Biocompatibility testing of simulated total joint arthoplasty articulation debris

Biological Reactions to Metal Particles and Ions in the Synovial Layer of Mice

Metal particles and ions released from implants not only have a fundamental effect on the longevity of total joint replacements, but can also be disseminated to remote organs. Periprosthetic tissues harvested during revision surgeries mainly reflect end-stage failure but may not adequately reveal initial biological reactions and systemic side effects. Therefore, primary reactions caused by metal particles and ions were investigated in an established murine model. Left knee joints in three groups, each consisting of ten female BALB/c mice, received injections of metal ions (MI), metal particles (MP) and phosphate-buffered saline (PBS) (control). Seven days after the injection, immunohistochemical analyses of the synovial layer were performed with respect to some biological markers including Tumor necrosis factor -α (TNF-α), Interleukin-6 (IL-6), Interleukin-1β (IL-1β), Cluster of Differentiation 45 (CD45), Cluster of Differentiation 68 (CD68) and Cluster of Differentiation 3(CD3). The MP group showed significantly enhanced proinflammatory cytokine expression (TNF-α, IL-6 and IL-1β) compared with the other groups (p < 0.05). Interestingly, CD3, as a marker for T lymphocytes, did not increase in any of the groups. The MI group showed a significantly increased expression of CD45 compared with the control group (p < 0.05). Therefore, during the primary process, metal particles have stronger pro-inflammatory potential than metal ions, and T lymphocytes did not seem to be activated in our murine model. Systemic reactions caused by metal particles and ions were found by observing the untreated right knees.

Local Biological Reactions and Pseudotumor-Like Tissue Formation in relation to Metal Wear in a Murine In Vivo Model

Metal wear debris and released ions (CoCrMo), which are widely generated in metal-on-metal bearings of hip implants, are also found in patients with metal-on-polyethylene bearings due to the mechanically assisted crevice corrosion of modular taper junctions, including head-neck and neck-stem taper interfaces. The resulting adverse reactions to metal debris and metal ions frequently lead to early arthroplasty revision surgery. National guidelines have since been published where the blood metal ion concentration of patients must consistently be monitored after joint replacement to prevent serious complications from developing after surgery. However, to date, the effect of metal particles and metal ions on local biological reactions is complex and still not understood in detail; the present study sought to elucidate the complex mechanism of metal wear-associated inflammation reactions. The knee joints in 4 groups each consisting of 10 female BALB/c mice received injections with cobalt chrome ions, cobalt chrome particles, and ultra-high-molecular-weight polyethylene (UHMWPE) particles or PBS (control). Seven days after injection, the synovial microcirculation and knee joint diameter were assessed via intravital fluorescence microscopy followed by histological evaluation of the synovial layer. Enlarged knee diameter, enhanced leukocyte to endothelial cell interactions, and an increase in functional capillary density within cobalt chrome particle-treated animals were significantly greater than those in the other treatment groups. Subsequently, pseudotumor-like tissue formations were observed only in the synovial tissue layer of the cobalt chrome particle-treated animals. Therefore, these findings strongly suggest that the cobalt chrome particles and not metal ions are the cause for in vivo postsurgery implantation inflammation.

Optimization of wear loss in silicon nitride (Si3N4)-hexagonal boron nitride (hBN) composite using DoE-Taguchi method

Introduction

The contacting surfaces subjected to progressive loss of material known as ‘wear,’ which is unavoidable between contacting surfaces. Similar kind of phenomenon observed in the human body in various joints where sliding/rolling contact takes place in contacting parts, leading to loss of material. This is a serious issue related to replaced joint or artificial joint.

Case description

Out of the various material combinations proposed for artificial joint or joint replacement Si₃N₄ against Al₂O₃ is one of in ceramic on ceramic category. Minimizing the wear loss of Si₃N₄ is a prime requirement to avoid aseptic loosening of artificial joint and extending life of joint.

Discussion and evaluation

In this paper, an attempt has been made to investigate the wear loss behavior of Si₃N₄–hBN composite and evaluate the effect of hBN addition in Si₃N₄ to minimize the wear loss. DoE–Taguchi technique is used to plan and analyze experiments.

Conclusion

Analysis of experimental results proposes 15 N load and 8 % of hBN addition in Si₃N₄ is optimum to minimize wear loss against alumina.