Miscibility and crystallization behaviors of biodegradable poly(butylene succinate-co-butylene terephthalate)/phenoxy blends

Effect of Styrene-Maleic Anhydride Copolymer on Properties of PBST/PLA Blends

Poly(butylene succinate-butylene terephthalate) (PBST) and polylactic acid (PLA) are both biodegradable polymeric materials. PBST has good ductility but low strength, while PLA exhibits high strength but poor toughness. Based on the complementary mechanical properties of the two polymers, PBST/PLA blends were prepared by melt blending in the mixing chamber of a torque rheometer using styrene-maleic anhydride copolymer (PSMA) as a compatibilizer. The effects of different contents of PSMA on the crystalline properties, thermal properties, mechanical properties, rheological behavior, and morphology of PBST/PLA blends were investigated. The results showed that the addition of PSMA improved the compatibility between PBST and PLA. When the amount of PSMA is 3-4 wt%, the comprehensive mechanical properties of the blends are optimal, and the tensile strength was increased by 61.7% compared with the binary blend without PSMA. Additionally, rheological tests illustrated that the blends exhibited a typical shear-thinning behavior and belonged to pseudoplastic non-Newtonian fluids.

The Relationship between Microstructure and Mechanical Properties of PBST Two-Component Crystalline Random Copolymers with Different BT Contents

The mechanical properties of two-component crystalline random copolymers are primarily based on their microstructure. At the same time, the influence of the composition on the crystallization behavior and crystal structure of these materials is also well known. Thus, in this study, a poly (butylene succinate-co-butylene terephthalate) random copolymer (PBST) with different molar ratios of butylene terephthalate (BT) was prepared. A systematic analysis of the crystallization behavior, crystal structure, and mechanical properties of PBST with different BT contents was carried out using WAXD, SAXS, and DSC analyses. The investigations showed that PBST-37.5 containing 37.5 mol% of BT content had the lowest strength and highest elasticity among the different compositions. This was because the two-component crystallization of poly (butylene terephthalate) (PBT) and poly (butylene succinate) (PBS) was greatly inhibited at the corresponding BT composition and the crystal growth was the least perfect, imparting poor strength to the PBT-37.5. Alternately, when the content of BT was 32.5 mol% in the PBST, the PBS segment could crystallize, and both PBT and PBS crystals were formed in the PBST-32.5. Thus, PBST-32.5 showed a higher material hardness than PBST-37.5. In contrast, when the BT content was greater than 37.5 mol% in the PBST, only PBT crystals existed in the PBST copolymer. Further, as the BT content increased, the crystal size of PBT gradually increased, which led to a closer packing of the crystal arrangement, increasing the crystallinity. This led to a gradual increase in the strength of the PBST material and a gradual decrease in its elasticity.

In-situ reaction compatibilization modification of poly(butylene succinate-co-terephthalate)/polylactide acid blend films by multifunctional epoxy compound

Poly(butylene succinate-co-terephthalate) (PBST) copolyester, is a new type of biodegradable synthetic polymer material that has emerged in recent years, but it cannot meet the market requirements, because of its low strength. The high-strength and high-modulus polylactic acid (PLA) was blended with PBST to increase its strength, and the chain extender ADR-4370 was used to modify PBST/PLA films by reaction and compatibilization. Compared with the 80/20 wt% PBST/PLA films, the tensile strength after modification with 0.3 wt% ADR was increased by 21.8 % and 44.3 % in the machine direction (MD) and in the transverse direction (TD), respectively. The Water Vapor Permeability (WVP) was decreased from 10.0 × 10^-14 to 3.09 × 10^-14 g·cm/cm²·s·Pa. The compatibilization mechanism was studied by gel permeation chromatography, infrared spectroscopy, dynamic mechanical analysis, rheological analysis, and other characterization methods. The formation of the copolymer PLA-g-PBST is the most important factor to improve the compatibility of the system and the mechanical properties of the films.