Curing effectiveness of a light emitting diode on dentin bonding agents

Enhancing Light-curing Competence: A Study of Radiant Exposure and Training Outcomes Among Dental Students

OBJECTIVES

The aim of this study was to measure radiant exposure and time necessary to deliver 16 J/cm2 of radiant exposure to simulated Class I and Class III preparations by first-year dental students. First-year dental students (n=89) received a 60-minute lecture on light-curing. Using the Managing Accurate Resin Curing Patient Simulator (MARC-PS) and protective blue-light-blocking glasses, students twice light-cured Class I and Class III restorations, using the Valo Grand Cordless light-curing unit with infection-control barriers on both Standard and High Power Plus modes. After their first attempts, if students did not obtain at least 16 J/cm2 of radiant exposure (RE), they received additional instruction. Paired t-tests were used to determine the change between the first and second attempts. After averaging two attempts, radiant exposure and time were compared between Standard and High Power Plus modes within individuals using paired t-tests.

RESULTS

79% of students provided 16 J/cm2 of radiant exposure on both attempts for Standard and High Power Plus modes. High Power Plus mode provided statistically significantly more radiant exposure and required less time to obtain 16 J/cm2 of radiant exposure for both restorations.

CONCLUSIONS

The MARC-PS is useful to identify students requiring instruction. It may be prudent to use High Power Plus mode or increase time on Standard mode to light-cure Class I restorations.

Influence of Layer Thickness and Shade on the Transmission of Light through Contemporary Resin Composites

BACKGROUND

Material-dependent parameters have an important impact on the efficiency of light polymerization. The present in vitro study aimed to investigate the influence of the increment thickness and shade of nano- and nanohybrid resin composites on the transmission of curing light.

METHODS

Three contemporary resin composites were evaluated: Tetric EvoCeram® (TEC); Venus Diamond® (VD); and Filtek Supreme XTE® (FS XTE). Light transmission (LT) was recorded in accordance with the sample thickness (0.5 to 2.7 mm) and the shade. Polymerized samples were irradiated for 10 s each using the high-power LED curing light Celalux 2 (1900 mW/cm2). LT was simultaneously recorded using the MARC Patient Simulator (MARC-PS).

RESULTS

LT was strongly influenced by the composite layer thickness. For 0.5 mm-thick samples, a mean power density of 735 mW/cm2 was recorded at the bottom side. For the 2.7 mm samples, a mean power density of 107 mW/cm2 was measured. Only LT was markedly reduced in the case of darker shades. From A1 to A4, LT decreased by 39.3% for FS XTE and 50.8% for TEC. Dentin shades of FS XTE and TEC (A2, A4) showed the lowest LT.

CONCLUSIONS

The thickness and shade of resin composite increments strongly influences the transmission of curing light. More precise information about these parameters should be included in the manufacture manual.

Effect of Thickness on Light Transmission and Vickers Hardness of Five Bulk-fill Resin-based Composites Using Polywave and Single-peak Light-emitting Diode Curing Lights

OBJECTIVES:

This study compared light transmission through different thicknesses of bulk-fill resin-based composites (RBCs) using a polywave and a single-peak light-emitting diode light-curing unit (LCU). The effect on the surface hardness was also evaluated.

METHODS:

Five bulk-fill RBCs were tested. Specimens (n=5) of 1-, 2-, 4-, or 6-mm thickness were photopolymerized for 10 seconds from the top using a polywave (Bluephase Style) or single-peak (Elipar S10) LCU, while a spectrophotometer monitored in real time the transmitted irradiance and radiant exposure reaching the bottom of the specimen. After 24 hours of storage in distilled water at 37°C, the Vickers microhardness (VH) was measured at top and bottom. Results were analyzed using multiple-way analysis of variance, Tukey post hoc tests, and multivariate analysis (α=0.05).

RESULTS:

The choice of LCU had no significant effect on the total amount of light transmitted through the five bulk-fill RBCs at each thickness. There was a significant decrease in the amount of light transmitted as the thickness increased for all RBCs tested with both LCUs ( p<0.001). Effect of LCU on VH was minimal (η_p²=0.010). The 1-, 2-, and 4-mm-thick specimens of SDR, X-tra Fill, and Filtek Bulk Restorative achieved a VH_bottom/top ratio of approximately 80% when either LCU was used.

CONCLUSIONS:

The total amount of light transmitted through the five bulk-fill RBCs was similar at the different thicknesses using either LCU. The polywave LCU used in this study did not enhance the polymerization of the tested bulk-fill RBCs when compared with the single-peak LCU.

Contemporary issues in light curing

This review article will help clinicians understand the important role of the light curing unit (LCU) in their offices. The importance of irradiance uniformity, spectral emission, monitoring the LCU, infection control methods, recommended light exposure times, and learning the correct light curing technique are reviewed. Additionally, the consequences of delivering too little or too much light energy, the concern over leachates from undercured resins, and the ocular hazards are discussed. Practical recommendations are provided to help clinicians improve their use of the LCU so that their patients can receive safe and potentially longer lasting resin restorations.

Knoop Microhardness Mapping Used to Compare the Efficacy of LED, QTH and PAC Curing Lights

The output of a curing light measured at a distance of 0 mm is a poor indicator of how much light energy will be delivered to a restoration in the mouth. When used for manufacturers' suggested curing times and at clinically relevant distances, some curing lights deliver much less energy than is recommended (&lt;10J/cm2) and produce softer composites.

Acid-etch interval and shear bond strength of Er,Cr:YSGG laser-prepared enamel and dentin

The formation of a superficial layer of tiny flakes has been observed on teeth prepared by Erbium lasers. It has been suggested that removing this layer (mechanically or chemically) may increase the bond strength of the resin composite. The purpose of this study is to evaluate the effect of various etching times on bond strength of resin composite to enamel and dentin prepared by Er,Cr:YSGG laser. Sixty previously flattened human molars were irradiated for 10 s by an Er,Cr:YSGG laser. Enamel (E) specimens were etched with 37% H(3)PO(4) for 20, 40 or 60 s and dentin (D) specimens were etched for 15 or 30 s. All specimens were prepared for a standard shear bond strength (SBS) test (1 mm/min). Data were analyzed [ANOVA, Tukey post-hoc, a < 0.05)] and the failure mode was studied under SEM. Mean SBS+/-sd (MPa) for each group was 16.97 +/- 7.77 (E20s), 21.34 +/- 3.55 (E40s), 14.08 +/- 4.77 (E60s), 13.62 +/- 7.28 (D15s) and 13.15 +/- 6.25 (D30s). SBS for E40s was significantly higher than E60s (p = 0.023). No difference was noted between the dentin groups. SEM evaluation showed predominantly cohesive failure. Within the limits of this study, etching time significantly influenced the SBS of composite resin to laser-prepared enamel. SEM showed subsurface cracks, fissures, and deformities leading to predominantly cohesive failure in both enamel and dentin.