Hydroquinone Decorated with Alkyne, Quaternary Ammonium, and Hydrophobic Motifs to Mitigate Corrosion of X-60 Mild Steel in 15 wt.% HCl

Synthesis of a new quaternary ammonium salt for efficient inhibition of mild steel corrosion in 15 % HCl: Experimental and theoretical studies

The corrosion phenomenon and its economic impacts can hardly be ignored in any application. This study synthesized a quaternary ammonium salt (3) containing hydrophobic dodecyl and electron-rich diallylbenzyl amine moieties to be used in 15 % HCl as a corrosion inhibitor of mild steel. Several techniques, such as 1H and 13C NMR, IR, TGA, and elemental analysis, have been used to characterize inhibitor 3. Popular corrosion measurement techniques, namely weight loss, potentiodynamic polarization techniques, and electrochemical impedance spectroscopy, have been used to determine the efficiency of inhibitor 3. At 303 K and a moderately low concentration of 50 ppm, the quaternary ammonium salt-based inhibitor demonstrated a maximum efficiency of ≈95.0 %. At elevated temperatures of 313, 323, and 333 K, the inhibition efficacy values were recorded as 91.3, 82.8, and 75.0 %, respectively. Adsorption isotherm study revealed that the adsorption of inhibitor 3 followed Langmuir adsorption isotherm. The value ofΔ G a d s ° was found to be - 40.19 kJ mol-1, indicating that inhibitor 3 became adsorbed via a mixed physi-chemisorption mechanism. A very high adsorption constant (K a d s ) of 1.53 × 105 L mol-1 suggested strong adsorption of inhibitor 3. The difference in activation energy (E a ) value of 42.4 kJ mol-1 between the control and the inhibited solution indicated an efficient adsorption of inhibitor 3. The ability of inhibitor 3 to retard both anodic and cathodic half-cell reactions was proved via open circuit potential and Tafel curves studies. Detailed discussions on the change in corrosion current densities (i c o r r ), polarization (R p ) and charge transfer (R c t ) resistances have been offered to discuss the inhibition efficiency. Water contact angle measurement showed a drastic increase in mild steel surface hydrophobicity following inhibitor 3 adsorption. SEM-EDX and XPS studies confirmed the definitive presence of inhibitor 3 on the mild steel surface. Density functional theory (DFT) studies revealed the frontier molecular orbitals with which the metal surface interacts. A detailed corrosion inhibition mechanism has been offered in the context of adsorption isotherm and DFT studies.

Corrosion inhibition of mild steel by Praecitrullus fistulosus (tinda fruit and peel) extracts

Metal corrosion has recently emerged as a growing concern, impacting both local and industrial operations and disrupting conventional production methods. The utilization of green inhibitors to mitigate the metal degradation has garnered extensive attention from researchers and industrial professionals due to their prominent advantages: high efficiency, cost-effectiveness, and eco-friendliness. A novel ecofriendly inhibitor was prepared from Praecitrullus fistulosus (tinda fruit and peel) for mild steel (MS) corrosion in 1 M HCl. The presence of phenol, 3,5-bis (1,1-dimethyl ethyl)-, 9-octadecenoic acid, methyl ester, hexadecanoic acid 15-methyl-, methyl ester, 9, 12-octadecadienoic acid, methyl ester, 9, 12, 15-octadecatrienoic acid, methyl ester, (Z,Z,Z-), ascorbic acid, and phytol were identified as major constituent through LC/MS analysis of tinda extracts. The existence of these compounds was further confirmed through FTIR analysis, which shows the presence of various functional groups, such as -OH, CO, C-O-C, CC, and aromatic rings in the tinda extracts. Electrochemical and gravimetric analyses were used to investigate the inhibitory effect of tinda extracts. Outcomes of Tafel analysis revealed that both tinda extracts significantly reduced the corrosion current as compared to blank and achieved 83.73 % and 87.59 % inhibition efficiencies at 200 mg L-1 of tinda peel extract (TPE) and tinda fruit extract (TFE), respectively. The change in corrosion potential (Ecorr) was within an ±85 mV range compared to that of the uninhibited system, indicating that both tinda extracts demonstrated a mixed-type inhibition behavior. During adsorption studies, the best fit was obtained for the Langmuir adsorption model. The obtained values of standard Gibbs free energy (ΔG°ads) for TPE and TFE lie between -20 and - 40 kJ mol-1 but close to -20 kJ mol-1, which reveals preferential physical adsorption of the extracts on the metal surface. Thermodynamic parameters, including activation energy, enthalpy, and entropy, were computed across the temperature range of 303 to 323 K, suggesting that corrosion occurs spontaneously by the endothermic process. FESEM analysis depicted that inhibited systems exhibited smooth and crack-free surfaces as compared to blank system. AFM images demonstrated that surface roughness was significantly reduced for the inhibited system. In EDX analysis, the weight percentage of Cl was reduced in the presence of tinda extracts as compared to blank, and in XRD analysis, iron chloride (FeCl2) peak did not appear in the presence of inhibitor but it was in the uninhibited system. All surface-related findings signify that tinda extracts are adsorbed on the MS surface and form a protective layer that separates the metal from the corrosive solution.