Biomedical research of novel biodegradable copoly(amino acid)s based on 6-aminocaproic acid and L-proline

A Highly Hydrophilic and Biodegradable Novel Poly(amide-imide) for Biomedical Applications

A novel biodegradable poly(amide-imide) (PAI) with good hydrophilicity was synthesized by incorporation of l-glycine into the polymer chain. For comparison purposes, a pure PAI containing no l-glycine was also synthesized with a three-step method. In this study, we evaluated the novel PAI's thermal stability, hydrophilicity, solubility, biodegradability and ability to support bone marrow mesenchymal stem cell (BMSC) adhesion and growth by comparing with the pure PAI. The hydrophilic tests demonstrated that the novel PAI has possible hydrophilicity at a 38° water contact angle on the molecule surface and is about two times more hydrophilic than the pure PAI. Due to an extra unit of l-glycine in the novel PAI, the average degradation rate was about 2.4 times greater than that of the pure PAI. The preliminary biocompatibility studies revealed that all the PAIs are cell compatible, but the pure PAI exhibited much lower cell adhesion than the l-glycine-incorporated novel PAI. The hydrophilic surface of the novel PAI was more suitable for cell adhesion, suggesting that the surface hydrophilicity plays an important role in enhancing cell adhesion and growth.

Degradable biocomposite of nano calcium-deficient hydroxyapatite-multi(amino acid) copolymer

Background and methods

A nano calcium-deficient hydroxyapatite (n-CDHA)-multi(amino acid) copolymer (MAC) composite bone substitute biomaterial was prepared using an in situ polymerization method. The composition, structure, and compressive strength of the composite was characterized, and the in vitro degradability in phosphate-buffered solution and preliminary cell responses to the composite were investigated.

Results

The composite comprised n-CDHA and an amide linkage copolymer. The compressive strength of the composite was in the range of 88–129 MPa, varying with the amount of n-CDHA in the MAC (ranging from 10 wt% to 50 wt%). Weight loss from the composite increased (from 32.2 wt% to 44.3 wt%) with increasing n-CDHA content (from 10 wt% to 40 wt%) in the MAC after the composite was soaked in phosphate-buffered solution for 12 weeks. The pH of the soaking medium varied from 6.9 to 7.5. MG-63 cells with an osteogenic phenotype were well adhered and spread on the composite surface. Viability and differentiation increased with time, indicating that the composite had no negative effects on MG-63 cells.

Conclusion

The n-CDHA-MAC composite had good cytocompatibility and has potential to be used as a bone substitute.