Preparation of bottlebrush polymer-modified magnetic graphene as immobilized metal ion affinity adsorbent for purification of hemoglobin from blood samples

An immobilized metal affinity (IMA) adsorbent was prepared by grafting bottlebrush polymer pendant with iminodiacetic acid (IDA) from the surface of polydopamine (PDA)-coated magnetic graphene oxide (magGO), via surface-initiated atom transfer radical polymerization (SI-ATRP). Poly(hydroxyethyl methacrylate) (PHEMA) was grafted firstly from the PDA-coated magGO as the backbone, and then poly(glycidyl methacrylate) was grafted from the PHEMA chains via the second SI-ATRP to afford the bottlebrush polymer-grafted magGO Thereafter, IDA was anchored on the nanocomposites to produce the IMA adsorbent after chelating copper ions. The adsorbent was characterized by various physical and physicochemical methods. Its adsorption properties were evaluated by using histidine-rich proteins (bovine hemoglobin, BHb) and other proteins (lysozyme and cytochrome-C). The results show that its maximum adsorption capacity to BHb was 378.6 mg g^-1, and the adsorption equilibrium can be quickly reached within 1 h. The adsorbent has excellent reproducibility and reusability. It has been applied to selectively purify hemoglobin from human whole blood, indicating its potential in practical applications. Graphical abstract.

Preparation and electromagnetic properties of core/shell polystyrene@polypyrrole@nickel composite microspheres

Through a novel method, we successfully synthesized electromagnetic (EM) functional polystyrene@polypyrrole@nickel (PS@PPy@Ni) composite microspheres. The PS@PPy spheres with well-defined core/shell structure have been synthesized via an in situ chemical oxidative copolymerization of pyrrole (Py) and N-2-carboxyethylpyrrole (PyCOOH) templated by PS microspheres. The reaction was carried out under heterophase conditions using the mixture of ethanol and water as the continuous phase. Tailored by the carboxyl groups on the surface of microspheres, magnetic nickel layer has been steady deposited onto the P(Py-PyCOOH) layer of the microspheres through an activation-electroless plating technology. The fine PS@P(Py-PyCOOH)@Ni core/shell structures could be obtained with the PyCOOH content up to 50 wt % in the P(Py-PyCOOH) layer. Moreover, the as-prepared PS@P(Py-PyCOOH)@Ni composites are ferromagnetic materials and behave as a good electromagnetic (EM) absorption material due to the coating of Ni layer around the PS@P(Py-PyCOOH) spheres. The PS@P(Py-PyCOOH)@Ni composite spheres show the remarkable EM wave absorption property with the maximum reflection loss (around -20.06 dB) at 10.69 GHz. The EM wave absorption can retained lower than -10 dB within a broad frequency range from 9.16 to 13.75 GHz.