Investigation on the Tensile Behavior and Morphology Evolution of Isotactic Polypropylene Films Polymerized with Different Ziegler-Natta Catalysts

Impacts of Modified Graphite Oxide on Crystallization, Thermal and Mechanical Properties of Polybutylene Terephthalate

In this study, the surface modification on graphene oxide (GO) was performed using octadecylamine (ODA). Furthermore, polybutylene terephthalate/GO (PBT/GO) composites were prepared to elucidate the role of GO surface modification on the mechanical performance, thermal stability and crystallization behavior. Results of Fourier transform infrared spectra (FT-IR), Raman spectrum, thermogravimetric analysis (TGA), X-ray photoelectron spectroscopy (XPS) and transmission electron microscope (TEM) revealed that ODA was successfully grafted on GO. Differential scanning calorimetry (DSC), wide-angle X-ray diffraction (WAXD), tensile test, Izod impact strength test and TGA were carried out on the PBT/GO composites. Results indicated that the addition of raw GO can enhance the crystallization temperature and degree of crystallinity and can slightly improve the thermal stability and tensile strength of the composites. However, the impact strength and elongation at break were seriously decreased owing to the poor compatibility between the GO and PBT matrix. Once the modified GO was added, the crystallization temperature and degree of crystallinity were greatly increased. The tensile strength increased greatly while the elongation at break and Izod impact strength were efficiently maintained; these were evidently higher than those of PBT/raw GO. Moreover, thermal stability was greatly enhanced. SEM (scanning electron microscope) observation results on the impact-fractured surface clearly confirmed the improved compatibility between the modified GO and PBT matrix. A related mechanism had been discussed.

Effects of Polypropylene Orientation on Mechanical and Heat Seal Properties of Polymer-Aluminum-Polymer Composite Films for Pouch Lithium-Ion Batteries

In this study, polyamide-aluminum foil-polypropylene (PA-Al-PP) composite films with different orientation status of the PP layer were prepared, and their morphology, tensile, peeling and heat seal behavior were studied. The comparative study of tensile and fracture behaviors of single-layer film of PA, Al and PP, as well as the composite films of PA-Al, PP-Al and PA-Al-PP revealed that in PA-Al-PP composite film, the PA layer with the highest tensile strength can share the tensile stress from the Al layer during stretching, while the PP layer with the lowest tensile strength can prevent further development of the small cracks on boundary of the Al layer during stretching. Moreover, the study of heat seal behavior suggested that both the orientation status and the heat seal conditions were important factors in determining the heat seal strength (HSS) and failure behavior of the sample. Four failure types were observed, and a clear correspondence between HSS and failure types was found. The results also elucidated that for the composite film, only in the cases where the tensile stress was efficiently released by each layer during HSS measurement could the composite film exhibit desired high HSS that was even higher than its tensile strength.