Backside wear of tibial polyethylene components is affected by gait pattern: A knee simulator study using rare earth tracer technology

Aseptic loosening of the option stemmed tibial tray in the Zimmer NexGen LPS total knee arthroplasty system

BACKGROUND

We investigated the relationship between the backside deformation of polyethylene (PE) tibial inserts and aseptic loosening of the Option stemmed tibial tray used with Zimmer NexGen posterior-stabilised (PS) devices. We hypothesized that explanted inserts used in PS designs would exhibit greater extents of PE backside deformation than those used in equivalent cruciate retaining (CR) designs and that PE inserts retrieved from total knee arthroplasties (TKAs) revised for aseptic tibial tray loosening would exhibit greater extents of backside deformation than TKAs revised for other reasons.

METHODS

A total of 73 explanted fixed-bearing TKAs (42 CR and 31 PS) were examined. PE components underwent geometric examination with a coordinate measuring machine using validated techniques. Multiple regression modelling was used to identify variables associated with revision secondary to aseptic loosing and to determine factors associated with increased PE backside deformation.

RESULTS

PE inserts retrieved from TKAs with aseptic loosening had significantly greater backside deformation than those retrieved from TKAs revised for other reasons (p < 0.001). Greater PE backside deformation was significantly associated with larger tray/insert clearance heights (p < 0.001), thinner inserts (p < 0.001) and PS TKAs (p = 0.001).

CONCLUSION

PE backside deformation was significantly greater in the PS TKAs. This may provide one explanation for the increased rate of aseptic loosening reported with the Option tibial tray used with the Legacy Posterior Stabilised (LPS) system.

A review of advances in tribology in 2020–2021

Around 1,000 peer-reviewed papers were selected from 3,450 articles published during 2020–2021, and reviewed as the representative advances in tribology research worldwide. The survey highlights the development in lubrication, wear and surface engineering, biotribology, high temperature tribology, and computational tribology, providing a show window of the achievements of recent fundamental and application researches in the field of tribology.

Similar Biomechanical Behavior in Gait Analysis between Ceramic-on-Ceramic and Ceramic-on-XLPE Total Hip Arthroplasties

In vitro measurements are widely used to implement gait kinematic and kinetic parameters to predict THA wear rate. Clinical tests of materials and designs are crucial to prove the accuracy and validate such measurements. This research aimed to examine the effect of CoC and CoXLPE kinematics and kinetics on wear during gait, the essential functional activity of humans, by comparing in vivo data to in vitro results. Our study hypothesis was that both implants would present the same hip joint kinematics and kinetics during gait. In total, 127 unilateral primary cementless total hip arthroplasties were included in the research. There were no statistically significant differences observed at mean peak abduction, flexion, and extension moments and THA kinematics between the two groups. THA gait kinematics and kinetics are crucial biomechanical inputs associated with implant wear. In vitro studies report less wear in CoC than CoXLPE when tested in a matched gait kinematic protocol. Our findings confirm that both implants behave identically in terms of kinematics in a clinical environment, thus strengthening CoC advantage in in vitro results. Correlated to all other significant factors that affect THA wear, it could address in a complete prism the wear on CoC and CoXLPE.

Joint line elevation and tibial slope are associated with increased polyethylene wear in cruciate-retaining total knee replacement

The purpose of this retrieval study was to determine the effect of implant positioning on wear, taking patient-related factors into account. Therefore, the volumetric material loss of 59 retrieved tibial liners was quantitatively determined using a coordinate measuring-machine. All retrievals were made of the same polyethylene and design by a single manufacturer. Using time in-situ and linear regression, a wear rate for each liner was determined and corrected for bedding-in. Backside damage was qualitatively scored. The following implant positioning parameters were obtained from radiographs: anatomical lateral-distal femoral angle, anatomical medial-proximal tibial angle, femoral tilt angle, and posterior tibial slope. The patella position was assessed by the Blackburne-Peel index and the Insall-Salvati ratio. Unlike the Insall-Salvati ratio, the Blackburne-Peel index is known to detect surgical joint line elevation. Using general linear modeling the most impactful factors on wear rate and backside damage was determined, thereby taking patient demographic factors into account. The mean volumetric wear rate was 11.6 mm³ /y. Wear decreased with older age (P = .021) and female sex (P = .001). The wear rate increased with joint line elevation as indicated from a decreased Blackburne-Peel index (P = .019), and increased with increased posterior tibial slope (P = .026). The backside damage score also increased with joint line elevation (P = .036). A Blackburne-Peel index decrease of 0.1, signifying joint line elevation, was found to increase the wear rate by 1.8 mm³ /y and increase back-sided wear. A high tibial slope (>7°) led to a 9.3 mm³ /y increase in wear rate compared with a low tibial slope (<3°). The results of this study demonstrate that tibial liner positioning has a significant impact on polyethylene wear with potential implications on osteolysis over time.