Alumina supported copper oxide nanoparticles (CuO/Al2O3) as high-performance electrocatalysts for hydrazine oxidation reaction

Direct hydrazine liquid fuel cell (DHFC) is perceived as effectual energy generating mean owing to high conversion efficiency and energy density. However, the development of well-designed, cost effective and high performance electrocatalysts is the paramount to establish DHFCs as efficient energy generating technology. Herein, gamma alumina supported copper oxide nanocatalysts (CuO/Al₂O₃) are synthesized via impregnation method and investigated for their electrocatalytic potential towards hydrazine oxidation reaction. CuO with different weight percentages i.e., 4%, 8%, 12%, 16% and 20% are impregnated on gamma alumina support. X-ray diffraction analysis revealed the cubic crystal structure and nanosized particles of the prepared metal oxides. Transmission electron microscopy also referred to the cubic morphology and nanoparticle formation. Electrochemical oxidation potential of the CuO/Al₂O₃ nanoparticles is explored via cyclic voltammetry as the analytical tool. Optimization of conditions and electrocatalytic studies shown that 16% CuO/Al₂O₃ presented the best electronic properties towards N₂H₂ oxidation reaction. BET analysis ascertained the high surface area (131.2546 m² g¹) and large pore diameter (0.279605 cm³ g^-1) for 16% CuO/Al₂O₃. Nanoparticle formation, high porosity and enlarged surface area of the proposed catalysts resulted in significant oxidation current output (600 μA), high current density (8.2 mA cm^-2) and low charge transfer resistance (3.7 kΩ). Electrooxidation of hydrazine on such an affordable and novel electrocatalyst opens a gateway to further explore the metal oxide impregnated alumina materials for different electrochemical applications.

Alternative Support Material to Platinum Catalyst Used for Oxygen Reduction Reaction: Nonporous Carbon

In this study, unlike the porous carbon as a conventional catalyst support material in fuel cells, nonporous carbon was synthesized in the presence of different acid concentrations (0.2 M-1 M) and investigated as a support material for platinum (Pt) catalysts in the oxygen reduction reaction (ORR). Since the micropore volume of the synthesized carbons is negligible, the detected surface areas with Brunauer-Emmett-Teller (BET) method were in the range of 19-23 m2/g. Among the support materials, the carbon-supported Pt catalyst synthesized in the presence of 1 M acid was investigated electrochemically in terms of hydrogen oxidation (HOR) and ORR half-cell reactions in the three-electrode system. The Pt catalyst supported with nonporous carbon, synthesized using 1 M acid, reached the maximum limiting current value of -0.25 mA/cm2 (@2500 rpm) at ORR hydrodynamic curves. Low internal and charge transfer resistances of the same catalyst in electrochemical impedance spectroscopy (EIS) analysis are attributable to its nonporous structure.

The Facile Deposition of Pt Nanoparticles on Reduced Graphite Oxide in Tunable Aryl Alkyl Ionic Liquids for ORR Catalysts

In this study, we present the facile formation of platinum nanoparticles (Pt-NPs) on reduced graphite oxide (rGO) (Pt-NP@rGO) by microwave-induced heating of the organometallic precursor ((MeCp)PtMe₃ in different tunable aryl alkyl ionic liquids (TAAIL). In the absence of rGO, transmission electron microscopy (TEM) reveals the formation of dense aggregates of Pt-NPs, with primary particle sizes of 2 to 6 nm. In contrast, in the Pt-NP@rGO samples, Pt-NPs are homogeneously distributed on the rGO, without any aggregation. Pt-NP@rGO samples are used as electrode materials for oxygen reduction reaction (ORR), which was assessed by cyclic voltammetry (CV) and linear sweep voltammetry (LSV). The electrochemical surface area (ECSA) and mass-specific activity (MA) increase up to twofold, compared with standard Pt/C 60%, making Pt-NP@rGO a competitive material for ORR.