Effect of diode laser-assisted bleaching on the bond strength of different adhesive systems to enamel: Interfacial SEM analysis

The Effect of Two Different Wavelengths of Diode Laser on the Shear Bond Strength of Composite to Dental Enamel after Bleaching Process: An In Vitro Study

INTRODUCTION

In recent years, tooth whitening has become one of the most popular ways of achieving the original tooth color. The effect of whitening gel can be improved through heat, light or laser. The bond strength between the enamel and the composite can be reduced through bleaching and laser radiation. The purpose of this study is to assess the shear bond strength of resin composite to enamel after a bleaching process using hydrogen peroxide, with and without a laser (970 nm and 445 nm lasers).

METHOD

This study used 51 extracted anterior teeth without caries that were divided into three groups. A 40% hydrogen peroxide gel was used on the enamel of all teeth. The control group received bleaching without a laser. Both the second and third treatment groups received bleaching with a laser, one with 970 nm and the other with 445 nm. After the bleaching process, all groups had etching, bonding and curing of the composite performed. Lastly, the shear bond strength between the enamel and the composite was measured and the failure modes were recorded. The data were compared using a one-way ANOVA test.

RESULTS

The mean shear bond strength between the enamel and the composite in the 445 nm group three (445 nanometer) was significantly lower than the other groups (p < 0.05). There was no significant difference between the control and the 970 nm groups (p = 0.2).

CONCLUSION

According to the laser wavelengths and parameters that were used in this study and the results of this study, office bleaching with a 445 nm laser weakened the shear bond strength between the enamel and the composite.

Comparative evaluation of bond strength of diode and neodymium-doped:Yttrium aluminum garnet-assisted bleached enamel with nanofilled composite: An in vitro study

Background

The world of esthetic dentistry is constantly making efforts toward the management of tooth staining. Laser-assisted bleaching is needed before adhesive restorations and has become common and advantageous as it accelerates bleaching action, reduces postoperative sensitivity, and promotes recrystallization of enamel.

Aim

The study aimed to evaluate and compare the bond strength of diode (Biolace: EpicX) and neodymium-doped:yttrium aluminum garnet (Nd:YAG) (LightWalker, Fotona, Slovenia) assisted bleached (Pola Office, SDI) enamel with nanofilled composite (GC Solare Sculpt).

Materials and Methods

The samples were divided into three groups (n = 11): Group A - Conventionally bleached enamel, Group B - Diode laser-assisted bleached enamel, Group C - Nd:YAG laser-assisted bleached enamel. After storing samples in Artificial Saliva for 2 weeks, bonding was performed, and nanofilled composite resin was applied through an incremental method. Samples were subjected to shear bond strength (SBS) analysis.

Conclusion

The use of Nd:YAG laser on bleached enamel significantly increases the bond strength with nanofilled composite resin.

Effectiveness of sodium hypochlorite treatment on the bonding of four adhesive systems to fluorotic enamel

The study evaluated the effect of sodium hypochlorite (NaOCl) treatment on fluorotic enamel bonding of four adhesive systems. They were Single Bond 2 (SB2), Prime&Bond NT (PBN), Clearfil SE Bond (CSB), and Single Bond Universal (SBU). One hundred eighteen extracted moderate fluorotic molars were divided into eight groups according to NaOCl pretreatment and four adhesive systems. The microshear bond strength (μSBS), etching pattern, and penetration depth (PD) were observed. The statistical method was two-way ANOVA and least significant difference (LSD) test (α=0.05). The application of NaOCl significantly increased the μSBS of PBN and SBU (p<0.05). The enamel-etching pattern of CSB and SBU was deeper under SEM. A noticeable increase of PD was in SB2 and SBU after the application of NaOCl (p<0.05). Pretreatment of 5.25% NaOCl for the 60 s can increase μSBS of PBN and SBU, PD of SB2 and SBU, and improve enamel-etching pattern of CSB and SBU to fluorotic enamel.