Foamed polyurethane plastics of reduced flammability

Bio-Based Alkali Lignin Cooperative Systems for Improving the Flame Retardant and Mechanical Properties of Rigid Polyurethane Foam

Lignin was utilized as an environmentally friendly synergistic agent to augment the fire resistance and mechanical characteristics of rigid polyurethane foam (PUF)/melamine-formaldehyde resin ammonium polyphosphate (MFAPP). The incorporation of lignin significantly enhanced the charring capability and flame retardancy of PUF/MFAPP. Specifically, PUF/MFAPP12/A-lignin3 exhibited a charring residue of 23.1% at 800 °C, accompanied by an increase in the limiting oxygen index (LOI) to 23.1%, resulting in a UL-94 V-0 rating. The cone calorimeter test (CCT) revealed that the peak heat release rate (PHRR), total heat release (THR), smoke production rate (SPR), and total smoke production (TSP) values of PUF/MFAPP12/A-lignin3 were all lower than for pure PUF. MFAPP and alkali lignin exerted a noticeable influence on the physical and mechanical properties, leading to increases in density (35.4 kg/m3), thermal conductivity (32.68 mW/(m·K)), and compressive strength (160.5 kPa). Observations of the morphology and elemental composition of char residues after combustion indicated the formation of an intact, thick, and continuous char layer enriched with nitrogen and phosphorus elements, which acted as a protective shield for the underlying foam.

Synthesis and Characterization of Flame Retarded Rigid Polyurethane Foams with Different Types of Blowing Agents

In this study, rigid polyurethane foams modified with non-halogenated flame retardant were obtained. The foams were synthesized using two systems containing different blowing agents. In the first one, cyclopentane and water were used as a mixture of blowing agents, and in the second one, only water was used as a chemical blowing agent. The systems were modified with the additive phosphorus flame retardant Roflam F5. The obtained modified foams were tested for their flammability and basic properties, such as apparent density, closed-cell contents and analyses of the cell structures, thermal conductivity, mechanical properties, and water absorption. Increasing the content of Roflam F5 caused a decrease in temperature during the combustion of the material and extended the burning time. The addition of 1.0 wt.% phosphorus derived from Roflam F5 caused the modified rigid polyurethane foam to become a self-extinguishing material. The increase in the content of Roflam F5 caused a decrease in the total heat release and the maximum heat release rate during the pyrolysis combustion flow calorimetry. The foams with the highest content of flame retardant and foamed with a chemical-physical and chemical blowing agent had a lower total heat release by 19% and 11%, respectively, compared to reference foams.

Thermal Insulating Rigid Polyurethane Foams with Bio-Polyol from Rapeseed Oil Modified by Phosphorus Additive and Reactive Flame Retardants

In this article, rigid polyurethane foams obtained with the addition of a bio-polyol from rapeseed oil, were modified with the dimethyl propane phosphonate as additive flame retardant and two reactive flame retardants diethyl (hydroxymethyl)phosphonate and diethyl bis-(2-hydroxyethyl)-aminomethylphosphonate. The influence of used flame retardants on the foaming process and characteristic processing times of tested polyurethane systems were determined. The obtained foams were tested in terms of cell structure, physical and mechanical properties, as well as flammability. Modified foams had worse mechanical and thermal insulation properties, caused by lower cellular density and higher anisotropy coefficient in the cross-section parallel to the foam rise direction, compared to unmodified foam. However, the thermal conductivity of all tested foam materials was lower than 25.82 mW/m∙K. The applied modifiers effectively reduced the flammability of rigid polyurethane foams, among others, increasing the oxygen index above 21.4 vol.%, reducing the total heat released by about 41-51% and the rate of heat release by about 2-52%. A correlation between the limiting oxygen index values and both total heat released parameters from the pyrolysis combustion flow calorimetry and cone calorimetry was observed. The correlation was also visible between the value of the heat release capacity (HRC) parameter obtained from the pyrolysis combustion flow calorimetry and the maximum average rate of heat emission (MARHE) from the cone calorimeter test.