Detecting Multiple Damages in UHPFRC Beams through Modal Curvature Analysis

Curvature-based damage detection has been previously applied to identify damage in concrete structures, but little attention has been given to the capacity of this method to identify distributed damage in multiple damage zones. This study aims to apply for the first time an enhanced existing method based on modal curvature analysis combined with wavelet transform curvature (WTC) to identify zones and highlight the damage zones of a beam made of ultra-high-performance fiber-reinforced concrete (UHPFRC), a construction material that is emerging worldwide for its outstanding performance and durability. First, three beams with a 2 m span of UHPFRC material were cast, and damaged zones were created by sawing. A reference beam without cracks was also cast. The free vibration responses were measured by 12 accelerometers and calculated by operational modal analysis. Moreover, for the sake of comparison, a finite element model (FEM) was also applied to two identical beams to generate numerical acceleration without noise. Second, the modal curvature was calculated for different modes for both experimental and FEM-simulated acceleration after applying cubic spline interpolation. Finally, two damage identification methods were considered: (i) the damage index (DI), based on averaging the quadratic difference of the local curvature with respect to the reference beam, and (ii) the WTC method, applied to the quadratic difference of the local curvature with respect the reference beam. The results indicate that the developed coupled modal curvature WTC method can better identify the damaged zones of UHPFRC beams.

Electrical and Self-Sensing Properties of Ultra-High-Performance Fiber-Reinforced Concrete with Carbon Nanotubes

This study examined the electrical and self-sensing capacities of ultra-high-performance fiber-reinforced concrete (UHPFRC) with and without carbon nanotubes (CNTs). For this, the effects of steel fiber content, orientation, and pore water content on the electrical and piezoresistive properties of UHPFRC without CNTs were first evaluated. Then, the effect of CNT content on the self-sensing capacities of UHPFRC under compression and flexure was investigated. Test results indicated that higher steel fiber content, better fiber orientation, and higher amount of pore water led to higher electrical conductivity of UHPFRC. The effects of fiber orientation and drying condition on the electrical conductivity became minor as sufficiently high amount of steel fibers, 3% by volume, was added. Including only steel fibers did not impart UHPFRC with piezoresistive properties. Addition of CNTs substantially improved the electrical conductivity of UHPFRC. Under compression, UHPFRC with a CNT content of 0.3% or greater had a self-sensing ability that was activated by the formation of cracks, and better sensing capacity was achieved by including greater amount of CNTs. Furthermore, the pre-peak flexural behavior of UHPFRC was precisely simulated with a fractional change in resistivity when 0.3% CNTs were incorporated. The pre-cracking self-sensing capacity of UHPFRC with CNTs was more effective under tensile stress state than under compressive stress state.

Feasibility of Reducing the Fiber Content in Ultra-High-Performance Fiber-Reinforced Concrete under Flexure

In this study, the flexural behavior of ultra-high-performance fiber-reinforced concrete (UHPFRC) is examined as a function of fiber length and volume fraction. Straight steel fiber with three different lengths (l_f) of 13, 19.5, and 30 mm and four different volume fractions (v_f) of 0.5%, 1.0%, 1.5%, and 2.0% are considered. Test results show that post-cracking flexural properties of UHPFRC, such as flexural strength, deflection capacity, toughness, and cracking behavior, improve with increasing fiber length and volume fraction, while first-cracking properties are not significantly influenced by fiber length and volume fraction. A 0.5 vol % reduction of steel fiber content relative to commercial UHPFRC can be achieved without deterioration of flexural performance by replacing short fibers (l_f of 13 mm) with longer fibers (l_f of 19.5 mm and 30 mm).