Effect of the Addition of Fique Bagasse Cellulose Nanoparticles on the Mechanical and Structural Properties of Plastic Flexible Films from Cassava Starch

One of the activities most representative of the agricultural sector in Colombia is the production of biodegradable fique fiber. The efficiency of the defiberization process of the fique leaves is very low since a mere 4% of the total weight of the leaf (cabuya) is used and marketed. The remaining 96%, composed of fique juice and bagasse, is considered to be waste and discarded, impacting the environment. The aim of this work was to study fique bagasse as a source of cellulose nanoparticles (CNCs). CNCs were obtained by acid hydrolysis and added at 10% to films made from cassava thermoplastic starch (TPS) by the casting method. Structural changes in the CNCs, TPS, and their mixtures were characterized by FTIR-ATR and their morphology and particle size by SEM and TEM microscopy, respectively. Thermal properties were analyzed using DSC and TGA, along with their effect on mechanical properties. Changes in the FTIR spectra indicated that the chemical method adequately removed hemicellulose and lignin from the fiber surface of fique bagasse. The CNCs showed a diameter and length of 7.5 ± 3.9 and 52.7 ± 18.1 nm, respectively, and TPS 10% CNC obtained an increase in mechanical strength of 116%. The obtainment of CNCs from lignocellulosic materials can thus be viewed as a favorable option for the subsequent reinforcement of a polymeric matrix.

A Pellet 3D Printer: Device Design and Process Parameters Optimization

A novel pellet 3D printer was first developed, and its structure was constructed out of three main parts. The material used in this device was polycaprolactone (PCL), which was praised for its good characteristics in the biomanufacturing and chemical industries. Three essential parameters that had important effects on the diameter of the printed fibers were systematically studied using a L9(34) orthogonal design table. Using the fused deposition modelling (FDM) method, some products were printed with this machine. Results showed that the stepper motor’s speed had the most significant effect on the diameter of the printed fibers. The optimal parameters were, a stepper motor speed of 1.256 mm3 s−1, a nozzle moving speed of 9.6 mm s−1, and 1.1 mm of height between the nozzle and the platform. Defects like gaps, warping, and poor surface quality were found to be related to different combinations of process parameters. By using the developed pellet 3D printer, the pre-step of making filaments can be avoided, which will bring convenience to FDM 3D printing.