (n = 7). All patients showed clinical signs of bruxism. Replicas of restorations on molars and premolars were realized at each evaluation time (baseline and then every year up to 5 years) and scanned to perform 3D profilometry. Baseline and recall scans were superimposed with Geomagic Control software. The mean material wear was calculated for the full occlusal area (FOA) and for the occlusal contact area (OCA), respectively. Clinical evaluation of restorations was performed at recall.

RESULTS

At 5 years, the estimated mean material wear for FOA was inferior to the accuracy threshold of the profilometry measurement chain. For OCA, the estimated mean wear of the material was - 27.97 µm. This material wear was shown to be significantly influenced by time (p < 0.0001) and patient (p = 0.026), while the type of tooth (molar or premolar) had no influence. At 5 years, the survival and the success rates of restorations were 99.48% and 90.62%, respectively.

SIGNIFICANCE

The PICN material exhibits a low wear process in the treatment of severe tooth wear despite the presence of clinical signs of bruxism, and it constitutes a suitable material for the One-step No-prep technique.

In vitro evaluation of fissure sealants' wear under erosive, abrasive and erosive/abrasive conditions

PURPOSE

To evaluate and compare the wear of selected resin-based fissure sealants with different compositions properties under erosive, abrasive, and erosive/abrasive conditions.

METHODS

Forty-five samples of the following resin-based fissure sealants were prepared: Fissurit (fluoride free), Fissurit F (with fluoride), Fissurit FX (55 wt.% filler content), Grandio Seal (70 wt.% nano-filler content) and bovine enamel. Fifteen samples from each material were randomly allocated into three groups according to the wear condition they would be subjected to as follows: erosive condition (citric acid, 1 min, pH 2.3), abrasive condition (120 brushing strokes at 2 N, toothpaste slurry RDA value = 69), and erosive/abrasive condition (combination of both). The wear challenges were repeated six times each day for 10 days. The material wear was measured using a stylus profilometer. Kruskal-Wallis and Conover's test was applied to compare the resulting material wear between the groups.

RESULTS

Under erosive conditions, Grandio Seal and Fissurit FX showed statistically significantly the least material wear. Under abrasive and erosive/abrasive conditions, Grandio Seal showed statistically significantly the least material wear. Fissurit F showed statistically significantly the highest material wear under abrasive and erosive/abrasive conditions, after dental enamel (p < 0.05).

CONCLUSION

Higher filler content in sealants leads to better wear resistance. Incorporating fluoride into sealants seems to reduce their wear resistance at similar filler contents.