Carbon nanomaterials as catalysts for hydrogen uptake and release in NaAlH4

Synthesis and characterization of a lithium-doped fullerane (Li(x)-C60-H(y)) for reversible hydrogen storage

Herein, we present a lithium-doped fullerane (Li(x)-C(60)-H(y)) that is capable of reversibly storing hydrogen through chemisorption at elevated temperatures and pressures. This system is unique in that hydrogen is closely associated with lithium and carbon upon rehydrogenation of the material and that the weight percent of H(2) stored in the material is intimately linked to the stoichiometric ratio of Li:C(60) in the material. Characterization of the material (IR, Raman, UV-vis, XRD, LDI-TOF-MS, and NMR) indicates that a lithium-doped fullerane is formed upon rehydrogenation in which the active hydrogen storage material is similar to a hydrogenated fullerene. Under optimized conditions, a lithium-doped fullerane with a Li:C(60) mole ratio of 6:1 can reversibly desorb up to 5 wt % H(2) with an onset temperature of ~270 °C, which is significantly less than the desorption temperature of hydrogenated fullerenes (C(60)H(x)) and pure lithium hydride (decomposition temperature 500-600 and 670 °C respectively). However, our Li(x)-C(60)-H(y) system does not suffer from the same drawbacks as typical hydrogenated fullerenes (high desorption T and release of hydrocarbons) because the fullerene cage remains mostly intact and is only slightly modified during multiple hydrogen desorption/absorption cycles. We also observed a reversible phase transition of C(60) in the material from face-centered cubic to body-centered cubic at high levels of hydrogenation.

Theoretical study of C60 as catalyst for dehydrogenation in LiBH4

Complex light metal hydrides possess many properties which make them attractive as a storage medium for hydrogen, but typically catalysts are required to lower the hydrogen desorption temperature and to facilitate hydrogen uptake in the form of a reversible reaction. The overwhelming focus in the search for catalysing agents has been on compounds containing titanium, but the precise mechanism of their actions remains somewhat obscure. A recent experiment has now shown that fullerenes (C(60)) can also act as catalysts for both hydrogen uptake and release in lithium borohydride (LiBH(4)). In an effort to understand the involved mechanism, we have employed density functional theory to carry out a detailed study of the interaction between this complex metal hydride and the carbon nanomaterial. Considering a stepwise reduction of the hydrogen content in LiBH(4), we find that the presence of C(60) can lead to a substantial reduction of the involved H-removal energies. This effect is explained as a consequence of the interaction between the BH(x)( - ) complex and the C(60) entity.

Improved hydrogen storage kinetics of nanoconfined NaAlH₄ catalyzed with TiCl₃ nanoparticles

Nanoparticles of NaAlH(4) have been infiltrated in nanoporous carbon aerogel with TiCl(3) nanoparticles in order to explore possible synergetic effects between nanoconfinement and a functionalized catalytic scaffold. Resorcinol formaldehyde carbon aerogels with an average pore size of 17 nm and total pore volume of 1.26 mL/g were infiltrated with TiCl(3) to obtain an aerogel doped with 3.0 wt % TiCl(3) nanoparticles. NaAlH(4) was melt-infiltrated into the functionalized carbon aerogel at 189 °C and p(H(2)) ∼ 186-199 bar. Energy-dispersive spectrometry (EDS) combined with focused ion beam (FIB) techniques revealed the presence of Na, Al, Ti, and Cl inside the aerogel scaffold material. The infiltrated NaAlH(4) was X-ray amorphous, whereas (27)Al magic-angle spinning (MAS) NMR spectroscopy confirmed the presence of nanoconfined NaAlH(4). Temperature-programmed desorption mass spectroscopy (TPD-MS) and Sieverts' measurements demonstrated significantly improved hydrogen desorption kinetics for this new nanoconfined NaAlH(4)-TiCl(3) material as compared to nanoconfined NaAlH(4) without the catalysts TiCl(3) and to bulk ball-milled samples of NaAlH(4)-TiCl(3). We find that the onset temperature for hydrogen release was close to room temperature (T(onset) = 33 °C), and the hydrogen release rate reached a maximum value at 125 °C, which demonstrates favorable synergetic effects between nanoconfinement and catalyst addition.

Nanoconfined hydrides for energy storage

The world in the 21(st) century is facing increasing challenges within the development of more environmentally friendly energy systems, sustainable and 'green chemistry' solutions for a variety of chemical and catalytic processes. Nanomaterials science is expected to contribute strongly by the development of new nanotools, e.g. for improving the performance of chemical reactions. Nanoconfinement is of increasing interest and may lead to significantly enhanced kinetics, higher degree of stability and/or more favourable thermodynamic properties. Nanoconfined chemical reactions may have a wide range of important applications in the near future, e.g. within the merging area of chemical storage of renewable energy. This review provides selected examples within nanoconfinement of hydrogen storage materials, which may serve as an inspiration for other research fields as well. Selected nanoporous materials, methods for preparation of nanoconfined systems and their hydrogen storage properties are reviewed.

Nanosizing and nanoconfinement: new strategies towards meeting hydrogen storage goals

Hydrogen is expected to play an important role as an energy carrier in a future, more sustainable society. However, its compact, efficient, and safe storage is an unresolved issue. One of the main options is solid-state storage in hydrides. Unfortunately, no binary metal hydride satisfies all requirements regarding storage density and hydrogen release and uptake. Increasingly complex hydride systems are investigated, but high thermodynamic stabilities as well as slow kinetics and poor reversibility are important barriers for practical application. Nanostructuring by ball-milling is an established method to reduce crystallite sizes and increase reaction rates. Since five years attention has also turned to alternative preparation techniques that enable particle sizes below 10 nanometers and are often used in conjunction with porous supports or scaffolds. In this Review we discuss the large impact of nanosizing and -confinement on the hydrogen sorption properties of metal hydrides. We illustrate possible preparation strategies, provide insight into the reasons for changes in kinetics, reversibility and thermodynamics, and highlight important progress in this field. All in all we provide the reader with a clear view of how nanosizing and -confinement can beneficially affect the hydrogen sorption properties of the most prominent materials that are currently considered for solid-state hydrogen storage.

Advanced materials for energy storage

Popularization of portable electronics and electric vehicles worldwide stimulates the development of energy storage devices, such as batteries and supercapacitors, toward higher power density and energy density, which significantly depends upon the advancement of new materials used in these devices. Moreover, energy storage materials play a key role in efficient, clean, and versatile use of energy, and are crucial for the exploitation of renewable energy. Therefore, energy storage materials cover a wide range of materials and have been receiving intensive attention from research and development to industrialization. In this Review, firstly a general introduction is given to several typical energy storage systems, including thermal, mechanical, electromagnetic, hydrogen, and electrochemical energy storage. Then the current status of high-performance hydrogen storage materials for on-board applications and electrochemical energy storage materials for lithium-ion batteries and supercapacitors is introduced in detail. The strategies for developing these advanced energy storage materials, including nanostructuring, nano-/microcombination, hybridization, pore-structure control, configuration design, surface modification, and composition optimization, are discussed. Finally, the future trends and prospects in the development of advanced energy storage materials are highlighted.