Thermal aging performance of glass fiber/polyphenylene sulfide composites in high temperature

Structural transformation and performance analysis of PPS-based bag filters in coal-fired power plants

Owing to the complicated environments, the service life of bag-filter or electrostatic-bag composite precipitators with polyphenylene sulfide (PPS) is greatly deviated from the ideal time. In this paper, the structural transformation of PPS-based bag filter materials collected from the coal-fired power plants with different loading units were investigated systematically. As the SO2 content increases, the surface evolution of PPS fibers from smoothness to crack occurs. An opposite trend is observed for melting point and cross breaking strength. The major reason for the failure of PPS-based bag filters is that working temperature (T) often passes through acid dew gas point (Ta), and the SO3 would be produced during the condensing of H2SO4 when T is lower than Ta. The SO3 with strong oxidation would attack the weak C-S bonds of PPS, resulting in the oxidation or even sulfonation of PPS-based bag filters. This work discloses the actual structural evolution of PPS and some corresponding rules under the complicated corrosive gases with high temperatures, which provides a guidance for prolonging the service life of PPS-based bag filters during the usage of coal-fired power plants.

Study on Preparation and Properties of Glass Fibre Fabric Reinforced Polyphenylene Sulphide Composites

In this paper, glass fiber fabric reinforced polyphenylene sulfide composites were prepared by hot pressing. The effects of glass fibre modification and hot pressing temperature on the properties of the composites were investigated using a scanning electron microscope, infrared spectrometer, universal testing machine, and DIGEYE digital imaging colour measurement system. The results show that after the treatment with a silane coupling agent, the silane coupling agent was more uniformly distributed on the surface of the glass fibres, and the bonding effect between the glass fibre fabric and polyphenylene sulphide was significantly improved. The strength of the composites increased and then decreased with the increase of hot pressing temperature, and the surface colour of the composites became darker and darker. When the hot-pressing temperature is 310 °C, the mechanical properties of glass fabric-reinforced polyphenylene sulfide composites are at their best, the tensile strength reaches 51.9 MPa, and the bending strength reaches 78 MPa.

Thermal Aging Effects on the Mechanical Behavior of Glass-Fiber-Reinforced Polyphenylene Sulfide Composites

In this article, the thermal aging behavior of polyphenylene sulfide (PPS) composites, reinforced by 20% glass fibers (GFs), in thermal aging temperatures ranging from 85 to 145 °C was studied. Tensile and bending properties and color changes in the thermally aged samples were investigated. The results showed that thermal aging at this temperature range resulted in the degradation of mechanical properties. Both the tensile and flexural strength of the GF/PPS composites were significantly reduced after thermal aging at 145 °C. Decreased strength and brittle fracture were observed because thermal aging at high temperatures resulted in the deterioration of the interfaces between the GFs and PPS matrix. The degradation of the mechanical properties of the composite samples can be reflected by the color change, which means that the mechanical properties of the GF/PPS composite samples under thermal aging are predictable using color change analysis.