Self-crosslinkable epoxidized natural rubber-silica hybrids

Natural Phenolic Compounds as Modifiers for Epoxidized Natural Rubber/Silica Hybrids

Silica is a popular filler, but in epoxidized natural rubber, can act as a cross-linking agent. Unfortunately, a high amount of silica is necessary to obtain satisfactory tensile strength. Moreover, a high amount of silica in ENR/silica hybrids is associated with low elongation at break. In our paper, we propose natural phenolic compounds, including quercetin, tannic acid, and gallic acid as natural and safe additional crosslinkers dedicated to ENR/silica hybrids to obtain bio-elastomers with improved mechanical properties. Therefore, toxic crosslinkers, such as peroxides or harmful accelerators can be eliminated. The impact of selected natural phenolic compounds on crosslinking effect, mechanical properties, color, and chemical structure of ENR/silica composite have been analyzed. The obtained results indicated that only 3 phr of selected natural phenolic compounds is able to improve crosslinking effect as well as mechanical properties of ENR/silica hybrids. Moreover, some of the prepared materials tend to regain mechanical properties after reprocessing. Such materials containing only natural and safe ingredients have a chance of becoming novel elastomeric biomaterials dedicated to biomedical applications.

Aging Resistance of Biocomposites Crosslinked with Silica and Quercetin

This research focuses on revealing the double role of quercetin accompanied by silica in epoxidized natural rubber. A crosslinking ability with antioxidative properties exists and reveals the dependence of these functions on quercetin content. Here, the aging resistance of self-healable biocomposites was analyzed. The self-healing properties were presented in our previous work. The stabilizing effect of quercetin applied as a crosslinking agent has been studied in epoxidized natural rubber with a 50 mol% of epoxidation (ENR-50). Some of five -OH moiety groups existing in the quercetin structure are able to react with epoxy rings of ENR-50 and cure this elastomer, whereas other free hydroxyl groups can donate the hydrogen molecule to a radical molecule, stabilizing it. The aging resistance of prepared composites was estimated by mechanical tests conducted before and after different types of aging, as well as by differences in color and surface energy between aged and un-aged samples. Changes within the oxygen function, which occurred as a result of the aging process, were observed using FT-IR absorbance spectroscopy. Furthermore, the impact of quercetin content on composites’ thermal stability was investigated by thermogravimetry (TGA). According to the results, a proper dose of quercetin can act as a crosslinker and antioxidant in ENR-50 at the same time.

Self-Healable Biocomposites Crosslinked with a Combination of Silica and Quercetin

In this publication, novel bio-based composites made of epoxidized natural rubber with 50 mol% of epoxidation (ENR-50) are presented. The obtained materials, partially cured with a totally environmentally friendly crosslinking system consisting of natural ingredients, including quercetin and silica, exhibit a self-healing ability resulting from the self-adhesion of ENR-50 and reversible physical forces between the curing agent and the matrix. The impact of natural components on the crosslinking effect in uncured ENR-50 matrix was analyzed based on rheometric measurements, mechanical tests and crosslinking density. The partially crosslinked samples were next cut into two separate pieces, which were instantly contacted together under a small manual press, left at room temperature for a few days for the healing process to occur and finally retested. The healing efficiency was estimated by measuring mechanical properties before and after the healing process and was also confirmed by photos taken using optical and scanning electron microscope (SEM). According to the results, a combination of silica and quercetin is a totally safe, natural and effective crosslinking system dedicated to epoxidized natural rubber. The novel composites containing ingredients safe for human beings exhibit promising self-healing properties with a healing efficiency of up to 45% without any external stimuli and stand a chance of becoming innovative biomedical materials.

Effect of SiO2 Particles on the Relaxation Dynamics of Epoxidized Natural Rubber (ENR) in the Melt State by Time-Resolved Mechanical Spectroscopy

The rheological behavior of an epoxidized natural rubber (ENR) nanocomposite containing 10 wt.% of silica particles was examined by time-resolved mechanical spectroscopy (TRMS), exploiting the unique capability of this technique for monitoring the time-dependent characteristics of unstable polymer melts. The resulting storage modulus curve has revealed a progressive evolution of the elastic component of the composite, associated with slower relaxations of the ENR macromolecular chains. Two major events were identified and quantified: one is associated with the absorption of the epoxidized rubber macromolecules onto the silica surface, which imposes further restrictions on the motions of the chains within the polymer phase; the second is related to gelation and the subsequent changes in rheological behavior resulting from the simultaneous occurrence cross-linking and chain scission reactions within the ENR matrix. These were quantified using two parameters related to changes in the storage and loss modulus components.