Macromolecular Insights into the Altered Mechanical Deformation Mechanisms of Non-Polyolefin Contaminated Polyolefins

Current recycling technologies rarely achieve 100% pure plastic fractions from a single polymer type. Often, sorted bales marked as containing a single polymer type in fact contain small amounts of other polymers as contaminants. Inevitably, this will affect the properties of the recycled plastic. This work focuses on understanding the changes in tensile deformation mechanism and the related mechanical properties of the four dominant types of polyolefin (PO) (linear low-density polyethylene (LLDPE), low-density polyethylene (LDPE), high-density polyethylene (HDPE), and polypropylene (PP)), contaminated with three different non-polyolefin (NPO) polymers (polyamide-6 (PA-6), polyethylene terephthalate (PET), and polystyrene (PS)). Under the locally elevated stress state induced by the NPO phase, the weak interfacial adhesion typically provokes decohesion. The resulting microvoids, in turn, initiate shear yielding of the PO matrix. LLDPE, due to the linear structure and intercrystalline links, is well able to maintain high ductility when contaminated. LDPE shows deformation similar to the pure material, but with decreasing ductility as the amount of NPO increases. Addition of 20 wt% PA-6, PET, and PS causes a drop in strain at break of 79%, 63%, and 84%, respectively. The typical ductile necking of the high-crystalline HDPE and PP is strongly disturbed by the NPO phase, with a transition even to full brittle failure at high NPO concentration.

The Effect of Injection Molding Temperature on the Morphology and Mechanical Properties of PP/PET Blends and Microfibrillar Composites

Within this research the effect of injection molding temperature on polypropylene (PP)/poly(ethylene terephthalate) (PET) blends and microfibrillar composites was investigated. Injection molding blends (IMBs) and microfibrillar composites (MFCs) of PP/PET have been prepared in a weight ratio 70/30. The samples were processed at three different injection molding temperatures (T_im) (210, 230, 280 °C) and subjected to extensive characterization. The observations from the fracture surfaces of MFCs showed that PET fibers can be achieved by three step processing. The results indicated that T_im has a big influence on morphology of IMBs and MFCs. With increasing the T_im, distinctive variations in particle and fiber diameters were noticed. The differences in mechanical performances were obtained by flexural and impact tests. Establishing relationships between the processing parameters, properties, and morphology of composites is of key importance for the valorization of MFC polymers.