Mechanical property and structure of a butadiene rubber composite filled with syndiotactic polybutadiene resin

Reinforcement of Styrene Butadiene Rubber Employing Poly(isobornyl methacrylate) (PIBOMA) as High Tg Thermoplastic Polymer

A set of poly(isobornyl methacrylate)s (PIBOMA) having molar mass in the range of 26,000–283,000 g mol⁻¹ was prepared either via RAFT process or using free radical polymerization. These linear polymers demonstrated high glass transition temperatures (T_g up to 201 °C) and thermal stability (T_onset up to 230 °C). They were further applied as reinforcing agents in the preparation of the vulcanized rubber compositions based on poly(styrene butadiene rubber) (SBR). The influence of the PIBOMA content and molar mass on the cure characteristics, rheological and mechanical properties of rubber compounds were studied in detail. Moving die rheometry revealed that all rubber compounds filled with PIBOMA demonstrated higher torque increase values ΔS in comparison with rubber compositions without filler, independent of PIBOMA content or molar mass, thus confirming its reinforcing effect. Reinforcement via PIBOMA addition was also observed for vulcanized rubbers in the viscoelastic region and the rubbery plateau, i.e. from −20 to 180 °C, by dynamic mechanical thermal analysis. Notably, while at temperatures above ~125 °C, ultra-high-molecular-weight polyethylene (UHMWPE) rapidly loses its ability to provide reinforcement due to softening/melting, all PIBOMA resins maintained their ability to reinforce rubber matrix up to 180 °C. For rubber compositions containing 20 phr of PIBOMA, both tensile strength and elongation at break decreased with increasing PIBOMA molecular weight. In summary, PIBOMA, with its outstanding high T_g among known poly(methacrylates), may be used in the preparation of advanced high-stiffness rubber compositions, where it provides reinforcement above 120 °C and gives properties appropriate for a range of applications.

In-chain functionalized syndiotactic 1,2-polybutadiene by a Ziegler–Natta iron(iii) catalytic system

Copolymerization of 1,3-butadiene with four 1-substituted 1,3-diene comonomers bearing amino and alkyoxy groups by a Ziegler–Natta iron(iii) catalytic system to access in-chain functionalized syndiotactic 1,2-polybutadiene is reported herein. The polar comonomer content can be easily regulated by varying the comonomer loadings or polymerization conditions, affording functionalized syndiotactic 1,2-polybutadiene with different amounts of functionalities. The incorporation of a polar comonomer showed little influence on the 1,2-content and stereoregularity of the resulting polymers, giving a 1,2-structure as high as ∼85% and an rrrr pentad of 81.0%. Significantly improved surface properties of the polymers was obtained after incorporation of polar comonomer, as revealed from the remarkably decreased water contact angles.

In-chain functionalized syndiotactic 1,2-polybutadiene through copolymerization of 1,3-butadiene and 1-substituted 1,3-diene comonomer by a Ziegler–Natta iron(iii) catalytic system.