Degradation of carbon tetrachloride using ultrasound‐assisted nanoscaled zero‐valent iron particles@sulfur/nitrogen dual‐doped reduced graphene oxide composite: Kinetics, activation energy, effects of reaction conditions and degradation mechanism

A review of the new multifunctional nano zero-valent iron composites for wastewater treatment: Emergence, preparation, optimization and mechanism

Nano zero-valent iron (NZVI) with high chemical reactivity and environmental friendliness had recently become one of the most efficient technologies for wastewater restoration. However, the unitary NZVI system had not met practical requirements for wastewater treatments. Expectantly, the development of NZVI would prefer multifunctional NZVI-based composites, which could be prepared and optimized by the combined methods and technologies. Consequently, a systematic and comprehensive summary from the perspective of multifunctional NZVI-composite had been conducted. The results demonstrated that the advantages of various systems were integrated by multifunctional NZVI-composite systems with a more significant performance of pollutant removal than those of the bare NZVI and its composites. Simultaneously, characteristics of the product prepared by the incorporation of numerous methods were superior to those by a simple method, resulting in the increase of the entirety efficiency. By comparison with other preparation methods, the ball milling method with higher production and field application potential was worthy of attention. After combining multiple technologies, the effect of NZVI and its composite systems could be dramatically strengthened. Preparation technology parameters and treatment effect of contaminants could be further optimized using more comprehensive experimental designs and mathematical models. The mechanism of the multifunctional NZVI system for contaminants treatment was primarily focused on adsorption, oxidation, reduction and co-precipitation. Multiple techniques were combined to enhance the dispersion, alleviating passivation, accelerating electron transfer efficiency or mass transfer action for optimizing the effect of NZVI composites.

Efficient Sequestration of Hexavalent Chromium by Graphene-Based Nanoscale Zero-Valent Iron Composite Coupled with Ultrasonic Pretreatment

Nanoscale zero-valent iron (nZVI) has attracted considerable attention for its potential to sequestrate and immobilize heavy metals such as Cr(VI) from an aqueous solution. However, nZVI can be easily oxidized and agglomerate, which strongly affects the removal efficiency. In this study, graphene-based nZVI (nZVI/rGO) composites coupled with ultrasonic (US) pretreatment were studied to solve the above problems and conduct the experiments of Cr(VI) removal from an aqueous solution. SEM-EDS, BET, XRD, and XPS were performed to analyze the morphology and structures of the composites. The findings showed that the removal efficiency of Cr(VI) in 30 min was increased from 45.84% on nZVI to 78.01% on nZVI/rGO and the removal process performed coupled with ultrasonic pretreatment could greatly shorten the reaction time to 15 min. Influencing factors such as the initial pH, temperature, initial Cr(VI) concentration, and co-existing anions were studied. The results showed that the initial pH was a principal factor. The presence of HPO₄²⁻, NO₃⁻, and Cl⁻ had a strong inhibitory effect on this process, while the presence of SO₄²⁻ promoted the reactivity of nZVI/rGO. Combined with the above results, the process of Cr(VI) removal in US-nZVI/rGO system consisted of two phases: (1) The initial stage is dominated by solution reaction. Cr(VI) was reduced in the solution by Fe²⁺ caused by ultrasonic cavitation. (2) In the following processes, adsorption, reduction, and coprecipitation coexisted. The addition of rGO enhanced electron transportability weakened the influence of passivation layers and improved the dispersion of nZVI particles. Ultrasonic cavitation caused pores and corrosion at the passivation layers and fresh Fe⁰ core was exposed, which improved the reactivity of the composites.