Facile and Low Environmental Impact Approach to Prepare Thermally Conductive Nanocomposites Based on Polylactide and Graphite Nanoplatelets

In this work, the preparation of nanocomposites based on poly(l-lactide) PLLA and graphite nanoplatelets (GNP) was assessed by applying, for the first time, the reactive extrusion (REX) polymerization approach, which is considered a low environmental impact method to prepare polymer systems and which allows an easy scalability. In particular, ad hoc synthesized molecules, constituted by a pyrene end group and a poly(d-lactide) (PDLA) chain (Pyr-d), capable of interacting with the surface of GNP layers as well as forming stereoblocks during the ring-opening polymerization (ROP) of l-lactide, were used. The nanocomposites were synthesized by adding to l-lactide the GNP/initiator system, prepared by dispersing the graphite in the acetone/Pyr-d solution, which was dried after the sonication process. DSC and X-ray diffraction measurements evidenced the stereocomplexation of the systems synthesized by using the pyrene-based initiators, whose extent turned out to depend on the PDLA chain length. All the prepared nanocomposites, including those synthesized starting from a classical initiator, that is, 1-dodecanol, retained similar electrical conductivity, whereas the thermal conductivity was found to increase in the stereocomplexed samples. Preferential localization of stereocomplexed PLA close to the interface with GNP was demonstrated by scanning probe microscopy (SPM) techniques, supporting an important role of local crystallinity in the thermal conductivity of the nanocomposites.

Solid-State Nuclear Magnetic Resonance (NMR) and Nuclear Magnetic Relaxation Time Analyses of Molecular Mobility and Compatibility of Plasticized Polyhydroxyalkanoates (PHA) Copolymers

The molecular mobility and compatibility of plasticized polyhydroxyalkanoates (PHA) were investigated, focusing on changes due to copolymerization using either flexible poly (butylene succinate) (PBS) or rigid poly(lactic acid) (PLA) units. For the case of a poly(3-hydroxybutyrate) (PHB) unit in plasticized PHA, copolymerization of either PBS or PLA decreased ¹H and 13C spin-lattice relaxation times in the laboratory frame (T₁H and T₁C) in the same manner, while PBS produced a lower ¹H spin-lattice relaxation time in the rotating frame (T₁ρH) than PLA. Both the signals of ¹H MAS (magic-angle spinning) and 13C PST (pulse saturation transfer) MAS nuclear magnetic resonance (NMR) spectra were sharpened and increased by copolymerization with PBS. A variable temperature relaxation time analysis showed that the decrease of T₁H values was dominated by the ¹H spin diffusion via the interface between PHB and the added polyester because of the good compatibility. Meanwhile, the decrease of T₁C values was dominated by increasingly rapid molecular motions of PHB because of the lowered crystallinity due to the plasticization. Slow molecular motions (kHz order) were enhanced more by the addition of PBS than PLA, although rapid molecular motions (MHz order) were enhanced by either polyester. Several NMR parameters were beneficial for analyzing the manufacturing process as the indexes of polymer compatibility and molecular motions.

Nucleating and Plasticization Effects in Drawn Poly(Lactic Acid) Fiber during Accelerated Weathering Degradation

Changes in the polymer properties of poly(lactic acid) (PLA) fibers during drawing and degradation processes were analyzed using solid-state NMR, with the goal of elucidating morphological changes that influence fiber tensile properties. Combination of X-ray diffraction (XRD) and differential scanning calorimeter (DSC) indicated that the drawn PLA fibers consisted of different proportions of α crystalline and amorphous forms. ¹³C CP-MAS NMR spectra showed amorphous-like broad singlet signals, of which the full width at half maximum (FWHM) decreased with increasing crystallinity and crystal orientation. The T₁H value decreased by interaction with additives and increased with increasing crystal orientation. The interaction with additives also reduced T₁C values, which increased with increasing crystallinity. Use of organic clay enhanced the crystallization of high draw-ratio PLA fibers due to nucleation, which increased tensile strength; this effect gradually decreased with time during accelerated weathering. In contrast, the plasticization due to the addition of flexible polymers increased fiber elongation, which rapidly dropped during the degradation. Changes of FWHM, T₁H, and T₁C values indicated that the degradation occurred at sites within the amorphous portions of the PLA fibers containing organic clay, while the flexible polymers were preferentially degraded if they were present in the PLA fibers.

Integrated analysis of solid-state NMR spectra and nuclear magnetic relaxation times for the phenol formaldehyde (PF) resin impregnation process into soft wood

Integrated analysis using a solid-state NMR method revealed that PF resin permeated not only lignin but also carbohydrate polymers.