Effect of waterborne epoxy resin sizing on the surface and properties of high‐strength‐high‐modulus polyimide fibers

Improving Interfacial and Compressive Properties of Polyimide Fiber by Constructing Inorganic Layers on Fiber Surface

The compressive performance of organic fiber has always been a key problem, limiting its development. In this paper, silicon oxide, alumina, and titanium oxide particles were separately deposited on the surface of high-strength and high-modulus polyimide (PI) fibers to form a structural supporting shell by using a magnetron sputtering method. The theoretical thickness was calculated by thermogravimetric analysis in good agreement with the actual thickness determined from scanning electron microscopy. The mechanics, surface, and interface properties of the measured fibers were analyzed mainly from the aspects of surface energy, interfacial shear strength (IFSS), and compression strength. The results showed that after magnetron sputtering, the inorganic shells were uniformly deposited on the surface of PI fiber, resulting in an increase in the content of inorganic elements as well as the roughness. As a result, the surface energy and IFSS of silica-coated fiber was increased by 174 and 85.6%, respectively, and compression strength was increased by 45.7%. This study provides a new approach for improving the interface property and compression strength of high-strength and high-modulus PI-fiber-reinforced composites.

Preparation and Interfacial Properties of Hydroxyl-Containing Polyimide Fibers

Developing polyimide (PI) fibers with excellent interfacial adhesion and high mechanical properties for the PI fiber-reinforced polymer matrix composites (PFRPs) industry has been challenging. In this work, 4,4'-diamino-(1,1'-biphenyl)-3,3'-diol (HAB) diamine was introduced into the rigid molecular chains, and the high-performance PI fibers, presenting an interfacial shear strength (IFSS) value of 46.33 MPa, tensile strength of 2.62 GPa, and modulus of 100.15 GPa, were successfully manufactured when the content of HAB in mixed diamines was 30 mol %. Fourier transform infrared (FTIR) spectroscopy identified the presence of intermolecular H-bonding interactions, and 2D small-angle X-ray scattering indicated that the introduction of HAB moiety contributed to reducing the radii of microvoids in the fibers, which were considered to be the key factors leading to a significant enhancement in the mechanical properties of the fibers. X-ray photoelectron spectroscopy (XPS) and the static contact angle intuitively illustrated that the synthetic fiber surface contained active hydroxyl groups. The IFSS value of PI fiber/epoxy resin composites (PI/EPs) was 56.47 MPa when the content of HAB reached 70 mol %. Failure morphologies confirmed that the interfacial adhesion of PI/EPs was enhanced owing to the surface activity of PI fibers. Consequently, this study provides an effective strategy to the long-standing problems of high mechanical performances and poor surface activity for traditional PI fibers used in the PFRPs industry.